Datasheet Polystone P Copolymer

Polystone P copolymer is a high strength, weldable, and corrosion resistant material suitable for chemical engineering, tank building, boat building, and ventilation equipment. It has a density of 0.91 g/cm3, water absorption below 0.1%, and flame retardancy of HB at thicknesses of 3-6 mm. Its mechanical properties include a yield stress of 23 N/mm2, elongation at break above 50%, tensile modulus of 1100 MPa, and notched impact strength above 40 kJ/m2. Its thermal properties allow service temperatures from -30 to 100°C continuously and up to 150°C briefly.

Uploaded by

Khanh Pham
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
137 views1 page

Datasheet Polystone P Copolymer

Polystone P copolymer is a high strength, weldable, and corrosion resistant material suitable for chemical engineering, tank building, boat building, and ventilation equipment. It has a density of 0.91 g/cm3, water absorption below 0.1%, and flame retardancy of HB at thicknesses of 3-6 mm. Its mechanical properties include a yield stress of 23 N/mm2, elongation at break above 50%, tensile modulus of 1100 MPa, and notched impact strength above 40 kJ/m2. Its thermal properties allow service temperatures from -30 to 100°C continuously and up to 150°C briefly.

Uploaded by

Khanh Pham
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
You are on page 1/ 1

Technical data sheet

Polystone P copolymer
Product characteristics

Typical field of application

High strength
High weldability
Excellent chemical and corrosion resistance

Chemical engineering and tank building


Boat building
Ventilation and equipment manufacturing

Test method

Unit

Value

Density

DIN EN ISO 1183-1

g/cm3

0,91

Water absorption

DIN EN ISO 62

<0,1

Flammability (Thickness 3 mm / 6 mm)

UL 94

General properties

HB

Mechanical properties
Yield stress

DIN EN ISO 527

N/mm

23

Elongation at break

DIN EN ISO 527

>50

Tensile modulus of elasticity

DIN EN ISO 527

MPa

1100

Notched impact strength (charpy)

DIN EN ISO 179

kJ/m

> 40

Shore hardness

DIN EN ISO 868

scale D

69

Melting temperature

ISO 11357-3

162-167

Thermal conductivity

DIN 52612-1

W / (m * K)

0,20

Thermal capacity

DIN 52612

kJ / (kg * K)

1,70

Coefficient of linear thermal expansion

DIN 53752

10-6K-1

120-190

Service temperature, long term

Average

-30 100

Service temperature, short term (max.)

Average

150

Heat deflection temperature

DIN EN ISO 306, Vicat B

85

Thermal properties

Electrical properties
Dielectric constant

IEC 60250

2,5

Dielectric dissipation factor (106Hz)

IEC 60250

0,00019

Volume resistivity

IEC 60093

*cm

>1014

Surface resistivity

IEC 60093

>1013

Comparative tracking index

IEC 60112

Dielectric strength

IEC 60243

600
kV/mm

45

Date: 08/10/2014

The data stated above are average values ascertained by statistical tests on a regular basis. They are in accordance with DIN EN 15860. The data above are provided purely for information
and shall not be regarded as binding unless expressly agreed in a contract of sale.

Rchling Engineering Plastics SE & Co. KG


Rchlingstr. 1 D-49733 Haren/Germany Tel. +49 5934 701-0 Fax +49 5934 701-299 [email protected] www.roechling.com