Wb1500e Eni Ci

This document provides information on a low strength welding electrode for cast iron. It deposits nearly pure nickel that is fully machinable, with a narrow fusion zone and minimal heat-affected zone. It can be used to weld grey and malleable cast iron components like cylinder heads, blocks, and pump castings, producing machinable, crack-free welds with low penetration and dilution. Specifications for the all-weld metal composition, mechanical properties, electrode sizes and lengths, current ranges, packing details, and storage/re-baking instructions are given.

Uploaded by

cwiksj
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
63 views1 page

Wb1500e Eni Ci

This document provides information on a low strength welding electrode for cast iron. It deposits nearly pure nickel that is fully machinable, with a narrow fusion zone and minimal heat-affected zone. It can be used to weld grey and malleable cast iron components like cylinder heads, blocks, and pump castings, producing machinable, crack-free welds with low penetration and dilution. Specifications for the all-weld metal composition, mechanical properties, electrode sizes and lengths, current ranges, packing details, and storage/re-baking instructions are given.

Uploaded by

cwiksj
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
You are on page 1/ 1

WB1500E M.M.A.

WELDING ELECTRODE

Classification AWS A5.15-90: ENi-CI BSEN1071-2003 : E C Ni-CI 3

Product Description Low strength weld for cast iron. Deposits almost pure Nickel that is fully machinable.
Narrow fusion zone, thus minimal HAZ. Smooth, quiet welding arc.

Application Can weld all standard grades of grey and malleable cast irons, typically cylinder heads
and blocks and pump castings. The stable arc achieved on low currents reduces
penetration and dilution, producing machinable crack-free welds.
All-Weld Metal Composition
(Weight %) C Mn Ni Si S P Al Cu+Ag
min. 1.0 0.10 88 0.30 - - - -
max. 2.0 0.40 - 1.00 0.02 0.02 0.10 0.10

Typical All-Weld Metal Ultimate Tensile Strength N/mm² -


Mechanical Properties Yield Stress/0.2% Proof Stress N/mm² -
Elongation on 5D % -
Impact Energy CV @ Joules -

Electrode Dia (mm) 1.6mm 2.0mm 2.5mm 3.2mm 4.0mm 5.0mm 6.0mm

Electrode Length (mm) - - 350 350 350 350 -

min. - - 55 75 95 145 -
Current Range
(Amps) max. - - 85 115 155 185 -

Packing Information

Kg Per Packet - - 5 5 5 5 -
Approx. Pieces Per Kg - - 50 32 21 13

Storage
Storage and Re-baking It is recommended that the WB range of electrodes are stored in a dry heated store at
a minimum temperature of 18C, and a maximum relative humidity of 60%. To avoid
damage to the coatings no more than 6 cartons should be staked on top of another.

Re-drying
If damp re-dry @ 180C for 1 hour.

Current Conditions AC (OCV70) DC+ and Welding Positions