Scribd
Upload
188 views2 pages

410S Data Sheet PDF

Uploaded by

sanketpavi21
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
188 views2 pages

410S Data Sheet PDF

Uploaded by

sanketpavi21
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
You are on page 1/ 2

P R O D U C T D A T A S H E E T

410S STEEL STAINLESS

AK Steel 410S Stainless Steel is a COMPOSITION PHYSICAL PROPERTIES


non-hardening modification of Type 410. % Density, 0.28 lbs/in3
A small titanium addition minimizes aus- Carbon 0.08 max. 7.73 g/cm3
tenite formation at high temperatures, Manganese 1.00 max.
thereby restricting the alloy’s ability
Phosphorus 0.040 max. Electrical Resistivity,
Sulfur 0.030 max. microhm-in (microhm-cm)
to harden. The result is a soft, ductile Silicon 1.00 max.
condition when the material is rapidly Chromium 11.5 - 14.50 68°F (21°C) – 23.7 (60)
Titanium 0.20 max.
cooled from above the critical tempera- Specific Heat, BTU/lb/ °F (kJ/kg•K)
ture. This non-hardening characteristic AVAILABLE FORMS 32 - 212°F (0 - 100°C) – 0.11 (0.46)
also retards formation of hardening AK Steel 410S is available in thicknesses Thermal Conductivity,
cracks when the steel is welded. The from 0.015" to 0.100" (0.38 to 2.54 mm) BTU/hr/ft2/ft/°F (W/m•K)
alloy is completely ferritic in the annealed in widths up to 48" (1219 mm). For other 212°F (100°C) – 15.6 (26.9)
condition. sizes, inquire.
Mean Coefficient of Thermal Expansion,
Because AK Steel 410S cools from
in/in/°F (µm/m•K)
elevated temperatures without marked
32 - 212°F (0 - 100°C) – 6.0 x 10-6 (10.8)
hardening, it is particularly useful for
32 - 600°F (0 - 315°C) – 6.4 x 10-6 (11.5)
annealing boxes, quenching racks,
32 -1000°F (0 - 538°C) – 6.7 x 10-6 (12.2)
oxidation-resistant partitions and other
32 -1200°F (0 - 649°C) – 7.5 x 10-6 (13.5)
high-temperature units.
Modulus of Elasticity, ksi (MPa)
29 x 103 (200 x 103)
MECHANICAL PROPERTIES
Typical Mechanical Properties* Melting Range,°F (°C)
2700 - 2790 (1482 - 1532)
Elongation Izod
UTS 0.2% YS % in 2" Hardness V-Notch Magnetic Characteristic,
ksi (MPa) ksi (MPa) (50.8 mm) Rockwell ft-lbs (J) Ferro-magnetic
65 (448) 40 (276) 25 B75 30 (42)
*Annealed - room temperature.

410S-S-08-01-07
AK STEEL 410S STAINLESS STEEL DATA SHEET
CORROSION RESISTANCE filler is required, AWS E/ER 309L or 430
The information and data in this product data sheet are
The corrosion resistance of AK Steel filler material is most often specified. accurate to the best of our knowledge and belief, but are
intended for general information only. Applications
410S Stainless Steel is similar to Type Type 410S is well known in reference suggested for the materials are described only to help
410. It provides adequate resistance to literature and more information can be readers make their own evaluations and decisions, and
are neither guarantees nor to be construed as express or
atmospheric corrosion, fresh water, obtained in this way. implied warranties of suitability for these or other
applications.
mild acids and alkalies, and some other HEAT TREATMENT
chemicals. Data referring to mechanical properties and chemical
AK Steel 410S is not hardenable by heat analyses are the result of tests performed on specimens
obtained from specific locations with prescribed
OXIDATION RESISTANCE treatment. It is annealed in the 1600 - sampling procedures; any warranty thereof is limited to

The oxidation resistance of AK Steel 410S 1650°F (871 - 899°C) range and then air the values obtained at such locations and by such
procedures. There is no warranty with respect to values
Stainless Steel is good. It can be up to cooled, mainly to relieve cold working of the materials at other locations.

1300°F (705°C) in continuous service. Scal- strains. Care should be exercised to AK Steel and the AK Steel logo are registered trademarks

ing becomes excessive above about avoid exposure at temperatures of of AK Steel Corporation.

1500°F (811°C) in intermittent service. 2000°F (1093°C) or above because of


possible embrittling effects. If exces-
FORMABILITY sively large grains are found after anneal-
AK Steel 410S Stainless Steel can be eas- ing mildly cold-worked material, the
ily formed by drawing, spinning, bend- annealing temperature should be
ing and roll forming. decreased to the 1200 - 1350°F (649 -
732°C) range.
WELDABILITY
This ferritic class of stainless steels METRIC CONVERSION
is generally considered to be weldable Data in this publication are presented in
by the common fusion and resistance U.S. customary units. Approximate met-
techniques. Special consideration is re- ric equivalents may be obtained by per-
quired to avoid brittle weld fractures forming the following calculations:
during fabrication by minimizing Length (inches to millimeters) –
discontinuities, maintaining low weld Multiply by 25.4
heat input, and occasionally warming
the part somewhat before forming. This Strength (ksi to megapascals or
particular alloy is generally considered meganewtons per square meter) –
to have slightly poorer weldability than Multiply by 6.8948
the most common alloy of the stain- Temperature (Fahrenheit to Celsius) –
less class, Type 409. A major difference (°Fahrenheit - 32) Multiply by 0.5556
is addition of aluminum to control hard-
ening, which results in the need for Density (pounds per cubic inch to
higher heat input to achieve penetra- kilograms per cubic meter) –
tion during arc welding. When a weld Multiply by 27,670