Technical Data Sheet
LOCTITE® EA 3476
Known as NORTH AMERICA - FIXMASTER STAINLESS STEEL PUTTY
May-2017
PRODUCT DESCRIPTION Hardener:
LOCTITE® EA 3476 provides the following product Weight per volume kg/L 1.43 to 1.46LMS
characteristics: (lbs/gal) (11.9 to 12.2LMS)
Technology Epoxy Viscosity, Brookfield - RVDV, 25 °C, mPa·s (cP):
Chemical Type Epoxy Spindle TF, speed 2.5 rpm 2,000,000 to 2,800,000
Appearance (Resin) Steel GrayLMS
Appearance (Hardener) WhiteLMS Mixed:
Appearance (Mixed) Metallic gray paste Density @ 21 °C 2.74
Components Two components - requires mixing Flash Point - See SDS
Mix Ratio, by volume - 4 : 1
Resin : Hardener
Mix Ratio, by weight - 9:1 TYPICAL CURING PERFORMANCE
Resin : Hardener
Cure Room temperature cure after mixing Curing Properties
Application North America - Metal Repair Gel Time @ 25 °C, minutes 40 to 50LMS
Specific Benefit ● Resists rust and corrosion - for Working life, minutes 20
long lasting repairs
● Rebuilds worn parts fast - limits
downtime Cure Speed vs. Temperature
● High stainless steel content - The graph below shows the shear strength developed with time
for durability on grit blasted steel lap shears at different temperatures and
● Superior adhesion - forms a tested according to ISO 4587.
solid bond to steel, cast iron, 150
45 °C
stainless steel, concrete, wood
and clean and abraded bronze, 125
% of Full Strength
35 °C
copper and aluminum
100
● Non-sag putty - allows 25 °C
application versatility by 75
conforming to unusual shapes
15 °C
50
LOCTITE® EA 3476 is a stainless steel filled, two-part epoxy 25
repair putty. It repairs parts where a stainless steel finish is 5 °C
desired. Once hardened, it can be machined, drilled, tapped or 0
0 2 4 6 8 12 16 20 24
filed just like the original metal. This product is typically Time, hours
used in applications with an operating range of 30 °C to
105 °C (20F to 225F). Typical application includes renewing, TYPICAL PROPERTIES OF CURED MATERIAL
rebuilding, resurfacing and repairing stainless steel equipment Cured @ 25 °C except where noted
and parts like pumps, shafts, and castings. It can also be used Physical Properties:
for making stainless steel molds. Tensile Strength, ISO 527-2 N/mm² 32
(psi) (4,700)
Tensile Modulus, ASTM D638 N/mm² 10,760
TYPICAL PROPERTIES OF UNCURED MATERIAL
(psi) (1,560,220)
Resin: Compressive Strength, ISO 604 N/mm² 69
Weight per volume kg/L 3.18 to 3.42 (psi) (9,920)
(lbs/gal) (26.5 to 28.5LMS) Compressive Modulus, ISO 604 N/mm² 3,700
Viscosity, Brookfield - RVDV, 25 °C, mPa·s (cP): (psi) (535,850)
Spindle TF, speed 2.5 rpm 2,000,000 to 3,000,000LMS
TDS LOCTITE® EA 3476, May-2017
Flexural strength , ASTM D790 N/mm² 46 Heat Aging
(psi) (6,730) Aged at temperature indicated and tested @ 22 °C
Flexural modulus N/mm² 6,660 200
(psi) (965,320) 120 °C 95 °C
% Initial Strength @ 22 °C
65 °C
Shore Hardness, ISO 868, Shore D 86 150 150 °C
Glass Transition Temperature, ASTM E 1640, °C 68
Coefficient of Thermal Expansion, ISO 11359-2 K-1:
100 180 °C
Below Tg 40×10-06
Above Tg 120×10-06
Elongation, ISO 527-2, % 0.32
Volume Shrinkage, % 5.7 50
Coefficient of Thermal Conductivity ASTM F 433, 0.8
W/(m·K)
0
Abrasion Resistance, ASTM D4060: mg 109
0 250 500 750 1000
1 Kg load, CS-10 wheels, Weight of Material Lost
Time, hours
Electrical Properties:
Volume Resistivity, IEC 60093, ohm-cm 0.39×1015 GENERAL INFORMATION
Surface Resistivity, IEC 60093, ohms 1.25×1015 This product is not recommended for use in pure oxygen
and/or oxygen rich systems and should not be selected as
a sealant for chlorine or other strong oxidizing materials.
