Hot Dip Galvanizing Process

The hot dip galvanizing process involves loading steel items, degreasing them using a hot caustic bath, pickling them in hydrochloric acid, pre-fluxing them in a zinc ammonium chloride solution, submerging them in molten zinc, and quenching them in a sodium dichromate solution. This coats the steel in a thick, abrasion-resistant zinc-iron alloy layer that protects it from rusting for over 50 years. Hot dip galvanizing coats all surfaces thoroughly, unlike alternative galvanizing methods.

Uploaded by

Natarajan Murugesan
Copyright
© © All Rights Reserved
Available Formats
Download as PDF, TXT or read online on Scribd
193 views

Hot Dip Galvanizing Process

The hot dip galvanizing process involves loading steel items, degreasing them using a hot caustic bath, pickling them in hydrochloric acid, pre-fluxing them in a zinc ammonium chloride solution, submerging them in molten zinc, and quenching them in a sodium dichromate solution. This coats the steel in a thick, abrasion-resistant zinc-iron alloy layer that protects it from rusting for over 50 years. Hot dip galvanizing coats all surfaces thoroughly, unlike alternative galvanizing methods.

Uploaded by

Natarajan Murugesan
Copyright
© © All Rights Reserved
Available Formats
Download as PDF, TXT or read online on Scribd
You are on page 1/ 13

The

hot dip galvanizing


process

Industrial Galvanizers
The hot dip galvanizing process

• Loading - jigging

• Degreasing Hot caustic

• Pickling Hydrochloric acid

• Pre-fluxing Zinc am. chloride

• Hot dip galvanizing Molten zinc

• Quenching Dichromate

Industrial Galvanizers
The hot dip galvanizing process
Loading - jigging

The steel items need to be supported during the hot dip


galvanizing process.

Can the item be easily jigged?


Will touch marks be a problem?

Solutions and molten zinc must be able to flow into all


sections and drain off all sections.

Steel items must be designed to prevent air, solutions and


molten zinc becoming trapped

Check design for possible problems

Industrial Galvanizers
The hot dip galvanizing process
Degreasing

A hot (90oC) caustic bath is used to remove -


Oil, grease, paint another organic compounds
If these contaminating materials are not removed, the next
stage of the process (pickling) is affected

Check if any paint is on item - some paints are not easily


removed and may require abrasive blasting before
galvanizing

Some pipes and pipe fittings have a black varnish coating


that cannot be removed in the caustic bath.

Industrial Galvanizers
The hot dip galvanizing process
Acid pickling

The steel items are immersed in hydrochloric acid to


remove - rust, mill scale and other metal oxides

The steel surface must be perfectly clean of these oxides


for the molten zinc to react with the steel

Very heavy rust may not be easily removed by pickling -


badly rusted items should be abrasive blasted or
mechanically cleaned first.

Industrial Galvanizers
The hot dip galvanizing process
Pre-fluxing

Steel items are water rinsed after pickling and immersed in


hot (70-80oC) zinc ammonium chloride (ZAC) solution.

The ZAC solution conditions the clean steel surface ready


for hot dip galvanizing.

Good pre-treatment = good quality galvanizing

Industrial Galvanizers
The hot dip galvanizing process
Quenching

After hot dip galvanized steel item is removed from the


galvanizing bath, it is immediately quenched in a sodium
dichromate solution

The dichromate quenching cools the item so that it can be


quickly handled and passivates the surface of the
galvanized coating to maintain its bright appearance.

Industrial Galvanizers
The hot dip galvanizing process
Hot dip galvanizing

The steel is immersed in molten zinc (temp 4500C)


The clean steel surface reacts with the molten zinc to form a
zinc-iron alloy which is very strongly bonded to the surface.

The hot dip galvanized coating forms in 3-5 minutes,


depending on the steel thickness.
Free zinc layer

Galvanized coating Alloy layers

Steel Micrograph - 100 X

Industrial Galvanizers
The hot dip galvanizing process
Quenching
After hot dip galvanized steel item is removed from the
galvanizing bath, it is immediately quenched in a sodium
dichromate solution
The dichromate quenching cools the item so that it can be
quickly handled and conditions the surface of the
galvanized coating to maintain its bright appearance.
Chromate quenching will reduce white rusting problems.
White rust forms when rainwater reacts with newly
galvanized steel to form zinc hydroxide.

Poor storage or HDG steel will also promote white rust.

Industrial Galvanizers
The hot dip galvanizing process
Characteristics
• Typically 65 - 150 microns thick (1 mm = 1000 microns)
• Zinc iron alloy layers make up 80% - 100% of the coating.

• The zinc-iron alloy layers are harder than 250 grade steel

Zinc

Zinc-iron alloys

Steel
Micrograph of hot dip galvanized coating

Industrial Galvanizers
The hot dip galvanizing process
Coating comparisons
Compared to zinc electroplating (ZEP) and continuous
galvanizing (CG), hot dip galvanizing (HDG) is better
because…..
- HDG is thicker and will last over 50 years or more
without rusting
- HDG is harder and is 5 times more abrasion resistant
than ZEP and CG
- HDG coats all external and internal surfaces and
edges. All CG coatings have cut, exposed edges
after processing.

Industrial Galvanizers
Coating thickness of coatings on
galvanized products

100
90

Z350 Gal. sheet


80
70
60
50
40
30
20
10
0

Industrial Galvanizers
For more information