Difference Between Electroplating &amp Galvanizing

This document compares hot dip galvanizing and electroplating (electro-galvanizing) for coating steel. Hot dip galvanizing involves immersing steel in molten zinc, resulting in a thicker zinc-iron alloy coating through a chemical reaction. Electroplating uses an electric current to apply a thinner, less protective zinc coating through mechanical bonding. Hot dip galvanizing provides better corrosion protection than electroplating due to its thicker, metallurgically bonded coating. Paint can also be successfully applied to hot dip galvanized steel if the proper procedures are followed.

Uploaded by

Sreedhar Patnaik.M
Copyright
© Attribution Non-Commercial (BY-NC)
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
168 views

Difference Between Electroplating &amp Galvanizing

This document compares hot dip galvanizing and electroplating (electro-galvanizing) for coating steel. Hot dip galvanizing involves immersing steel in molten zinc, resulting in a thicker zinc-iron alloy coating through a chemical reaction. Electroplating uses an electric current to apply a thinner, less protective zinc coating through mechanical bonding. Hot dip galvanizing provides better corrosion protection than electroplating due to its thicker, metallurgically bonded coating. Paint can also be successfully applied to hot dip galvanized steel if the proper procedures are followed.

Uploaded by

Sreedhar Patnaik.M
Copyright
© Attribution Non-Commercial (BY-NC)
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
You are on page 1/ 3

Hot Dip Galvanized Information Sheet No.

1
Hot Dip Galvanizing versus Electro-plating (Electro-galvanizing)
The following summary addresses the question of the differences between Hot Dip Galvanizing and that of Zinc Electro Plating (Electro galvanizing). Zinc Electro Plating (Electro galvanizing) Electro galvanizing is the name applied to the process of covering steel with a thin coating of zinc by means of passing an electric current between an anode (zinc) and the steel (cathode). The process is illustrated in the following diagram.
P ro d u c t im m e r s e d in a c o a tin g s o lu tio n D C c u r re n t p a s s e d b e tw e e n th e p r o d u c t (c a th o d e ) & a n e le c tr o d e (a n o d e ) C o a tin g g o v e rn e d b y :
C u r r e nt T e m p e r a tu r e C h e m ic a l c o m p o s itio n P r o c e s s tim e

E le c tro p la tin g

M e ta ls u s e d fo r e le c tr o p la tin g :
C opper N ic k e l Z in c C hrom e

The characteristics of an electro-galvanized coating are summarized as follows. Uniform smooth coating with a bright luster. Coating thickness usually between 6 to 10 microns (m). The coating consists of +99% zinc. Zinc is deposited by means of a cold process. The adhesion of the coating to the steel consists of Mechanical Bonding. The process is carried out at normal room temperatures. Product profiles can affect the uniformity of the coating due to what is known as the Faraday Cage effect.
Micrograph of Electroplating (x 200)
8 to 10m 10

Zinc Coating

Steel

Micrograph of a typical Electro galvanized coating

Mechanical Bonding
Electrolytically applied Zinc layer
Electro-galvanized

Hot Dip Galvanized Information Sheet No.1


Hot Dip Galvanizing versus Electro-plating (Electro-galvanizing)

Hot Dip Galvanizing As the name implies the application of the zinc coating is a hot process whereby the cleaned steel is immersed in molten zinc usually at a temperature of between 445 and 450 When C C. the cleaned steel is immersed into the molten zinc, a chemical reaction results, which we refer to as following metallurgical laws. As a result of this process the coating consists of a series of zinc iron alloy layers and usually a top pure zinc layer. The adhesion of the coating to the steel is therefore determined by means of a chemical bond, or a metallurgical bond. Such bonding is considered to be far superior to that of a mechanical bond. The characteristics of a hot dip galvanized coating are summarized as follows: Relatively uniform and can range from a bright silvery to a dull grey surface finish depending on the chemical analysis of the steel being processed. Coating thickness usually between 55 to >100 micros (m), depending on steel thickness as well as the chemical composition of the steel being processed. The coating consists of a series of zinc iron layers, the formation of which is influenced by the chemical composition of the steel being processed.

HDG Factors
Zn Coating thickness Steel composition i.e. reactive steels Immersion Time Zinc Temperature Speed of Withdrawal Angle of withdrawal Lead & Aluminium Content of the Zn

Hot Dip Galvanizing Process and factors that affect coating thickness

Eta - Layer

60 to 80m Barrier Protection

Zeta - Layer

Micrograph (x200) of a typical Hot Dip Galvanized coating on Aluminum Killed Steel.

Delta - Layer
Gamma - Layer

Steel

Barrier Protection 1ST Line of Defence

page 2 of 3

Hot Dip Galvanized Information Sheet No.1


Hot Dip Galvanizing versus Electro-plating (Electro-galvanizing)

Corrosion Protection The corrosion protection of a zinc coating, in a given environment, is generally a function of the coating thickness, i.e. the thicker the coating the longer the service life of the product that is being protected. It therefore follows that a hot dip galvanized coating will provide greater corrosion protection to steel when compared to that of an electroplated product. This factor is illustrated by the fact that electro galvanized coatings are generally <10m whereas hot dip galvanized coatings are normally >55m, i.e. five times thicker. Painting of Hot Dip Galvanized Coatings It is a misconception that one cannot successfully apply paint onto a hot dip galvanized surface. In point of fact, it is becoming more and more commonplace to successfully paint galvanized products, provided the process conforms to a recognised specification and is carried out in terms of the correct procedure. Generally this misconception has arisen due to the incorrect procedures being followed when paint is applied to any zinc surface. The following photograph is an illustration of a hot dip galvanized structure onto which paint has been correctly applied.

Athlone Stadium Cape Tow n

page 3 of 3