EN - MATERIALS SPECIFICATIONS

Designation Chemical composition (cast analysis) (% min.)

Name Number C Si max Mn P max S max Cr Mo Ni others
GP240GH 1.0619 0,18 to 0,23 0,60 0,50 to 1,20 0,030 0,020 1) -- -- -- --
G20Mo5 1.5419 0,18 to 0,23 0,60 0,50 to 1,00 0,025 0,020 1) -- 0,40 to 0,60 -- --
G17CrMo5-5 1.7357 0,15 to 0,20 0,60 0,50 to 1,00 0,020 0,020 1) 1,00 to 1,50 0,45 to 0,65 -- --
G17CrMo9-10 1.7379 0,13 to 0,20 0,60 0,50 to 0,90 0,020 0,020 1) 2,00 to 2,50 0,90 to 1,20 -- --
GX15CrMo5 1.7365 0,12 to 0,19 0,80 0,50 to 0,80 0,025 0,025 4,00 to 6,00 0,45 to 0,65 -- --
G20Mn5 1.6220 0,17 to 0,23 0,60 1,00 to 1,60 0,020 0,020 1) -- -- 0,80 max --
G9Ni10 1.5636 0,06 to 0,12 0,60 0,50 to 0,80 0,020 0,015 -- -- 2,00 to 3,00 --
G9Ni14 1.5638 0,06 to 0,12 0,60 0,50 to 0,80 0,020 0,015 -- -- 3,00 to 4,00 --
GX5CrNi19-10 2) 1.4308 2) 0,07 max 1,50 1,50 0,040 0,030 18,00 to 20,00 -- 8,00 to 11,00 --
GX5CrNiNb19-11 2) 1.4552 2) 0,07 max 1,50 1,50 0,040 0,030 18,00 to 20,00 -- 9,00 to 12,00 Nb: 8 x C, max: 1,00
GX5CrNiMo19-11-2 2) 1.4408 2) 0,07 max 1,50 1,50 0,040 0,030 18,00 to 20,00 2,00 to 2,50 9,00 to 12,00 --
GX5CrNiMoNb19-11-2 2) 1.4581 2) 0,07 max 1,50 1,50 0,040 0,030 18,00 to 20,00 2,00 to 2,50 9,00 to 12,00 Nb: 8 x C, max: 1,00
GX2CrNiMoN22-5-3 1.4470 0,03 max 1,00 2,00 0,035 0,025 21,00 to 23,00 2,50 to 3,50 4,50 to 6,50 N: 0,12 to 0,20
1) For castings of ruling thickness <28 mm, % 0,030 S is permitted
2) It should be pointed out that the suggested chemical composition ranges of these alloyed corrosion resistant steel grades are rather large. Accord ing to the final
destination (high temperature/low temperature, etc…) it may be advisable for the founder to aim for narrower ranges for different elements in order t o achieve the most
suitable structures.

MECHANICAL PROPERTIES
Designation Heat treatment °C Test at room temperature Test at elevated temperature
Impact
Normalizing Tempering Tensile test test Tensile test
Name Number Symbol 2) (+ N) or (+T) Rp0,2 Rm A KV Rp0,2 Mpa *) min at °C
Quenching Mpa *) Mpa *) % J
100° 200° 300° 350° 400° 450° 500° 550°
(+ Q) 1) min min min.
GP240GH 1.0619 + N 900 to 980 -- 240 420 to 600 22 27 210 175 145 135 130 125 -- --
+ QT 890 to 980 600 to 700 240 420 to 600 22 40 210 175 145 135 130 125 -- --
G20Mo5 1.5419 + QT 920 to 980 650 to 730 245 440 to 590 22 27 -- 190 165 155 150 145 135 --
G17CrMo5-5 1.7357 + QT 920 to 960 680 to 730 315 490 to 690 20 27 -- 250 230 215 200 190 175 160
G17CrMo9-10 1.7379 + QT 930 to 970 680 to 740 400 590 to 740 18 40 355 345 330 315 305 280 240
GX15CrMo5 1.7365 + QT 930 to 990 680 to 730 420 630 to 760 16 27 -- 390 380 -- 370 -- 305 250
1) +Q means quenching media: air or liquid. +T = tempering. +N = normalizing
2) If there are alternative specifications for heat treatment, the requested alternative shall be indicated on the order, e.g.: GP240GH +QT1 or 1.0619 +QT1
*) 1 Mpa = 1N/mm 2

Designation Heat treatment °C Test at room temperature Impact test

Tensile strength

Name Number Symbol 1) Quenching Tempering Rp0,2 Rm A KV At

Mpa *) Mpa *) % J °C
min min min.
G20Mn5 1.6220 + N 900 to 980 -- 300 480 to 620 20 27 -30
+ QT 900 to 940 610 to 660 300 500 to 650 22 27 -40
G9Ni10 1.5636 + QT 830 to 890 600 to 650 280 480 to 630 24 27 -70
G9Ni14 1.5638 + QT 820 to 900 590 to 650 360 500 to 650 20 27 -90
1) +Q: quenching in water. +T = tempering. +N = normalizing.
*) 1 Mpa = 1 N/mm 2

Designation Heat treatment Test at room temperature Test at elevated temperature

+ AT 1)
Tensile test Impact test Tensile test
Name Number °C Rp1,0 5) Rm A KV °C 8) Rp1,0 5) Mpa *) min. at °C
Mpa *) Mpa *) % J
100° 200° 300° 350° 400° 500° 550°
min min min.
GX5CrNi19-10 1.4308 1050 to 1150 200 440 to 640 30 60 7) RT 7) 160 125 110 -- -- --
GX5CrNiNb19-11 1.4552 1050 to 1150 200 440 to 640 25 40 RT 165 145 130 -- 120 110 100
GX5CrNiMo19-11-2 1.4408 1080 to 1150 210 440 to 640 30 60 7) RT 7) 170 135 115 -- 105 -- --
GX5CrNiMoNb19-11-2 1.4581 1080 to 1150 210 440 to 640 25 40 RT 185 160 145 -- 130 120 115
GX2CrNiMoN22-5-3 1.4470 1120 to 1150 2) 3) 420 6) 600 to 800 20 30 RT 330 6) 280 6) 4) -- -- -- --
1) The heat treatment for all the steel grades is +AT +QW (solution annealing + water quenching).
2) After solution annealing at high temperature, castings may be cooled down to 1040 °C to 1010 °C prior to water quenching in order to improve corrosion resistance and
prevent cracks in complex shapes.
3) As far as steel castings for pressure vessel are concerned the austenitic-ferritic steel are not considered in their age hardened condition.
4) For similar reasons as those concerning note 3) the austenitic-ferritic steel have not to be used for temperatures higher then 250 °C in pressure vessel applications.
5) Rp0,2 may be estimated by lowering Rp1,0 by 25 Mpa.
6) Rp0,2
7) For use at low temperature impact properties may be agreed and the following applies: Steel number 1.4308 KV J min. 60 at -196 °C.
8) RT = Room temperature. *) 1 Mpa = 1 N/mm 2