N38EH

N38EH Grade Sintered Neodymium Iron Boron Magnets

These are also referred to as "Neo" or NdFeB magnets. They offer a

combination of high magnetic output at moderate cost. Please contact ALB Characteristic Units C // C
for additional grade information and recommendations for protective coating.
Reversible Temperature Coefficients (1)
Assemblies using these magnets can also be provided.

Thermal Properties
of Induction, α(Br) %/ºC -0.120
of Coercivity, α(Hcj) %/ºC -0.420
Coefficient of Thermal Expansion (2)
-6
Characteristic Units min. nominal max. ∆L/L per ºCx10 7.5 -0.1
Gauss 12,000 12,350 12,800 Thermal Conductivity W / (m • K) 7.6
Br, Residual Induction
mT 1200 1235 1280 Specific Heat (3) J / (kg • K) 460
Magnetic Properties

Oersteds 11,300 11,750 12,200 Curie Temperature, Tc ºC 310

HcB, Coercivity
kA/m 899 935 971 psi 41,300
Flexural Strength

Properties
Oersteds 30,000 MPa 285
HcJ, Intrinsic Coercivity

Other
kA/m 2,388 Density g/cm3 7.5
MGOe 36 38 40 Hardness, Vickers Hv 620
BHmax, Maximum Energy Product
kJ/m3 287 303 318 Electrical Resistivity,   • cm 180
Notes: (1) Coefficients measured between 20 and 200 ºC
(2) Between 20 and 200 ºC (3) Between 20 and 140 ºC
Demagnetisation Curves
kG Tesla
Pc = B H
0.5
Grade: N38EH 0.75 1 1.5 2 3 5
15

14 1.4

13

-40°C 1.2
12

20°C 11

Flux Density, B
10 1.0

0.3 9

8 0.8

60°C 7

Polarization, J
6 0.6
80°C
5

100°C
4 0.4
120°C
0.1 3
150°C
2 0.2
180°C
200°C
220°C
1

0 0
30
kOe 28 26 24 22 20 18 16 14 12 10 8 6 4 2 0

kA/m 2230 2070 1910 1750 1590 1430 1275 1115 955 795 640 475 320 160 0
Demagnetizing Field, H
1 kA/m = 12.566 Oe 1 kOe = 79.577 kA/m

Notes: The material data and demagnetization curves shown above represent typical properties that may vary due to product shape and size.
Magnets can be supplied thermally stabilized or magnetically calibrated to customer specifications.
Additional grades are available. Please contact the factory for information.