D59A

This document provides technical data for D 59 A refractory material from HASLE Refractories A/S, including its chemical analysis, physical properties, and performance characteristics. Key information includes that it has 62% Al2O3, a service temperature of 1650°C, bulk density of 2450 kg/m3, modulus of rupture maintained between 18-20 MPa up to 1500°C, cold crushing strength increasing from 130 to 185 MPa from 110°C to 1500°C, and thermal conductivity ranging from 1.40 to 1.63 W/mK from 400°C to 1200°C. The material also has low drying shrinkage, reversible expansion to 1000°C, and is rated as

Uploaded by

Safrin Sangia
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
450 views1 page

D59A

This document provides technical data for D 59 A refractory material from HASLE Refractories A/S, including its chemical analysis, physical properties, and performance characteristics. Key information includes that it has 62% Al2O3, a service temperature of 1650°C, bulk density of 2450 kg/m3, modulus of rupture maintained between 18-20 MPa up to 1500°C, cold crushing strength increasing from 130 to 185 MPa from 110°C to 1500°C, and thermal conductivity ranging from 1.40 to 1.63 W/mK from 400°C to 1200°C. The material also has low drying shrinkage, reversible expansion to 1000°C, and is rated as

Uploaded by

Safrin Sangia
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
You are on page 1/ 1

HASLE Refractories A/S

Technical data
D 59 A from HASLE Refractories A/S

HASLE
Chemical analysis: D 59 A
Al2O3......................................................................... % 62
TiO2........................................................................... % 1,4
SiO2........................................................................... % 33
Fe2O3....................................................................... % 1,1
CaO......................................... % 1,4
SiC............................................ % -
Physical data:
Refractoriness PCE 36
Max. service temperature °C 1650
3
Bulk density kg/m 2450
Max. grain size mm 10
Modulus of rupture
after heating to: 110°C MPa 18
500°C MPa 18
1000°C MPa 18
1500°C MPa 20
Cold crushing strength
after heating to: 110°C MPa 130
500°C MPa 140
1000°C MPa 155
1500°C MPa 185
Drying shrinkage: 110°C % 0,1
Linear shrinkage
excl. drying shrinkage
after heating to: 500°C % 0,0
1000°C % 0,2
1500°C % - 0,3
Thermal conductivity: 400°C W/mK 1,40
800°C W/mK 1,51
1200°C W/mK 1,63
Alkali test (scale 0-10) ........................ 1
2
Resistance to abrasion.......... g/cm 0,15
Resistance to thermal shock ........ Extra high
Reversible linear expansion
to 1000°C................................ % 0,50
Average water addition............. % 4-5

The technical data represent average reference values established by DIN- and EN-test procedures in
our ceramic laboratory. They serve to give general information, they are liable to natural deviations, and
they are not to be cited as guaranteed properties or guaranteed values.

Rev. 09.04