Study of Use of Polystyrene As A Partial Replacement For Fine Aggregate in Concrete
Study of Use of Polystyrene As A Partial Replacement For Fine Aggregate in Concrete
Volume 3, Issue 6, June – 2018 International Journal of Innovative Science and Research Technology
ISSN No:-2456-2165
“Study of Use of Polystyrene as a Partial Replacement
for Fine Aggregate in Concrete”
Sachin A. Gaikwad1, Mukund M. Pawar 2
PG Student1, Associate Professor2
Civil Engineering Department, SVERI’s COE, Pandharpur, Maharashtra, India
Abstract:- In Civil engineering, due to urbanization the II. LITERATURE REVIEW
demand for construction material increases, with the increase
in demand there is a strong need to utilize alternative [1] In this study author has used waste polystyrene and
materials for sustainable development. Polystyrene (also resin in concrete to produce new concrete material. Author
known as EPS Foam or Styrofoam) is a highly popular concludes that as the EPS and resin ratio increases, density,
plastic packaging material. Polystyrene is essentially non- compressive strength and thermal conductivity of concrete
biodegradable and taking hundreds perhaps thousands of decreased. Author also says that it is a best material for partition
years to decompose in case of land filling. Other disposal wall, ceiling, flooring, bricks etc.
methods or treatments methods are creating hazardous effect
on environment. However, this material is having properties [2] In this paper author said that thermocol has high
such as sound insulation, high thermal conductivity, and thermal insulation and high sound absorption. Author also says
lightweight so we can use this material in concrete. This that it is excellent material to use in construction of walls and
paper highlights the study of properties such as compressive ceiling. Author concludes that thermocol is applied in concrete
strength and tensile strength of Polystyrene based concrete due to its light weight nature which can give us light weight
which is compared with conventional concrete. concrete
Keywords:- Compressive Strength, Tensile Strength, Fine [3] In this paper, author says that Lightweight concrete can
Aggregate, Waste Polystyrene. be used for repairing wooden floors of building, carrying wall of
low thermal conduction, bridge deck etc . Author suggests that it
I. INTRODUCTION is possible to improve the compressive strength versus specific
gravity or to reach equivalent strength for lower specific gravity.
Due to industrialization construction industry is growing In this study cement to EPS ratio is kept 1: 1
day by day along with this there is increase in demand of
construction materials. For sustainable development there is need III. METHODOLOGY
of utilizing alternative materials in construction and utilization of
waste material is very important aspect of sustainability. Different basic tests are taken on concrete ingredient that is
cement (Ordinary Portland cement 43 grade), fine aggregate and
Polystyrene is one of the highly popular plastic packaging coarse aggregate. Mix proportion of concrete is modified for
materials. It is waste material induced from packaging industry using polystyrene with partial replacement of fine aggregate with
which causes pollution and is harmful to ecosystem. This waste 0%, 5%, 10%, 15%, 20% and 25% of polystyrene. Different
is becoming expensive to dispose .Due large and bulky nature, elements are casted with this percentage replacement and tested
polystyrene take up significant space for its disposal and also its under standard conditions.
treatment and disposal is creating environmental sustainability
problem. Currently millions of tons of waste polystyrene are A. Test on Ingredients
produced in world. Polystyrene Foam is a non- biodegradable
material. Polystyrene is essentially non-biodegradable and taking
Coarse
thousands of years to decompose in case of land filling. Other Test Fine Aggregate
Aggregate
disposal methods or treatments methods are creating hazardous
effect on environment. However, this material is having
Specific
properties such as sound insulation, high thermal conductivity, 2.60 2.7
Gravity
and lightweight so we can use these materials in construction
industry which will add new material for construction and add Water
new method of its disposal which is environmental friendly. Absorption 0.52 1.00
This study aims at the use of polystyrene in concrete and (%)
analyzing its properties such as compressive strength, tensile
strength along with its comparative study of strength against Fineness
3.48 6.9
conventional concrete. In this study 5-30% Fine aggregate is Modulus
replaced by polystyrene. Table 1. Physical Properties of Materials- Aggregates
IJISRT18JU302 www.ijisrt.com 371
Volume 3, Issue 6, June – 2018 International Journal of Innovative Science and Research Technology
ISSN No:-2456-2165
V. TEST RESULTS AND DISCUSSION
Test Results
On the concrete specimen the compressive strength and
spilt tensile strength test were conducted, results obtained are
Fineness of Cement 5.33% discussed below:
A. Compressive Strength
Specimens are casted in concrete cube of size (150mm X
Initial Setting Time 50 min
150mm X 150mm) and cured the tested under compressive
strength under compression testing machine (CTM). Graph No.1
shows compressive strength of concrete using polystyrene at 7 th
Final Setting Time 563 min and 28th day for 0.50 W/C.
