Format No:SSA/TRF/GEN

Issue No:01, Issue Date:10-05-2018

Page 1 of 3

CIN:U74990DL2010PTC354497 TEST REPORT

Test Report Issued To:
Test Report No: M200919009/M200919009-11
L&T CONSTRUCTION (HCIC)
Date of Issue: 30-Sep-2020
MTHL-PKG-3, L&T HEAVY CIVIL INFRASTRUCTURE IC,
LABHESHWAR AURA,, SECTOR-9, PLOT 89, ULWE,,
NAVI MUMBAI, MAHARASHTRA, INDIA, 412206,
Sample Receipt Date: 19-Sep-2020
Date of Start of Testing: 19-Sep-2020
Date of Completion of Test: 29-Sep-2020

Customer Relationship Number 53291

Sample Description :
CEMENT, GRADE: OPC 53, MAKE: ULTRATECH, WEEK NO. 37,
LOCATION : PROJECT BATCHING PLANT, SAMPLE ID:
LT/MTHL/P3/SPL/CEMENT/192

Customer Reference No
Partial Report
:
L&T/MTHL P-3/QC-TP/2020/0198 DT: 19/09/2020

Kind Attention : MR. PALLAB KUILA

E-Mail: [email protected] Contact No: 9029555171

Sample Condition : GOOD

Sample Quantity (Approx) : - Sample Size (Approx) : -

SAMPLE NOT DRAWN BY OUR LABORATORY. THE RESULTS RELATE ONLY TO THE ITEMS TESTED

Digitally signed
by Yogesh Singh
Date:
2020.09.30
11:24:25 +05:30
Report Issued By
ULR-TC816320000005269F
Authencity of report can be verified by mail at [email protected]
This is a Digitally Signed Report and hence doesn't require Physical Signature.

Spectro SSA Labs Pvt. Ltd, R-489, Rabale, MIDC, Navi Mumbai- 400701 (India)
Phone :022-25893335 || Web : www.spectrossa.com || Email:[email protected]
ISO 9001:2008 Certified Laboratory
Please refer to our Website http://www.spectro.in/spectro-policies.html for Terms & Condition
 Format No: SSA/TRF/GEN
Issue No: 01, Issue Date:10.05.2018

CIN: U74990DL2010PTC354497
TEST REPORT Page 2 of 3
Report No M200919009/M200919009-11

ID- M200919009-1

Chemical Analysis
Sr.No. Tests/Parameter Results Requirement Test method Conformity
(as per
IS:269:2015)

1 Lime Saturation Factor 0.93 0.8-1.02 IS:4032-1985(RA:2019) Yes

CaO-0.7 SO3
2.8 SiO2+1.2 Al2O3+0.65Fe203

2 Al2O3 to Fe203 Ratio 1.04 0.66 Min. IS:4032-1985(RA:2019) Yes

3 Insoluble Residue, % by mass 0.94 5.0 Max. IS: 4032:1985(RA:2019) Yes

Clause.4.10

4 Magnesia (MgO), % by mass 2.31 6.0 Max. IS: 4032:1985(RA:2019) Yes

clause.4.8.1

5 Total Sulphur Content (SO3), % by mass 2.77 3.5Max. IS: 4032:1985(RA:2019) Yes
clause.4.9
6 Loss on Ignition, % by mass 3.87 4.0 Max. IS: 4032:1985(RA:2019) Yes
clause.4.2

7 Chloride (Cl), % by mass 0.016 0.10 Max. IS: 4032:1985(RA:2019) Yes

clause.4.13 Amnd.2 (2010)

8 Alkali Content (as Na2O), % by mass # 0.33 0.60 Max. IS: 4032:1985(RA:2019) Yes
clause.4.11.4

# In the case of reactive aggregates, the use of cement with alkali content below 0.60% expressed as sodium oxide (Na2O +
0.658 K2O), is recommended.

Digitally signed
by RAKESH
ULR-TC816320000005269F KUMAR
Date: 2020.09.30
11:24:25 +05:30
Analyst Signature Testing(TC-8163) Authorised Signatory
 Format No: SSA/TRF/GEN
Issue No: 01, Issue Date:10.05.2018

CIN: U74990DL2010PTC354497
TEST REPORT Page 3 of 3
Report No M200919009/M200919009-11
ID-M200919009-1

Sl. Tests Results Requirements Conformity Test Method

No.
(as per IS: 269:2015)

1 Standard Consistency, % 29.5 --- --- IS:4031(Pt.4)-

1988/R2019

2 Fineness, M2/Kg (Blaine) 290.2 225 Min. Yes IS:4031(Pt.2)-

1999/R2013

3 Setting Time (Minutes)

IS:4031(Pt.5)-
(a) Initial 140 30 Min. Yes
1988/R2019
(b) Final 220 600 Max.
4 Soundness
IS:4031(Pt.3)-
(a) Lechatelier Expansion (mm) 1.0 10 Max. Yes 1988/R2019
(b) Auto Clave Expansion (%) 0.04 0.8 Max.

5 Density, g/cc 3.13 --- --- IS:4031(Pt.11)-

1988/R2019

6 Compressive Strength, Mpa

(a) At 3 days 36.5 27 Min. IS:4031(Pt.6)-

Yes
(b) At 7 days 47.5 37 Min. 1988/R2019
(c) At 28 days Awaited 53 Min. Awaited

---------------------------------------------------------------END OF REPORT---------------------------------------------------------------

-- End of Test Report --

Digitally signed
by Yogesh Singh
ULR-TC816320000005269F Date:
2020.09.29
11:24:27 +05:30
Analyst Signature Testing(TC-8163) Authorised Signatory