Procedure To Determine The Ductility of Bitumen

This document outlines the procedure to determine the ductility of bitumen using a three step process: 1) Completely melt the bituminous material and pour it into a mould to cool for 30-40 minutes before placing in a water bath at a specified temperature for 85-95 minutes. 2) Remove the briquette specimen from the mould and place in a testing machine, pulling the clips apart at a uniform speed until the briquette ruptures. 3) The ductility is reported as the average distance in cm that the clips were pulled to produce rupture in three normal tests that are within ±0.5 percent of their mean value.

Uploaded by

aditya singh
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
42 views1 page

Procedure To Determine The Ductility of Bitumen

This document outlines the procedure to determine the ductility of bitumen using a three step process: 1) Completely melt the bituminous material and pour it into a mould to cool for 30-40 minutes before placing in a water bath at a specified temperature for 85-95 minutes. 2) Remove the briquette specimen from the mould and place in a testing machine, pulling the clips apart at a uniform speed until the briquette ruptures. 3) The ductility is reported as the average distance in cm that the clips were pulled to produce rupture in three normal tests that are within ±0.5 percent of their mean value.

Uploaded by

aditya singh
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
You are on page 1/ 1

Procedure

to

determine

the

Ductility

Of

Bitumen

i) Completely melt the bituminous material to be tested by heating it to a temperature of 75


to 100oC above the approximate softening point until it becomes thoroughly fluid. Assemble
the mould on a brass plate and in order to prevent the material under test from sticking,
thoroughly coat the surface of the plate and the interior surfaces of the sides of the mould
with a mixture of equal parts of glycerine and dextrin. While filling, pour the material in a thin
stream back and forth from end to end of the mould until it is more than level full. Leave it
to cool at room temperature for 30 to 40 minutes and then place it in a water bath maintained
at the specified temperature for 30 minutes, after which cut off the excess bitumen by means
of a hot, straight-edged putty knife or spatula, so that the mould is just level full. ii) Place the
brass plate and mould with briquette specimen in the water bath and keep it at the specified
temperature for about 85 to 95 minutes. Remove the briquette from the plate, detach the
side pieces and the briquette immediately.
iii) Attach the rings at each end of the two clips to the pins or hooks in the testing machine
and pull the two clips apart horizontally at a uniform speed, as specified, until the briquette
ruptures. Measure the distance in cm through which the clips have been pulled to produce
rupture. While the test is being done, make sure that the water in the tank of the testing
machine covers the specimen both above and below by at least 25mm and the temperature
is

maintained

continuously

within

REPORTING

0.5oC
OF

of

the

specified

temperature.
RESULTS

A normal test is one in which the material between the two clips pulls out to a point or to a
thread and rupture occurs where the cross-sectional area is minimum. Report the average of
three normal tests as the ductility of the sample, provided the three determinations be within
0.5 percent of their mean value.