TDS Ep100-20

This document provides product information for a chromate-free 2K epoxy primer suitable for steel, zinc, aluminum and other substrates. The primer contains epoxy resin and has a solid content of 65-68% by weight. It protects against corrosion and can be used underwater or for chemical resistance. The primer can be applied by brush, roller or spray equipment and has a theoretical coverage rate of 26.3-27.4 sqm/kg at 10 microns thick. It is mixed at a 5:1 ratio with a hardener and has a pot life of 7-9 hours.

Uploaded by

radule021
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
220 views2 pages

TDS Ep100-20

This document provides product information for a chromate-free 2K epoxy primer suitable for steel, zinc, aluminum and other substrates. The primer contains epoxy resin and has a solid content of 65-68% by weight. It protects against corrosion and can be used underwater or for chemical resistance. The primer can be applied by brush, roller or spray equipment and has a theoretical coverage rate of 26.3-27.4 sqm/kg at 10 microns thick. It is mixed at a 5:1 ratio with a hardener and has a pot life of 7-9 hours.

Uploaded by

radule021
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
You are on page 1/ 2

EP 100-20

gb 11/1214

2K EP Primer
page 1 / 2

Product Information
Product description
Operational Sector :

Chromate free groundcoat based on 2K zinc phosphate epoxy


resin, suitable for steel, zinc plated steel, aluminium, glas fibre
reinforced materials and mineral substrates. Recommended as
groundcoat for use underwater and as protection coat against
chemical agents. Also suitable as intermediate coat by the
application of EP-Zinkstaubgrundierung.

Specification :

Binder base:
Solid content:

Features :

Theoret. Consumption :

26,3 - 27,4 m / kg (by 10 m dry coat thickness)


32,9 - 33,2 m / l (by 10 m dry coat thickness)

Storage :

In tightly closed original containers at least 3 years shelf life

VOC content :

EU limiting value for the product (cat. B/c): 540 g/l


This product contains max. 540 g/l VOC. [ 4.51 lbs/gal ]

epoxy resin
65 - 68 weight-%
44 - 45 volume-%
Delivery viscosity (DIN 53 211): thixotropic
Density (DIN EN ISO 2811):
1.4 - 1.5 kg / l
Gloss (DIN EN ISO 2813):
10 - 20 units / 60 (matt)
excellent protection against corrosion
electrostatically applicable
outstanding chemical and mechanical resistance
usable as insulation on thermoplastic substrate
short-term temperature exposure: 180C
permanent temperature exposure: 150C
adhesion test (DIN EN ISO 2409):
Steel, galvanized steel and aluminium: Gt 0 (very good);

Application
Processing Conditions:

From + 10 C and up to 80 % relative air humidity.

Substrate Preparation :

Steel: clean, eventually sand (remove rust, cinder, oxides) and


degrease with Mipa Silikonentferner.
Zinc: clean with ammonia alkaline wetting agent (Mipa
Zinkreiniger)
Aluminium: clean, sand and degrease with Mipa Silikonentferner (anti-silicone).

This data sheet is for information purpose only! To our knowledge the data provided complies with the latest standard and is
based on years of experience in the manufacture of our products. However the data is not binding and without warranty. Please
follow recommendations stated on the relevant safety data sheet and precautions stated on the product label. We reserve our
right to make additions, deletions, or modifications to the information at any time without prior notification.

MIPA SE D-84051 Essenbach Tel. 08703/922-0 Telefax 08703/922-100

EP 100-20

gb 11/1214

2K EP Primer
page 2 / 2

Product Information
Application Process :
Brushing, rolling
Air / Flow jar
HVLP
Airless

Pressure
[bar]
4
2,5 - 3
120 - 150

Nozzle
[mm]
1.5 - 1.8
1.5 - 1.8
0.28 - 0.33
(65 - 95 )

Spraying
Operations
2-3
2-4
1-2

Dilution :

Mipa EP-Verdnnung

Hardener :

Mipa EP 950-10, EP 950-25

Mixing Ratio :

By weight: 5 : 1 (EP 100-20 : Hardener)


By volume: 3 : 1 (EP 100-20 : Hardener)
dust dry
45 - 55 min.

Dilution
5 - 10 %
20 - 25 %
20 - 25 %
10 - 15 %

Dry
Object temp. 20 C
Object temp. 60 C

set to touch
4-5h

handle
recoatable
10 - 12 h
1h
45 min.
Re-coatable earliest after 1 hour and latest after 24 hours.
By drying times longer than 24 hours, an intermediate sanding is
required.

Pot Life :

7 - 9 hours

Application Proposal :

Steel:
Primer:
EP 100-20 (coat thickness:
Top coat: PU 200-90 (coat thickness:
Zinc:
Primer:
EP 100-20 (coat thickness:
Top coat: PU 200-90 (coat thickness:
Aluminium:
Primer:
EP 100-20 (coat thickness:
Top coat: PU 200-90 (coat thickness:

50 - 70 m)
50 - 60 m)
50 - 70 m)
50 - 60 m)
50 - 70 m)
50 - 60 m)

Special Recommendations
To be used only by professionals. Some colours may contain lead therefore do not use for
childrens toys or for objects which may be chewed or sucked.

Cleaning of Tools
Tools should be cleaned immediately after use with Nitroverdnnung.

This data sheet is for information purpose only! To our knowledge the data provided complies with the latest standard and is
based on years of experience in the manufacture of our products. However the data is not binding and without warranty. Please
follow recommendations stated on the relevant safety data sheet and precautions stated on the product label. We reserve our
right to make additions, deletions, or modifications to the information at any time without prior notification.

MIPA SE D-84051 Essenbach Tel. 08703/922-0 Telefax 08703/922-100