Magnetic Particle Inspection Report

This magnetic particle inspection report summarizes an inspection of ferromagnetic material for surface-breaking defects. The inspection was performed on [DATE] according to procedure SPT-OP-NDT-001 using AC yoke, prods, and coil equipment with a 1000 LUX light intensity and black particle ink. The material, surface condition, and scope of inspection are described. No visible indications of defect were found during the inspection. The report is signed by the level II certified inspector and is to be kept for a minimum of 3 years.

Uploaded by

Mim Ann Nur
Copyright
© © All Rights Reserved
Available Formats
Download as PDF, TXT or read online on Scribd
21 views

Magnetic Particle Inspection Report

This magnetic particle inspection report summarizes an inspection of ferromagnetic material for surface-breaking defects. The inspection was performed on [DATE] according to procedure SPT-OP-NDT-001 using AC yoke, prods, and coil equipment with a 1000 LUX light intensity and black particle ink. The material, surface condition, and scope of inspection are described. No visible indications of defect were found during the inspection. The report is signed by the level II certified inspector and is to be kept for a minimum of 3 years.

Uploaded by

Mim Ann Nur
Copyright
© © All Rights Reserved
Available Formats
Download as PDF, TXT or read online on Scribd
You are on page 1/ 1

Inspection, Certification, Non Destructive Testing, Heavy

Lift Consulting, Survey And Technical Supplier

Doc ID: SPT-OP-NDT-002

MAGNETIC PARTICLE INSPECTION REPORT

Effective Date: 10-07-2014

Revision No: 02

Client
Client Address

:
:

Report No.
Procedure No.

: RPT/SPT/UMW-N7/MPI/001
: SPT-OP-NDT-001

Location of Inspection

Refer to PO

Date of Inspection

Due Inspection

: -

Drawing No.
Material spec.
Light type
Contrast paint
Batch no. of

:
:
:
:
:

Welding process
Test Specification
Light intensity
Particle Ink

:
:
:
:
:

MPI equipment

Yoke

Prods

Coil

Type of current

AC

Permanent

HWDC / HWAC

Others

Type of Inspection

Dry

Wet

Fluorescent

Lifting Force Test

Method examination

Continuous

Residual

Non
Fluorescent

As forged

As Rolled

Others (As
Cast)

Pole Spacing

Others (After
clean)

Lifting Block

Surface condition

Ferromagnetic
Natural
WCP-2
1365002

As welded

Surface preparation

Brushing

Machining

Blasting

Time of inspection

After weld

After hydrotest

After PWHT

Scope of inspection

Base metal

Edge prep

Back chipping

Weld part

Repair weld

Others (

Description

Area Inspected

ASME Section V, Article 7 : 2010


1000 LUX
7HF
1485052
Equipment Idenfication

Accepted

Serial No. : 475

- 10 LBS

- 3" > 6"

- S/N: 15656
- Cal Due: April 2017

Rejected

Remarks

Pictures:

Acceptance Criteria : API RP 8B


Notes : : Ok , X : Not Ok , N/A : Not Applicable
Result : No visible indication of defect during the time of test.
Inspector Name & Signature : Mohd Farith Sahat

Inspector Certification : NDT Level II

Date :

Report to be kept 3 years minimum

Except for cases of proven negligence of fraud by SIAPTEK, the Client agrees to hold harmless and indemnify SIAPTEK and its inspectors, technicians, officers, employees, agents or subcontractors against all claims (actual or threatened) by them and by any third party for loss,
damage or expense of whatsoever nature including all legal expenses and related costs and however arising relating to the performance, purported performance or non-performance of the services or out of or in connection with Clients product, process or service the subject of the
certification including, without limitation, product liability claims. The total liability of SIAPTEK to the Client in respect of any claims for loss, damage or expense of any nature and howsoever arising shall be limited, in respect of any one event or series of connected events, to an
amount equal to US$ 1,000 (excluding Value Added Tax thereon).

www.siaptek.com