Palladium Refining Tutorial
Palladium Refining Tutorial
Best
Rate
vote
com_content
79
Palladium (Pd) refining can be a daunting task, similar to the other Platinum group metals (PGM's) refining process. This is mainly due to their similar (but different) physical and chemical properties. Separating Palladium from base metals and especially from sister PGM's, is rarely achieved completely in one refining cycle. Sounds kind of rough, but rest assured that this process is doable, even by the non-chemist in a garage lab. However, basic experience and acquaintance with lab techniques and chemicals is required. In this step by step tutorial a process of refining and re-refining Palladium metal is described in detail (including a video tutorial, see bottom of page). It covers attaining a desirable purity of 99.9 and above metal sponge. Melting of the metal is only briefly overviewed mainly because most buyers of Palladium metal prefer it in powder form (or as salt) rather then a bullion bar or an unmarked button. This is a refining process in which the initial feedstock is already of relatively high PGM content and has little to no presence of base metals. Recovered black PGM powder (AKA 'PGM black') can have a variety of sources; whether it is Catalytic Converters, Monolithic Ceramic Capacitors, Dental scrap or any other source, in which a recovery process is applied. It is important to mention that almost every step in the following described process can be performed using an alternative method. Therefore, the writer does not claim this process to be the only or the best one. One should take the time to do more research on the alternatives, some of which are mentioned here.
IMPORTANT SAFETY NOTE: All procedures described here MUST only be performed outdoors and away from people and animals, or in a fume hood. The reader has sole responsibility not to hurt himself or others when following this tutorial.
Neutralization of AR solution.
Neutralizing the solution basically means to make sure there is no more free Nitric Acid as well as nitrate ions left in solution. This can be achieved by means of slow evaporation and repeated additions of HCl. That's why you were advised earlier to use only minimal amounts of rinse water. - Place the wide beaker on heating element, set on low heat and allow the solution to slowly evaporate (NOTE: Do not boil!). - When the solution turns to syrup like consistency and crystallizations start to appear, add enough HCl to dissolve the crystals and shift the solution consistency back like water. Notice if brown fumes are emitted upon addition of HCl. If so, repeat the previous step again until no more
brown fumes appear. The color of the solution is basically orange but the high concentration makes it look like blood, almost brown.
As you probably understand by now, when working with any of the Platinum group metals, the key to the process success and for achieving good separation, is to work with concentrated solutions. - Transfer the solution to a more graduated flask or cup if needed.
When called for, use this solution only when it is very cold to insure it will not dissolve any salts. When not in use, store it back in the fridge or ice bate. For convenience sake, we will refer to this wash solution as wash 'solution A' to distinguish it from water washes or other steps that call for the use of Ammonium Chloride.
- Add just a little of the above solution to the PGM bearing solution and observe. If Platinum (Pt) is present in the solution, it will come down at once as bright yellow crystals of Ammonium Hexachloroplatinate (NH4)2PtCl6. Rhodium (Rh) will come out with the Platinum if present. Iridium (Ir) will also come out of solution upon addition of NH4Cl, but will take its time doing so. If Iridium is suspected to be in the solution, wait at least 1-2 hours before moving on to the next step. Remember, the more concentrated the PGM solution, the faster it will drop.
- If any colored salts form upon addition of Ammonium chloride, filter them out with a Vacuum System (Amazon Link) and wash it in the filter several times with 'solution A' until wash solution turns out clear of color. Using a vacuum filter system will reduce this step (and further steps) down to few minutes and minimize the use of wash solution. Try not to dilute the main liquor too much. The solution now contains mostly Palladium (and Ru / base metals if present). If too dilute, evaporate the solution down once again to a more concentrated volume.
- There are several ways to introduce Chlorine to the solution, each with its own pro's and con's. In the Video Tutorial, a chlorine gas generator was used and the gas was bubbled through the solution. An alternative, is to use Sodium/Potassium Chlorate, adding few crystals at a time and let tem react completely before next addition, the chlorates react with the acid to form Cl gas within the solution.
