ABSTRACT Microelectromechanical systems (MEMS) (also written as micro-electro-mechanical, or MicroElectroMechanical) is the technology of the very small, and merges at the nanoscale intonanoelectromechanical systems (NEMS) and nanotechnology. MEMS technology can be implemented using a number of different materials and manufacturing techniques; the choice of which will depend on the device being created and the market sector in which it has to operate. MEMS promises to revolutionize nearly every product category by bringing together silicon-based microelectronics with micromachining technology, making possible the realization of complete systems-on-a-chip.

WHAT IS MEMS TECHNOLOGY?

Micro-Electro-Mechanical Systems (MEMS) is the integration of mechanical elements, sensors, actuators, and electronics on a common silicon substrate through microfabrication technology. Microelectromechanical systems (MEMS) (also written asmicro-electro-mechanical, or MicroElectroMechanical) is the technology of the very small, and merges at the nanoscale intonanoelectromechanical systems (NEMS) and nanotechnology. MEMS are also referred to as micromachines (in Japan), orMicro Systems Technology - MST (in Europe). MEMS are separate and distinct from the hypothetical vision of molecular nanotechnology or molecular electronics. MEMS are made up of components between 1 to 100 micrometres in size (i.e. 0.001 to 0.1 mm) and MEMS devices generally range in size from 20 micrometres (20 millionths of a metre) to a millimetre. They usually consist of a central unit that processes data, the microprocessor and several components that interact with the outside such as microsensors. At these size scales, the standard constructs of classical physics do not always hold true. Due to MEMS large surface area to volume ratio, surface effects such as electrostatics and wetting dominate volume effects such as inertia or thermal mass.

HISTORICAL BACKGROUND

The invention of the transistor at Bell Telephone Laboratories in 1947 sparked a fastgrowing microelectronic technology. Jack Kilby of Texas Instruments built the firstintegrated circuit (IC) in 1958 using germanium (Ge) devices. It consisted of one transistor, three resistors, and one capacitor. The IC was implemented on a sliver of Ge that was glued on a glass slide. Later that same year Robert Noyce of Fairchild Semiconductor announced the development of a planar double-diffused Si IC. The complete transition from the original Ge transistors with grown and alloyed junctions to silicon (Si) planar double-diffused devices took about 10 years. The success of Si as an electronic material was due partly to its wide availability from silicon dioxide (SiO2) (sand), resulting in potentially lower material costs relative to other semiconductors. Since 1970, the complexity of ICs has doubled every two to three years. The minimum dimension of manufactured devices and ICs has decreased from 20 microns to the sub micron levels of today. Current ultra-large-scale-integration (ULSI) technology enables the fabrication of more than 10 million transistors and capacitors on a typical chip. IC fabrication is dependent upon sensors to provide input from the surrounding environment, just as control systems need actuators (also referred to as transducers) in order to carry out their desired functions. Due to the availability of sand as a material, much effort was put into developing Si processing and characterization tools. These tools are now being used to advance transducer technology. Todays IC technology far outstrips the original sensors and actuators in performance, size, and cost. Attention in this area was first focused on microsensor (i.e., microfabricated sensor) development. The first microsensor, which has also been the most successful, was the Si pressure sensor. In 1954 it was discovered that the piezoresistive effect in Ge and Si had the potential to produce Ge and Si strain gauges with a gauge factor (i.e., instrument sensitivity) 10 to 20 times greater than those based on metal films. As a result, Si strain gauges began to be developed commercially in 1958. The first high-volume pressure sensor was marketed by National Semiconductor in 1974. This sensor included a temperature controller for constant-temperature operation. Improvements in this technology since then have included the utilization of ion implantation for improved

control of the piezoresistor fabrication. Si pressure sensors are now a billion-dollar industry. Around 1982, the term micromachining came into use to designate the fabrication of micromechanical parts (such as pressure-sensor diaphragms or accelerometer suspension beams) for Si microsensors. The micromechanical parts were fabricated by selectively etching areas of the Si substrate away in order to leave behind the desired geometries. Isotropic etching of Si was developed in the early 1960s for transistor fabrication. Anisotropic etching of Si then came about in 1967. Various etch-stop techniques were subsequently developed to provide further process flexibility.

