SRF Limited: Typical Properties of Tufnyl Rms 1 Steel Grey

The document provides typical properties of TUFNYL RMS 1 STEEL GREY engineering plastic material. It lists values for tensile strength, elongation at break, flexural strength, flexural modulus, impact strength, hardness, mold shrinkage, specific gravity, melting point, and heat deflection temperature. It recommends pre-drying granules at 100/80°C for 2-4 hours before injection molding and provides recommended temperature settings for the feed, compression, melting, nozzle, and mold of 265-280°C and 80-100°C respectively.

Uploaded by

ரஞ்சன் ஞானயோளி
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
350 views

SRF Limited: Typical Properties of Tufnyl Rms 1 Steel Grey

The document provides typical properties of TUFNYL RMS 1 STEEL GREY engineering plastic material. It lists values for tensile strength, elongation at break, flexural strength, flexural modulus, impact strength, hardness, mold shrinkage, specific gravity, melting point, and heat deflection temperature. It recommends pre-drying granules at 100/80°C for 2-4 hours before injection molding and provides recommended temperature settings for the feed, compression, melting, nozzle, and mold of 265-280°C and 80-100°C respectively.

Uploaded by

ரஞ்சன் ஞானயோளி
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
You are on page 1/ 1

SRF LIMITED

ENGINEERING PLASTICS BUSINESS


Typical Properties of
TUFNYL RMS 1 STEEL GREY
All Properties measured at 23 Deg. / 50% RH on dry-as-molded test specimens.
Only typical data for material selection purposes only. Users has to establish material suitability.

ASTM
PROPERTY METHOD UNIT VALUE

Tensile Strength D-638 Mpa 80


Elongation @ break D-638 % 15.0
Flexural Strength D-790 Mpa 130
Flexural Modulus D-790 Mpa 2800
Impact Strength, Izod D-256A Kg.cm/cm 7.0
Rockwell Hardness D- 785 M scale 80
R Scale 115
Mold Shrinkage (Along the D-955 % 1.5~1.8
flow on 3 MM Thickness)
Specific Gravity D-792 - 1.14
Melting Point D-2117 Deg C 260
Heat Deflection Temperature D-648 Deg C
At 18.5Kgf Load 75
At 4.6 Kgf Load 145

It is recommended to pre dry the Nylon granules in vacuum / air


circulated ovens at 100/80Deg.c for 2 - 4 hrs. Using perforated trays.
Injection Moulding Parameters: Temperature setting in Deg.C
Feed Compression Melting Nozzle Melt Mould
250 270 285 280 265 –280 80 -100
Plant: Manali Industrial Area, Manali, Chennai – 600 068, INDIA
Phone: +91-44-2594 6206 Fax: +91-44-2594 3073 Email: [email protected]
Corporate office: Unitech Crest, Block C, Plot 946, Sector 45, Gurgaon, Haryana-122 003
Registered office: Express Building, 9-10, Bahadur Shah Zafar Marg, New Delhi-110 002

You might also like