TYPICAL PERFORMANCE OF CURED MATERIAL For safe handling information on this product, consult the
Shear Strength Safety Data Sheet (SDS).
Lap Shear Strength, ISO 4587:
Grit Blasted Mild Steel (GBMS) N/mm² 12.4
(psi) (1,800) Surface Preparation
Proper surface preparation is critical to the long-term
performance of this product. The exact requirements vary with
TYPICAL ENVIRONMENTAL RESISTANCE severity of the application, expected service life, and initial
Cured for 72 hours @ 21°C substrate conditions
Lap Shear Strength, ISO 4587:
Grit Blasted Mild Steel (GBMS)
Directions for use:
Hot Strength
1. Remove dirt, oil, grease, etc. with a suitable cleaner, e.g.
Tested at temperature
high pressure water cleaning system using Loctite® SF
150 7840™ (Loctite® Natural Blue® cleaner/degreaser).
2. Blast all surfaces to be coated with a sharp edged angular
% Initial Strength @ 22 °C
125 grit to a depth of profile of 75 to 100 microns and a degree of
cleanliness of Near White Metal (SIS SA 2½ /SSPC-SP 10).
100 3. After blasting, metal surfaces should be cleaned with
waterless cleaner, e.g. with Loctite® SF 7611™ (Loctite® Pro
75
Strength Parts Cleaner), and be coated before any oxidation
50 or contamination takes place.
4. Metal that has been in contact with salt solutions, e.g.
25 seawater, should be grit blasted, high-pressure water blasted,
and left for 24 hours to allow any salts in the metal to sweat to
0 the surface. A test for chloride contamination should be
0 50 100 150 200 performed. The procedure should be repeated until chloride
Temperature, °C concentration on the surface is below 40 ppm.
Application
1. Mix resin and hardener according to mix ratios listed or
transfer entire kit onto a clean and dry mixing surface and
mix material vigorously until a uniform color is obtained.
2. Apply material to prepared surface by first forcing a thin
layer deep into the texture of the substrate.
3. Then Immediately build up to the desired finished
thickness.
4. If using to rebuild shaft, the following applies:
● Machine the worn area down 3 mm (0.125 in) to
produce a square shoulder on part. The material is
Henkel Americas Henkel Europe Henkel Asia Pacific
+860.571.5100 +49.89.320800.1800 +86.21.2891.8859
For the most direct access to local sales and technical support visit: www.henkel.com/industrial
TDS LOCTITE® EA 3476, May-2017
stronger with a square edge versus a feathered Loctite Material SpecificationLMS
edge. LMS dated January-20, 2001 (Resin) and LMS dated October-
● Machine a spiral cut in bottom of area to be repaired 16, 2001 (Hardener). Test reports for each batch are available
to provide mechanical keying into surface. for the indicated properties. LMS test reports include selected
● Apply excess product to ensure small shrinkage QC test parameters considered appropriate to specifications
during cure does not produce depression. for customer use. Additionally, comprehensive controls are in
● Machine the surface to original dimensions prior to place to assure product quality and consistency. Special
full cure, as the product is very wear resistant. customer specification requirements may be coordinated
through Henkel Loctite Quality.
Inspection
Storage
● Visually inspect for pinholes and misses just after Store product in the unopened container in a dry location.
application. Storage information may be indicated on the product container
● Once the coating has cured, repeat visual inspection to labeling.
confirm it is free from pinholes, misses and mechanical Optimal Storage: 8 °C to 21 °C. Storage below 8 °C or
damages. greater than 28 °C can adversely affect product properties.
● Control thickness of the coating, especially in the critical Material removed from containers may be contaminated during
points. use. Do not return product to the original container. Henkel
● Perform a test with a holiday detector to confirm coating Corporation cannot assume responsibility for product which
continuity. has been contaminated or stored under conditions other than
those previously indicated. If additional information is required,
Coverage please contact your local Technical Service Center or
Customer Service Representative.