Be VERY careful handling and storing chlorates, especially Sodium chlorate, those are strong oxidizers that can prove explosive if not handled correctly. Another alternative is to use dry pure Sodium/Calcium Hypochlorite pellets or granules, again adding slowly and let them react completely before adding more. Bleach (clorox 3% and higher) can also be used to provide the Chlorine. - Keep adding Chlorine until no more red palladium salt is forms. -Notice the color of the solution. It should be much lighter in color as the Pd drops out of solution. Add a bit more ammonium salt and more chlorine to make sure no more Pd can be precipitated (due to low Pd ppm). - Using a Vacuum filter system, filter the brick red Pd powder. Wash the filter and powder several times with 'solution A' until washes come out clear of color.
- The left over dilute solution will be treated again with Aluminum / Zinc to precipitate any left over PGM's and then combined with the next batch. At this point one can choose to re-refine the brick red palladium salt (recommended) or move on to the conversion step. Converting the palladium salt at this point will most likely produce a final product purity of above 99% (depending on starting material). To ensure purity of 99.9% and above, a re-refining step is necessary.
Best
Rate
vote
com_content
80
Re-refining demonstration
Calcining of small quantities (up to few ounces of salt) can be performed in a fused quartz dish or in a high end (German made) borosilicate crystallization dish. It is important that the dish can take the heat of the process which will exceed 400C (752F). Larger batches are usually done in specialized quartz vessels that fit into a tube furnace. The calcining process is shared by other PGM salts and is done pretty much the same way. An alternative method to calcining is a reduction of the Pd salt with Formic acid in aqueous conditions. - Let the colored Pd salt dry on the filter for few days (or force dry with gentle warm air flow). Once dried, break the caked powder and transfer as much of it as possible to the crystallization dish. Soak the filter paper with the left over powder in warm water do dissolve traces of Pd Salt and combine it with former left over dilute Palladium solutions to be recovered later with Zinc/Aluminum. - Place the dish on a hotplate and set it on low heat. As in the picture, use sand to evenly spread the heat across the dish, thus, preventing thermal shock to the glass.
Soon, white smoke will appear and the powder will start changing colors as it converts. Temperature must be raised slowly and gradually. A sudden spike in temperature will cause values to escape with the smoke. The smoke needs to be only white, any other color to it, is a sure sign that some values are evaporating. You can better test the color of the smoke by holding a flask filled with ice water above the smoke and notice the color of the condensation. - Raise temperature gradually and slowly (every few minutes take it up a notch) to max heat. Most hot plates max out at around 350-400C. The process is pretty much done when all that's left is gray/black powder and no more white smoke is
emitted. If a thick layer of powder is calcined, it is recommended to mix the powder with a glass rod to fully expose all of the salt to the heat. Yellow Palladosammine Chloride salt will convert to metal sponge at much lower temperature then brick red Ammonium Hexachloropalladate salt. It only takes about 150C (302F). One more good reason (out of many) why one should re-refine Palladium salt. The entire calcining process should take about 1-2 hours, depending on batch size. The bigger the batch, the longer it takes. - When the calcining process is done and the Palladium sponge has cooled down to ambient temperature, wash is once or twice with warm water to remove traces of Pd salt that had not converted to metal, join this wash with previous dilute Pd solutions to be recovered later. - Dry and collect the black Palladium powder. Store it in an air tight bag or vial. The reason for an air tight storing of the powder is because Palladium is a catalyst. It will slowly react with Carbon monoxide in the atmosphere to form carbonates on the surface of the metal. The phenomena can affect metal purity later, while melting it.
---------------------------------------------------------------------------------------------------------------------------The Palladium powder/sponge is ready to be sold or stored as is. If one wishes to melt it, it is highly recommended to melt it in a high back fused silica (Amazon Link) or alumina melting dish under Oxy/hydrogen flame or alternatively, in an induction furnace. Melting Palladium with a Fuel/Oxy based torch (e.g. propane, acetylene) may prove troublesome for the same reason mentioned above. The metal may absorb carbon, resulting in a dark blackish metal rather than silvery white.