The WRC-AL70 is a one-part ready mixed refractory compound containing steel fibers that can be easily installed to form complex lining shapes without seams. It has a working life of 20-30 minutes, a thickness range of 15-50mm, and 12 month shelf life. The compound is versatile up to 500°C and provides adequate lining protection for quick turnarounds.

Uploaded by

TrungThanh Tran
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
84 views

WRC Specification

The WRC-AL70 is a one-part ready mixed refractory compound containing steel fibers that can be easily installed to form complex lining shapes without seams. It has a working life of 20-30 minutes, a thickness range of 15-50mm, and 12 month shelf life. The compound is versatile up to 500°C and provides adequate lining protection for quick turnarounds.

Uploaded by

TrungThanh Tran
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
You are on page 1/ 2

Specification of WRC-AL70

Characteristics-
One part ready mixed compound with steel fibers.

Easy to instal

Working life of 20 to 30 minutes.

Can be formed into complex shapes and will provide a lining without any joints or seams.

Lining thickness can range from 15mm to 50mm.

12 month shelf life if stored in a cool, dry place.

Versatile in applications up to 500°C

Provides adequate lining protection that can be applied during quick turnarounds or short
outage periods.

Specification-

Property Standard SI Units 400° C 815° C 1250° C


Chemical Analysis X-Ray Defraction
Alumina Oxide 88%
SiO2 5.0%
TiO2 1.8%
Other 5.2%
Density 3.04 g/cm3 3.03 g/cm3 3.06 g/cm3
Apparent Porosity NBR 8382/6220 14.1% 17.8% 19.6%
Modulus of NBR 8382/6220 20.0 MPa 17.3 MPa 29.0 MPa
Rupture NBR 11222
Cold Crushing NBR 11222 90.0 MPa 88.0 MPa 76.0 MPa
Strength NBR 8385
Linear Expansion NBR 13185 -0.15% -0.31% -0.15%
Setting Time (60° 1 to 1.5 Hours 8.8 cm3 8.8 cm3 8.8 cm3
C)
Moisture Content 5.0% - 6.0%
(Water)
Maximum Use 500° C
Temperature
Abrasion
Resistance
Shelf Life 12 Months

Indicative Consumption - Coverage at 1”(25mm) thick/ 50lb(25kg) bag 3.52 ft2 (0.3M2)
Specification of WRC-SC50
Characteristics-

WRC-SC50 silicon carbide based trowelable, wearing compound that is used to provide abrasion
resistance in low and high temperature applications where traditional refractory brick are not
feasible or cost effective. This trowelable compound offers the installer the ability to form an
abrasion resistant lining to combat abrasion as well as offer good thermal shock protection.

Specification-

Property Property SI Units


Chemical Analysis Chemical Analysis

Silicon Carbide Silicon Carbide 58%


Other Other 42%

Density (400° C) Density (400° C) 2.45 g/cm3

Modulus of Rupture After 1 Day Modulus of Rupture After 1 Day 8.5 MPa
RT RT
Modulus of Rupture After 1 Day Modulus of Rupture After 1 Day 11.2 MPa
RT RT
Setting Time Setting Time 60 - 120 Minutes
Moisture Content (Water) Moisture Content (Water) 9% - 12%
Maximum Use Temperature Maximum Use Temperature 500° C
Abrasion Resistance After 1 Day Abrasion Resistance After 1 Day 9.0 cm3
RT RT
Abrasion Resistance After 7 Day Abrasion Resistance After 7 Day 8.5 cm3
RT RT
Abrasion Resistance Abrasion Resistance 0.8 cm3/50cm2

Indicative Consumption - Coverage at 1”(25mm) thick/ 50lb(25kg) bag 3.52 ft2 (0.3M2)