These techniques also form the basis of the bulk micromachining processing techniques. Bulk micromachining designates the point at which the bulk of the Si substrate is etched away to leave behind the desired micromechanical elements. Bulk micromachining has remained a powerful technique for the fabrication of micromechanical elements. However, the need for flexibility in device design and performance improvement has motivated the development of new concepts and techniques for micromachining.

Among these is the sacrificial layer technique, first demonstrated in 1965 by Nathanson and Wickstrom, in which a layer of material is deposited between structural layers for mechanical separation and isolation. This layer is removed during the release etch to free the structural layers and to allow mechanical devices to move relative to the substrate. A layer is releasable when a sacrificial layer separates it from the substrate. The application of the sacrificial layer technique to micromachining in 1985 gave rise to surface micromachining, in which the Si substrate is primarily used as a mechanical support upon which the micromechanical elements are fabricated.

Prior to 1987, these micromechanical structures were limited in motion. During 1987-1988, a turning point was reached in micromachining when, for the first time,

techniques for integrated fabrication of mechanisms (i.e. rigid bodies connected by joints for transmitting, controlling, or constraining relative movement) on Si were demonstrated. During a series of three separate workshops on microdynamics held in 1987, the term MEMS was coined. Equivalent terms for MEMS are microsystems (preferred in Europe) and micromachines (preferred in Japan).

MEMS DESCRIPTION MEMS technology can be implemented using a number of different materials and manufacturing techniques; the choice of which will depend on the device being created and the market sector in which it has to operate.

MATERIALS FOR MEMS MANUFACTURING

Silicon Silicon is the material used to create most integrated circuits used in consumer electronics in the modern world. The economies of scale, ready availability of cheap high-quality materials and ability to incorporate electronic functionality make silicon attractive for a wide variety of MEMS applications. Silicon also has significant advantages engendered through its material properties. In single crystal form, silicon is an almost perfect Hookean material, meaning that when it is flexed there is virtually nohysteresis and hence almost no energy dissipation. As well as making for highly repeatable motion, this also makes silicon very reliable as it suffers very little fatigue and can have service lifetimes in the range of billions to trillions of cycles without breaking. The basic techniques for producing all silicon based MEMS devices are deposition of material layers, patterning of these layers by photolithographyand then etching to produce the required shapes. Polymers Even though the electronics industry provides an economy of scale for the silicon industry, crystalline silicon is still a complex and relatively expensive material to produce. Polymers on the other hand can be produced in huge volumes, with a great variety of material characteristics. MEMS devices can be made from polymers by processes such as injection moulding, embossing or stereolithography and are especially well suited to microfluidic applications such as disposable blood testing cartridges.

Metals Metals can also be used to create MEMS elements. While metals do not have some of the advantages displayed by silicon in terms of mechanical properties, when used within their limitations, metals can exhibit very high degrees of reliability. Metals can be deposited by electroplating, evaporation, and sputtering processes. Commonly used metals

include gold, nickel, aluminium, chromium, titanium, tungsten, platinum, andsilver.

FABRICATION TECHNOLOGIES The three characteristic features of MEMS fabrication technologies are miniaturization, multiplicity, and microelectronics. Miniaturization enables the production of compact, quick-response devices. Multiplicity refers to the batch fabrication inherent in semiconductor processing, which allows thousands or millions of components to be easily and concurrently fabricated. Microelectronics provides the intelligence to MEMS and allows the monolithic merger of sensors, actuators, and logic to build closed-loop feedback components and systems. The successful miniaturization and multiplicity of traditional electronics systems would not have been possible without IC fabrication technology. Therefore, IC fabrication technology, or microfabrication, has so far been the primary enabling technology for the development of MEMS. Microfabrication provides a powerful tool for batch processing and miniaturization of mechanical systems into a dimensional domain not accessible by conventional (machining) techniques. Furthermore, microfabrication provides an opportunity for integration of mechanical systems with electronics to develop high-performance closed-loop-controlled MEMS.

Advances in IC technology in the last decade have brought about corresponding progress in MEMS fabrication processes. Manufacturing processes allow for the monolithic integration of microelectromechanical structures with driving, controlling, and signalprocessing electronics. This integration promises to improve the performance of micromechanical devices as well as reduce the cost of manufacturing, packaging, and instrumenting these devices. IC Fabrication Any discussion of MEMS requires a basic understanding of IC fabrication technology, or microfabrication, the primary enabling technology for the development of MEMS. The major steps in IC fabrication technology are film growth, doping, lithography, etching, dicing, and packaging.

