This document provides 10 sample exam items for the API-510 exam. Each item contains a question with 4 possible answers, only one of which is correct. The items cover topics such as determining the appropriate NDE method, expected corrosion locations, pressure vessel testing procedures, inspection purposes, corrosion rate calculations, extending vessel life, temporary repairs, crack repairs, verifying welder qualifications, and identifying welding processes.

Uploaded by

Magira Pasaribu
Copyright
© Attribution Non-Commercial (BY-NC)
Available Formats
Download as PDF, TXT or read online on Scribd
385 views

API 510 Examination Sample Items

This document provides 10 sample exam items for the API-510 exam. Each item contains a question with 4 possible answers, only one of which is correct. The items cover topics such as determining the appropriate NDE method, expected corrosion locations, pressure vessel testing procedures, inspection purposes, corrosion rate calculations, extending vessel life, temporary repairs, crack repairs, verifying welder qualifications, and identifying welding processes.

Uploaded by

Magira Pasaribu
Copyright
© Attribution Non-Commercial (BY-NC)
Available Formats
Download as PDF, TXT or read online on Scribd
You are on page 1/ 3

510 examination sample items

SAMPLE API-510 Exam Items


The items below are examples of what an exam item might look like. If you have questions about an item or
disagree with the answer, please email us at [email protected] and we will forward to one of our subject
matter experts.
Correct Answer: 4

A. The nondestructive examination method to be used for a particular inspection should


be determined by the:

1. availability of certified NDE examiners.


2. length of time since the last inspection.
3. age of the component to be inspected.
4. type, location, and orientation of the expected
flaws.

Correct Answer: 3

B. In planning for an internal inspection of a vessel that has contained


acidic corrodents, what type and location of corrosion would you expect
to find on the vessel shell, away from the welds?

1. Hydrogen blistering in the vapor space


2. Hydrogen embrittlement in the vapor space
3. Hydrogen blistering near the liquid level
4. Hydrogen embrittlement below the liquid level

Correct Answer: 1

C. A pressure vessel is scheduled for pneumatic testing using the


methodology of ASME Code, Section VIII, Division 1, with the maximum
allowable working pressure = 635 psig at 375° F. The vessel is
constructed of SA-516 Gr. 65 material and is neither enameled nor
lined. The test metal temperature will be a minimum of 50° F, per the
owner's specifications. How many pressurization steps are needed to
achieve the minimum required test pressure, and at what minimum
pressure will the visual examination be performed?

1. 6 steps; 635 psig


2. 6 steps; 793.75 psig
3. 9 steps; 635 psig
4. 9 steps; 793.75 psig

Correct Answer: 4

D. The principal reason for inspecting a pressure relief device is to


determine:

1. the remaining life.


2. the spring coil diameter.
3. the body thickness.
4. if it is functioning properly.
Correct Answer: 1

E. A pressure vessel has been in service for 12 years and has a history
of corrosion over its service life. The original thickness was 1.9375
inches; the current thickness is 1.405 inches. What is the corrosion rate
for this vessel?

1. 0.044 inch per year


2. 0.089 inch per year
3. 0.266 inch per year
4. 0.532 inch per year

Correct Answer: 3

F. What can be done to extend the life of a vessel with a corroded area
in the shell plate 6 inches from the weld, a joint efficiency of less than 1,
and a corrosion thickness currently near the minimum required
thickness?

1 . Recalculate t minimum for current operating


conditions using E < 1.
2. Recalculate t minimum for current operating
conditions using E = 1.
3. Recalculate t minimum for design conditions using
E = 1.
4. Monitor the thickness during the run.

Correct Answer: 2

G. Temporary repairs to pressure vessels:

1. must be replaced with permanent repairs during the


next scheduled shutdown.

2. may remain in place for long periods if approved by


the pressure vessel engineer.

3. may remain in place for long periods if approved by


the API-authorized pressure vessel inspector.

4. may remain in place permanently if approved by


the pressure vessel engineer and the API authorized
pressure vessel inspector.

Correct Answer: 2

H. Who must be consulted before the repair of a crack at a discontinuity


where stress concentrations may be serious?

1. The owner-user
2. The pressure vessel engineer
3. The National Board inspector
4. The vessel manufacturer
Correct Answer: 4

I. The WPS and the PQR are used to determine:

1. if the welder is able to deposit sound weld metal.


2. if the welder is able to operate welding equipment.
3. the welder's ability to produce welds that are
radiographically free of defects.
4. if a weldment has the required properties for the
intended application.

Correct Answer: 3

J. In a certain arc welding process, coalescence of metals is produced


by an arc between a tungsten electrode and the work, and shielding is
obtained from a gas or gas mixture. Both pressure and filler metal may
or may not be used. This process is called:

1. FCAW.
2. GMAW.
3. GTAW.
4. SAW.