Property Test Method Unit Typicalvalue : BL 4M License Grade Code HM 8355 (THT)

This document provides information about the product "BL 4M", which is a high density polyethylene used for large containers and jerry cans. It has a high molar mass and is easily processable, with high stiffness and strength as well as good environmental stress crack resistance. Typical properties include a density of 0.952 g/cm3, melt flow rates of 0.35 g/10min and 9.5 g/10min, an impact strength of 10 mj/mm2, and a flexural creep modulus of 1100 Mpa.

Uploaded by

MohamadMostafavi
Copyright
© © All Rights Reserved
Available Formats
Download as PDF, TXT or read online on Scribd
91 views

Property Test Method Unit Typicalvalue : BL 4M License Grade Code HM 8355 (THT)

This document provides information about the product "BL 4M", which is a high density polyethylene used for large containers and jerry cans. It has a high molar mass and is easily processable, with high stiffness and strength as well as good environmental stress crack resistance. Typical properties include a density of 0.952 g/cm3, melt flow rates of 0.35 g/10min and 9.5 g/10min, an impact strength of 10 mj/mm2, and a flexural creep modulus of 1100 Mpa.

Uploaded by

MohamadMostafavi
Copyright
© © All Rights Reserved
Available Formats
Download as PDF, TXT or read online on Scribd
You are on page 1/ 1

BL 4M

License Grade Code HM 8355(THT)

Product Description:
“BL 4M” is a high density polyethylene with 1-Butene as co monomer.
It is high molar mass,easily processable, high stiffness and strength, good ESCR, very good molding surface
finish.

Applications:

 Jerry can
 General- purpose grade for large containers

Typicaldata
PROPERTY TEST METHOD UNIT TYPICALVALUE*

Mass density (23 C) ISO 1183 g/cm3 0.952

Melt Flow Rate (190 C/5.06kg) ISO 1133 g/10min 0.35

Melt Flow Rate (190 C/21.16kg) ISO 1133 g/10min 9.5

FRR(21.6/5) - 27

Impact strength (23 C) ISO 179/1eA mj/mm2 10

Swell ratio MPC-Test % 115

Flextural Creep Modulus DIN 19537-2 Mpa 1100


(4point,1min)

Tensile Modulus ISO 527 Mpa 1200


(23 C,v=1mm/min,secant)

Stress at Break ISO 527 Mpa 34

Elongation at Break ISO 527 % >800

Elongation atYield ISO 527 % 10

SofteningTemperature ISO 306 C 80

BrittleTemperature ASTM D746-72 C <-80

shore D hardness ISO 868 62

ESCRinfullnotchcreeptest ISO CD 16770 [email protected] Mpa 5


(80 C,2%Arcopal)

 Typical values not to be constructed as specifications.


 Recommended injection moulding temp. 180-220 c