API 571 Part 4

The document discusses corrosion under insulation (CUI) and methods for inspecting and preventing it. It notes that carbon steels, 300 series stainless steels, and duplex stainless steels can experience localized corrosion under insulation. Common inspection techniques mentioned include visual examination after removing insulation, ultrasonic thickness measurements, guided wave ultrasonics, and infrared thermography to detect wet insulation. The document emphasizes developing an inspection plan considering equipment susceptibility and using multiple inspection techniques.

Uploaded by

Bashu Poudel
Copyright
© © All Rights Reserved
Available Formats
Download as PDF, TXT or read online on Scribd
601 views

API 571 Part 4

The document discusses corrosion under insulation (CUI) and methods for inspecting and preventing it. It notes that carbon steels, 300 series stainless steels, and duplex stainless steels can experience localized corrosion under insulation. Common inspection techniques mentioned include visual examination after removing insulation, ultrasonic thickness measurements, guided wave ultrasonics, and infrared thermography to detect wet insulation. The document emphasizes developing an inspection plan considering equipment susceptibility and using multiple inspection techniques.

Uploaded by

Bashu Poudel
Copyright
© © All Rights Reserved
Available Formats
Download as PDF, TXT or read online on Scribd
You are on page 1/ 20

API510/570-Exam

Valves and fittings (irregular insulation surfaces).

API510/570-Exam

4.3.3.5 Appearance or Morphology of Damage


a) Carbon and low alloy steels are subject to localized pitting corrosion and or
localized loss in thickness.
b) 300 Series SS are also subject to Stress Corrosion Cracking (SCC) if
chlorides are present, while the duplex SS are less susceptible.
c) 300 Series SS and duplex SS are subject to pitting and localized corrosion.
For 300 Series SS, specifically in older calcium silicate insulation (known to
contain chlorides), localized pitting and chloride stress corrosion cracking
can occur.
d) After insulation is removed from carbon and low alloy steels, CUI damage
often appears as loose, flaky scale covering the corroded component.
Damage may be highly localized (Figure 4-73 to 4-79).
e) In some localized cases, the corrosion can appear to be carbuncle type
pitting (usually found under a failed paint/coating system).
f) Tell tale signs of insulation and paint/coating damage often accompany
CUI.

API510/570-Exam

300 Series SS are also subject to Stress Corrosion


Cracking (SCC) if chlorides are present, while the
duplex SS are less susceptible

API510/570-Exam

4.3.3.6 Prevention / Mitigation


a) Since the majority of construction materials used in plants are susceptible
to CUI degradation, mitigation is best achieved by using appropriate
paints/coatings and maintaining the insulation/sealing/vapor barriers to
prevent moisture ingress.
b) Flame-sprayed aluminum coatings have been used on carbon steels. The
coating corrodes preferentially by galvanic action, thereby protecting the
base metal.
c) High quality non-metallic coatings, properly applied to the surfaces to be
insulated can provide long term protection.
d) Thin aluminum foil wrapped on stainless steel piping and equipment has
been used on stainless steels as an effective barrier under insulation.

API510/570-Exam

e) Careful selection of insulating materials is important. Closed-cell foam


glass materials will hold less water against the vessel/pipe wall than
mineral wool and potentially be less corrosive.
f) Low chloride insulation should be used on 300 Series SS to minimize the
potential for pitting and chloride SCC.
g) It is not usually possible to modify operating conditions. However,
consideration should be given to removing the insulation on equipment
where heat conservation is not as important.

API510/570-Exam

Closed-cell foam glass materials will


hold less water against the vessel/pipe
wall than mineral wool and potentially
be less corrosive

API510/570-Exam

4.3.3.7 Inspection and Monitoring


a) An inspection plan for corrosion under insulation should be a structured and
systematic approach starting with prediction/analysis, then looking at the
more invasive procedures. The inspection plan should consider operating
temperature; type and age/condition of coating; and type and age/condition
of insulation material. Additional prioritization can be added from a physical
inspection of the equipment, looking for evidence of insulation, mastic
and/or sealant damage, signs of water penetration and rust in gravity drain
areas around the equipment.
b) Although external insulation may appear to be in good condition, CUI
damage may still be occurring. CUI inspection may require removal of some
or all insulation. If external coverings are in good condition and there is no
reason to suspect damage behind them, it may not be necessary to remove
them for inspection of the vessel. ()

API510/570-Exam

c) Considerations for insulation removal are not limited to but include:


1.
2.
3.
4.
5.

History of CUI for the vessel or comparable equipment.


Visual condition of the external covering and insulation.
Evidence of fluid leakage, e.g. stains.
Equipment in intermittent service.
Condition/age of the external coating, if applicable.

d) Common areas of concern in process units are high moisture areas such
as those down-wind from cooling towers, near steam vents, deluge
systems, acid vapors, or near supplemental cooling with water spray.

API510/570-Exam

Common areas of concern in process units are high moisture areas

API510/570-Exam

e) When developing the inspection plan for CUI inspection, the inspector
should consider
1. Areas that are most susceptible to CUI. If CUI damage is found, the
inspector should inspect other susceptible areas on the vessel.
2. Utilize multiple inspection techniques to produce the most cost effective
approach, including:

Partial and/or full stripping of insulation for visual examination.


UT for thickness verification.
Real-time profile x-ray (for small bore piping).
Neutron backscatter techniques for identifying wet insulation.
Deep penetrating eddy-current inspection (can be automated with a
robotic crawler).
IR thermography looking for wet insulation and/or damaged and missing
insulation under the jacket.
Guided wave UT.

API510/570-Exam

4.3.3.8 Related Mechanisms


Atmospheric corrosion (see 4.3.2), oxidation (see 4.4.1) and chloride SCC (see
4.5.1).

API510/570-Exam

Guided wave UT

API510/570-Exam

Guided wave UT

API510/570-Exam

UT for thickness verification

API510/570-Exam

UT for thickness verification

http://www.impresub.com/en/services/ndt-inspection.html

API510/570-Exam

UT for thickness verification

API510/570-Exam

API510/570-Exam

API510/570-Exam

API510/570-Exam

Figure 4-73 Tee in a 1000 psig ethylene line before insulation removal.