Film growth: Usually, a polished Si wafer is used as the substrate, on which a thin film is grown. The film, which may be epitaxial Si, SiO2, silicon nitride (Si3N4), polycrystalline Si (polysilicon), or metal, is used to build both active or passive components and interconnections between circuits.

Doping: To modulate the properties of the device layer, a low and controllable level of an atomic impurity may be introduced into the layer by thermal diffusion or ion implantation.

Lithography: A pattern on a mask is then transferred to the film by means of a photosensitive (i.e., light sensitive) chemical known as a photoresist. The process of pattern generation and transfer is called photolithography. A typical mask consists of a glass plate coated with a patterned chromium (Cr) film.

Etching: Next is the selective removal of unwanted regions of a film or substrate for pattern delineation. Wet chemical etching or dry etching may be used. Etch-mask materials are used at various stages in the removal process to selectively prevent those portions of the material from being etched. These materials include SiO2, Si3N4, and hard-baked photoresist. Dicing: The finished wafer is sawed or machined into small squares, or dice, from which electronic components can be made. Packaging: The individual sections are then packaged, a process that involves physically locating, connecting, and protecting a device or component. MEMS design is strongly coupled to the packaging requirements, which in turn are dictated by the application environment. Surface Micromachining Surface micromachining enables the fabrication of complex multicomponent integrated micromechanical structures that would not be possible with traditional bulk

micromachining. This technique encases specific structural parts of a device in layers of a sacrificial material during the fabrication process. The substrate wafer is used primarily as a mechanical support on which multiple alternating layers of structural and sacrificial material are deposited and patterned to realize micromechanical structures. The sacrificial material is then dissolved in a chemical etchant that does not attack the structural parts. The most widely used surface micromachining technique, polysilicon surface micromachining, uses SiO2 as the sacrificial material and polysilicon as the structural material.

At the University of Wisconsin at Madison, polysilicon surface micromachining research started in the early 1980s in an effort to create high-precision micro pressure sensors. The control of the internal stresses of a thin film is important for the fabrication of microelectromechanical structures. The microelectronic fabrication industry typically grows polysilicon, silicon nitride, and silicon dioxide films using recipes that minimize time. Unfortunately, a deposition process that is optimized to speed does not always create a low internal stress film. In fact, most of these films have internal stresses that are highly compressive (tending to contract). A freestanding plate of highly compressive polysilicon that is held at all its edges will buckle (i.e., collapse or give way). This is highly undesirable. The solution is to modify the film deposition process to control the internal stress by making it stress-free or slightly tensile.

One way to do this is to dope the film with boron, phosphorus, or arsenic. However, a doped polysilicon film is conductive, and this property may interfere with the mechanical devices incorporated electronics. Another problem with doped polysilicon is that it is roughened by hydrofluoric acid (HF), which is commonly used to free sections of the final mechanical device from the substrate. Rough polysilicon has different mechanical properties than smooth polysilicon. Therefore, the amount of roughening must be taken into account when designing the mechanical parts of the micro device.

A better way to control the stress in polysilicon is through post annealing, which involves the deposition of pure, fine-grained, compressive (i.e., can be compressed) polysilicon. Annealing the polysilicon after deposition at elevated temperatures can change the film to be stress-free or tensile. The annealing temperature sets the films final stress. After this, electronics can then be incorporated into polysilicon films through selective doping, and hydrofluoric acid will not change the mechanical properties of the material.

Deposition temperature and the films silicon to nitride ratio can control the stress of a silicon nitride (Si3N4) film. The films can be deposited in compression, stress-free, or in tension.

Deposition temperature and post annealing can control silicon dioxide (SiO2) film stress. Because it is difficult to control the stress of SiO2 accurately, SiO2 is typically not used as a mechanical material by itself, but as electronic isolation or as a sacrificial layer under polysilicon. Micromolding In the micromolding process, microstructures are fabricated using molds to define the deposition of the structural layer. The structural material is deposited only in those areas constituting the microdevice structure, in contrast to bulk and surface micromachining, which feature blanket deposition of the structural material followed by etching to realize the final device geometry. After the structural layer deposition, the mold is dissolved in a chemical etchant that does not attack the structural material. One of the most prominent micromolding processes is the LIGA process. LIGA is a German acronym standing for lithographie, galvanoformung, und abformung (lithography, electroplating, and molding). This process can be used for the manufacture of high-aspect-ratio 3D microstructures in a wide variety of materials, such as metals, polymers, ceramics, and glasses. Photosensitive polyimides are also used for fabricating plating molds. The photolithography process is similar to conventional photolithography, except that polyimide works as a negative resist.