Soundness 1 mm
Table 2. Physical Properties of Materials- Cement
B. Properties of Polystyrene
Test Polystyrene
Specific Gravity 0.011
Water Absorption (%) 0.0
Moisture Content 0.0 Graph 1: Compressive Strength of Polystyrene based Concrete
Fineness Modulus 3.5 A. Spilt Tensile Strength
Specimens are casted in concrete cylinder of size (150mm
Table 3. Physical Properties of Polystyrene
X 300mm) and cured and then tested. Graph No.2 shows Spilt
Tensile strength of concrete using polystyrene at7th and 28th day
C. Casting of Specimen
for 0.50 W/C.
Specimens are casted as per design mix and tested after
appropriate curing, and tests taken are compressive strength or
cubes (150mm X 150mm X 150mm) and spilt tensile strength of
cylinders (150mm X 300mm). From the studies, optimum results
are found out and compared with conventional concrete.
IV. MIX PROPORTION
Concrete mix design procedure as per IS 10262:2009, a
concrete mix proportions with characteristic compressive
strength or 20Mpa was designed without any admixtures with
water cement ratio 0.50. The mix adopted for study is given in
table below:
Fine Coarse
Material Water Cement Graph 2: Tensile Strength of Polystyrene based Concrete
Aggregate Aggregate
3
Kg/ m 186 372 688 1165
It can be observed from the results that, compressive
Ratio 0.5 1 1.85 3.13
strength and tensile strength of concrete will decrease with
Table 4. Mix Proportion Concrete
partial replacement of fine aggregate with polystyrene as
compared to conventional concrete which is considerable for
lightweight concrete.
IJISRT18JU302 www.ijisrt.com 372
Volume 3, Issue 6, June – 2018 International Journal of Innovative Science and Research Technology
ISSN No:-2456-2165
Which do not require high compressive and tensile strength
also after this study; it has proven better way for disposal of
polystyrene.
VI. CONCLUSION
The partial replacement of fine aggregate with polystyrene
reduces the compressive strength and tensile strength of concrete.
This polystyrene based concrete is best suitable for non-structural
elements.
REFERENCES
[1]. Ayse Kaya, FilizKar, “Properties of concrete containing
waste expanded polystyrene and natural resin”, Construction
and Building Materials 105 (2016) 572-578.
[2]. Dr. G. Elangovan , “Experimental study on light weight
concrete by partial replacement of fine aggregate using
flyash and adding thermocol”, International Journal on
Engineering Technology and Sciences, Volume II, Issue IX,
September-2015.
[3]. AbhijitMandlik, TarunSarthakSood, ShekarKarade,
SangramNaik, AmrutaKulkarni, “Lightweight Concrete
Using EPS”, International Journal of Science and research
(IJSR), Volume 4 Issue 3, March 2015
[4]. Ali a sayadi, juan v tapia, thomas r neitzert, g charles
Clifton,“ Effectof expanded polystyrene particles on fire
resistance, thermal conductivity and compressive strength of
foamed concrete”, construction and building materials 112
(2016) 716-724.
[5]. IS 383:1970 “Specifications for coarse and fine aggregates
from natural sources for concrete”, Bureau of Indian
Standards, New Delhi.
[6]. IS 456: 2000 – ‘Code of practice for plain and
reinforcedConcrete’, Bureau of Indian Standards, New Delhi
[7]. IS: 10262: 1982, “Recommended guidelines for concrete
mix design” Bureau of Indian Standards, New Delhi.