The document provides specifications for manufacturing a barrel extension from SAE 8620 steel, including: 1) The steel alloy, heat treatment process of carburizing, stress relieving, hardening, and tempering. 2) Dimensions and tolerances for features on the part. 3) A note that threads must be masked during carburizing or processed to avoid carburization. 4) Requirements for minimum hardness values after stress relieving and surface finish standards.

Uploaded by

Geoff Crook
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
14K views1 page

Ar15 Barrel Extension New

The document provides specifications for manufacturing a barrel extension from SAE 8620 steel, including: 1) The steel alloy, heat treatment process of carburizing, stress relieving, hardening, and tempering. 2) Dimensions and tolerances for features on the part. 3) A note that threads must be masked during carburizing or processed to avoid carburization. 4) Requirements for minimum hardness values after stress relieving and surface finish standards.

Uploaded by

Geoff Crook
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
You are on page 1/ 1

NOTES:

1. SAE 8620 STEEL, AMS 6274 OR AMS 6276


B .005 DIA EXCEPT AS NOTED
2. ALL DIAMETERS
3. CARBURIZE TOTAL CASE DEPTH .010 TO .015
BEFORE GRIND. SUGGESTED HEAT TREAT
PROCEDURE: LIQUID CARBURIZE AT 1550 F
FOR 1-1/4 HOURS (CASE DEPTH .010 TO .015)
AIR COOL, WASH CLEAN. STRESS RELIEVE AT
850 F FOR 1 HOUR. ROUGH MACHINE, REHEAT
TO 1450 DEGREES F, OIL QUENCH, TEMPER AT 350 F
FOR 1 HOUR. THREAD TO BE MASKED OR
PART TO BE PROCESSED SO THREAD IS NOT
CARBURIZED.
4. OPTIONAL STRESS RELIEF PERMITTED IN AREA
SHOWN. MAXIMUM STRESS RELIEF TEMPERATURE
900 F. MINIMUM ALLOWABLE HARDNESS IN
THIS AREA SHALL BE RH 15N-85.5.
5. GRIND AFTER HEAT TREAT.
6. MINIMUM PERMISSIBLE CASE DEPTH .005
AFTER GRIND.
7. FINISH 63 EXCEPT AS NOTED.
8. FILLET RADII .010, EXCEPT AS NOTED.
9. BREAK SHARP EDGES .005-.010 EXCEPT AS NOTED.
10. MIL-W-13856 APPLIES.

22.50
BSC

32

+.000
.993 - .003
B .004 DIA

R.031
NOTES 5 AND 6 APPLY

.078

32

A
+.0000
.9987 - .0008

1.170

125

.160

.990

+.0015
.1235 - .0000
B .0032 TOTAL

1.121

.001
AUXILIARY
SECTION A-A
B .001
SCALE 2 : 1
K

13/16-16UN-3B
.020 X 45 CHAMFER TYP TO
MINOR DIA .745-.7533
THEORETICAL PROJECTED
PITCH DIA .7719-.7766
SHARP CORERS
MAJJOR DIA .8125 MIN
PITCH DIA MUST BE PARALLEL TO
AXIS -B- WITHIN .020 IN 10 INCHES
SLOTS -D- PERMISSIBLE ON MINOR
DIA.

.907.001

SECTION A-A
DETAIL D
SCALE 2 : 1

B .001

.830
X 90 4

UNLESS OTHERWISE SPECIFIED:

.125 R

DIMENSIONS ARE IN INCHES


TOLERANCES:
FRACTIONAL
ANGULAR: MACH
BEND
TWO PLACE DECIMAL
THREE PLACE DECIMAL
INTERPRET GEOMETRIC
TOLERANCING PER:
MATERIAL

NAME
DRAWN

USED ON
APPLICATION

MWB 02/19/13

CHECKED

DETAIL K
SCALE 2 : 1

TITLE:

BARREL EXTENSION

ENG APPR.
MFG APPR.
Q.A.
COMMENTS:

SIZE DWG. NO.

REV

FINISH

SHEET 1 OF 1

SCALE: 1:1 WEIGHT:

DO NOT SCALE DRAWING

TANGENT TO
.100 DIA
BASIC 8 PLACES

DATE

SAE 8620 STEEL

NEXT ASSY

NOTES 5 AND
6 APPLY

.001

22.50

22.50

.620

NOTES 5 AND 6 APPLY

.790
DIA

32

+.005
.572 - .000

.760.002

+.005
.830 - .000

R.015

R.010

+.003
.124 - .000
8 SLOTS
EQ SP

30 2

.020 X 45

You might also like