High aspect ratio (HAR) silicon micromachining In many cases the distinction between these two has diminished. A new etching technology, deep reactive ion etching, has made it possible to combine good performance typical of bulk micromachining with comb structures and in-plane operation typical of surface micromachining. While it is common in surface micromachining to have structural layer thickness in the range of 2 m, in HAR silicon micromachining the thickness can be from 10 to 100 m. The materials commonly used in HAR silicon micromachining are thick polycrystalline silicon, known as epi-poly, and bonded siliconon-insulator (SOI) wafers although processes for bulk silicon wafer also have been created (SCREAM). Bonding a second wafer by glass frit bonding, anodic bonding or alloy bonding is used to protect the MEMS structures. Integrated circuits are typically not combined with HAR silicon micromachining. The consensus of the industry at the moment seems to be that the flexibility and reduced process complexity obtained by having the two functions separated far outweighs the small penalty in packaging. A comparison of different high-aspect-ratio microstructure technologies can be found in the HARMST article.

APPLICATIONS Pressure Sensors MEMS pressure microsensors typically have a flexible diaphragm that deforms in the presence of a pressure difference. The deformation is converted to an electrical signal appearing at the sensor output. A pressure sensor can be used to sense the absolute air pressure within the intake manifold of an automobile engine, so that the amount of fuel required for each engine cylinder can be computed. In this example, piezoresistors are patterned across the edges of a region where a silicon diaphragm will be micromachined. The substrate is etched to create the diaphragm. The sensor die is then bonded to a glass substrate, creating a sealed vacuum cavity under the diaphragm. The die is mounted on a package, where the topside of the diaphragm is exposed to the environment. The change

in ambient pressure forces the downward deformation of the diaphragm, resulting in a change of resistance of the piezoresistors. On-chip electronics measure the resistance change, which causes a corresponding voltage signal to appear at the output pin of the sensor package. Accelerometers Accelerometers are acceleration sensors. An inertial mass suspended by springs is acted upon by acceleration forces that cause the mass to be deflected from its initial position. This deflection is converted to an electrical signal, which appears at the sensor output. The application of MEMS technology to accelerometers is a relatively new development.

One such accelerometer design is discussed by DeVoe and Pisano (2001). It is a surface micromachined piezoelectric accelerometer employing a zinc oxide (ZnO) active piezoelectric film. The design is a simple cantilever structure, in which the cantilever beam serves simultaneously as proof mass and sensing element. One of the fabrication approaches developed is a sacrificial oxide process based on polysilicon surface micromachining, with the addition of a piezoelectric layer atop the polysilicon film. In the sacrificial oxide process, a passivation layer of silicon dioxide and low-stress silicon nitride is deposited on a bare silicon wafer, followed by 0.5 micron of liquid phase chemical vapor deposited (LPCVD) phosphorous-doped polysilicon. Then, a 2.0micron layer of phosphosilicate glass (PSG) is deposited by LPCVD and patterned to define regions where the accelerometer structure will be anchored to the substrate. The PSG film acts as a sacrificial layer that is selectively etched at the end to free the mechanical structures. A second layer of 2.0-micron-thick phosphorus-doped polysilicon is deposited via LPCVD on top of the PSG, and patterned by plasma etching to define the mechanical accelerometer structure. This layer also acts as the lower electrode for the sensing film. A thin layer of silicon nitride is next deposited by LPCVD, and acts as a stress-compensation layer for balancing the highly compressive residual stresses in the ZnO film. By varying the thickness of the Si3N4 layer, the accelerometer structure may be tuned to control bending effects resulting from the stress gradient through the device thickness. A ZnO layer is then deposited on the order of 0.5 micron, followed

bysputtering of a 0.2-micron layer of platinum (Pt) deposited to form the upper electrode. A rapid thermal anneal is performed to reduce residual stresses in the sensing film. Afterwards, the Pt, Si3N4, and ZnO layers are patterned in a single ion milling etch step, and the devices are then released by passivating the ZnO film with photoresist, and immersing the wafer in buffered hydrofluoric acid, which removes the sacrificial PSG layer.

