Material Specification Sheet Saarstahl - C45: 1.0503 BS: Afnor: Sae: Material Group: Chemical Composition: Application

This document provides material specification details for Saarstahl C45 steel. It lists the material number, international grades, chemical composition ranges, applications, heat treatment processes, and mechanical properties. Saarstahl C45 is a plain carbon steel suitable for mechanical engineering and automotive components. It can be hardened through quenching and tempering, with a minimum 0.2% proof stress of 490 MPa and tensile strength between 700-850 MPa.

Uploaded by

shankarjb
Copyright
© Attribution Non-Commercial (BY-NC)
Available Formats
Download as PDF, TXT or read online on Scribd
1K views

Material Specification Sheet Saarstahl - C45: 1.0503 BS: Afnor: Sae: Material Group: Chemical Composition: Application

This document provides material specification details for Saarstahl C45 steel. It lists the material number, international grades, chemical composition ranges, applications, heat treatment processes, and mechanical properties. Saarstahl C45 is a plain carbon steel suitable for mechanical engineering and automotive components. It can be hardened through quenching and tempering, with a minimum 0.2% proof stress of 490 MPa and tensile strength between 700-850 MPa.

Uploaded by

shankarjb
Copyright
© Attribution Non-Commercial (BY-NC)
Available Formats
Download as PDF, TXT or read online on Scribd
You are on page 1/ 2

Material specification sheet

Saarstahl - C45
Material No.: Former brand name: International steel grades:

1.0503 BS: C45, 50CS, 080M46


AFNOR: C45, AF65C45, 1C45
SAE: 1045

Material group: Steel for quenching and tempering according to DIN EN 10083
Cr+Mo+
Chemical C Si Mn P S Cr Mo Ni
Ni
composition: 0,42 0,50
(Typical analysis in %) <0,40 <0,045 <0,045 <0,40 <0,10 0,40 <0,63
0,50 0,80

Application: Plain carbon steel for mechanical engineering and automotive


components

Hot forming and Forging or hot rolling: 1100 - 850°C


heat treatment:
Normalising: 840 - 880°C/air
Soft annealing: 680 - 710°C/furnace
Hardening: 820 - 860°C/water, oil
Tempering: 550 - 660°C/air

Mechanical Treated for cold shearability +S: max. 255 HB


Properties: Soft annealed +A: max. 207 HB

Quenched and tempered, +QT:

Diameter d [mm] < 16 >16 – 40 >40 – 100 >100 – 160 >160 – 250

Thickness t [mm] <8 8<t<20 20<t<60 60<t<100 100<t<160

0,2% proof stress


Rp0,2 [N/mm²] min. 490 min. 430 min. 370 - -

Tensile strength Rm [N/mm²] 700 - 850 650 - 800 630 - 780 - -

Fracture elongation A5 [%] min. 14 min. 16 min. 17 - -

Reduction of area Z [%] min. 35 min. 40 min. 45 - -


Normalised, +N:

Diameter d [mm] < 16 >16 – 100 >100 – 250

Thickness t [mm] < 16 16<t<100 100<t<250

0,2% proof stress


Rp0,2 [N/mm²] min. 340 min. 305 min. 275

Tensile strength Rm [N/mm²] min. 620 min. 580 min. 560

Fracture elongation A5 [%] min. 14 min. 16 min. 16