Inertial Sensors Inertial sensors are a type of accelerometer and are one of the principal commercial products that utilize surface micromachining. They are used as airbag-deployment sensors in automobiles, and as tilt or shock sensors. The application of these accelerometers to inertial measurement units (IMUs) is limited by the need to manually align and assemble them into three-axis systems, and by the resulting alignment tolerances, their lack of in-chip analog-to-digital conversion circuitry, and their lower limit of sensitivity. A three-axis force-balanced accelerometer has been designed at the University of California, Berkeley, to overcome some of these limitations. The accelerometer was designed for the integrated MEMS/CMOS technology. This technology involves a manufacturing technique where a single-level (plus a second electrical interconnect level) polysilicon micromachining process is integrated with 1.25micron CMOS.

Microengines A three-level polysilicon micromachining process has enabled the fabrication of devices with increased degrees of complexity. The process includes three movable levels of polysilicon, each separated by a sacrificial oxide layer, plus a stationary level. Operation of the small gears at rotational speeds greater than 300,000 rpm has been demonstrated. Microengines can be used to drive the wheels of microcombination locks. They can also

be used in combination with a microtransmission to drive a pop-up mirror out of a plane. This device is known as a micromirror.

Some other applications MEMS IC fabrication gears to transfer power. A recently developed MicroStar cross-connect fabric developed by Bell Labs, a microoptoelectromechanical system device, is based on MEMS technology. The most pervasive bottlenecks for communications carriers are the switching and cross-connect fabrics that switch, route, multiplex, demultiplex, and restore traffic in optical networks. The optical transmission systems move information as photons, but switching and crossconnect fabrics until now have been largely electronic, requiring costly and timeconsuming bandwidth-limiting optical-to-electronic-to-optical conversions at every network connection and cross point. MicroStar is composed of 256 mirrors, each one 0.5 mm in diameter, spaced 1 mm apart, and covering less than 1 square inch of silicon. The mirrors sit within the router so that only one wavelength can illuminate any one mirror. Each mirror can tilt independently to pass its wavelength to any of 256 input and output fibers. The mirror arrays are made using a self-assembly process that causes a frame around each mirror to lift from the silicon surface and lock in place, positioning the mirrors high enough to allow a range of movement. MicroStar is part of Lucent Technologys Lambda Router cross-connect system aimed at helping carriers deliver vast amounts of data unimpeded by conventional bottlenecks. technologies have also allowed the manufacture of

microtransmissions using sets of small and large gears interlocking with other sets of

As a final example, MEMS technology has been used in fabricating vaporization microchambers for vaporizing liquid microthrusters for nanosatellites. The chamber is part of a microchannel with a height of 2-10 microns, made using silicon and glass

substrates. The nozzle is fabricated in the silicon substrate just above a thin-film indium tin oxide heater deposited on glass.

RESEARCH AND DEVELOPMENT Researchers in MEMS use various engineering software tools to take a design from concept to simulation, prototyping and testing. Finite element analysis is often used in MEMS design. Simulation of dynamics, heat, and electrical domains, among others, can be performed by ANSYS, COMSOL and CoventorWare-ANALZYER. Other software, such as CoventorWare-ARCHITECT and MEMS-PRO, is used to produce a design layout suitable for delivery to a fabrication firm and even simulate the MEMS embedded in a system. Once prototypes are on-hand, researchers can test the specimens using various instruments, including laser doppler scanning vibrometers, microscopes, and stroboscopes.

THE FUTURE

Each of the three basic microsystems technology processes we have seen, bulk micromachining, sacrificial surface micromachining, and micromolding/LIGA, employs a different set of capital and intellectual resources. MEMS manufacturing firms must choose which specific microsystems manufacturing techniques to invest in.

MEMS technology has the potential to change our daily lives as much as the computer has. However, the material needs of the MEMS field are at a preliminary stage. A thorough understanding of the properties of existing MEMS materials is just as important as the development of new MEMS materials.

Future MEMS applications will be driven by processes enabling greater functionality through higher levels of electronic-mechanical integration and greater numbers of mechanical components working alone or together to enable a complex action. Future MEMS products will demand higher levels of electrical-mechanical integration and more intimate interaction with the physical world. The high up-front investment costs for largevolume commercialization of MEMS will likely limit the initial involvement to larger companies in the IC industry. Advancing from their success as sensors, MEMS products will be embedded in larger non-MEMS systems, such as printers, automobiles, and biomedical diagnostic equipment, and will enable new and improved systems.