To achieve a 6 mm (.25 in) thickness, the coverage rate will
be 232cm² (36in²) for 0.45kg (1lb), excluding overthickness,
repairs, etc. Conversions
(°C x 1.8) + 32 = °F
kV/mm x 25.4 = V/mil
Repairs
mm / 25.4 = inches
Any voids, pinholes, or low thickness areas found in the µm / 25.4 = mil
coating should be repaired by lightly abrading, cleaning, and N x 0.225 = lb
applying further product. N/mm x 5.71 = lb/in
N/mm² x 145 = psi
Clean-up MPa x 145 = psi
Immediately after use clean tools with suitable cleaner, e.g. N·m x 8.851 = lb·in
N·m x 0.738 = lb·ft
Loctite® 7070™ or a solvent such as acetone or isopropyl
N·mm x 0.142 = oz·in
alcohol. Once cured, the material can only be removed mPa·s = cP
mechanically
Note:
Technical Tips for Working With Epoxies The information provided in this Technical Data Sheet (TDS) including the
recommendations for use and application of the product are based on our
Environmental Conditions knowledge and experience of the product as at the date of this TDS. The product
● Relative humidity: <85% can have a variety of different applications as well as differing application and
working conditions in your environment that are beyond our control. Henkel is,
● Ambient temperature: >15°C (60F) and rising therefore, not liable for the suitability of our product for the production processes
● Substrate temperature must always be 3°C (7F) higher and conditions in respect of which you use them, as well as the intended
than the dew point to avoid condensing moisture on parts. applications and results. We strongly recommend that you carry out your own
prior trials to confirm such suitability of our product.
Any liability in respect of the information in the Technical Data Sheet or any other
Working time and cure depends on temperature and mass: written or oral recommendation(s) regarding the concerned product is excluded,
● The higher the temperature, the faster the cure. except if otherwise explicitly agreed and except in relation to death or personal
● The larger the mass of material mixed, the faster the cure. injury caused by our negligence and any liability under any applicable mandatory
product liability law.
In case products are delivered by Henkel Belgium NV, Henkel Electronic
To speed the cure of epoxies at low temperatures: Materials NV, Henkel Nederland BV, Henkel Technologies France SAS and
● Store epoxy at room temperature. Henkel France SA please additionally note the following:
● Pre-heat repair surface until warm to the touch. In case Henkel would be nevertheless held liable, on whatever legal ground,
Henkel’s liability will in no event exceed the amount of the concerned delivery.
In case products are delivered by Henkel Colombiana, S.A.S. the following
To slow the cure of epoxies at high temperatures: disclaimer is applicable:
● Mix epoxy in small masses to prevent rapid curing. The information provided in this Technical Data Sheet (TDS) including the
● Cool resin/hardener component(s). recommendations for use and application of the product are based on our
knowledge and experience of the product as at the date of this TDS. Henkel is,
therefore, not liable for the suitability of our product for the production processes
and conditions in respect of which you use them, as well as the intended
applications and results. We strongly recommend that you carry out your own
prior trials to confirm such suitability of our product.
Any liability in respect of the information in the Technical Data Sheet or any other
written or oral recommendation(s) regarding the concerned product is excluded,
except if otherwise explicitly agreed and except in relation to death or personal
injury caused by our negligence and any liability under any applicable mandatory
product liability law.
Henkel Americas Henkel Europe Henkel Asia Pacific
+860.571.5100 +49.89.320800.1800 +86.21.2891.8859
For the most direct access to local sales and technical support visit: www.henkel.com/industrial
TDS LOCTITE® EA 3476, May-2017
In case products are delivered by Henkel Corporation, Resin Technology
Group, Inc., or Henkel Canada Corporation, the following disclaimer is
applicable:
The data contained herein are furnished for information only and are believed to
be reliable. We cannot assume responsibility for the results obtained by others
over whose methods we have no control. It is the user's responsibility to
determine suitability for the user's purpose of any production methods mentioned
herein and to adopt such precautions as may be advisable for the protection of
property and of persons against any hazards that may be involved in the handling
and use thereof. In light of the foregoing, Henkel Corporation specifically
disclaims all warranties expressed or implied, including warranties of
merchantability or fitness for a particular purpose, arising from sale or use
of Henkel Corporation’s products. Henkel Corporation specifically
disclaims any liability for consequential or incidental damages of any kind,
including lost profits. The discussion herein of various processes or
compositions is not to be interpreted as representation that they are free from
domination of patents owned by others or as a license under any Henkel
Corporation patents that may cover such processes or compositions. We
recommend that each prospective user test his proposed application before
repetitive use, using this data as a guide. This product may be covered by one or
more United States or foreign patents or patent applications.
Trademark usage: [Except as otherwise noted] All trademarks in this document
are trademarks and/or registered trademarks of Henkel and its affiliates in the
U.S. and elsewhere.
Reference N/A
Henkel Americas Henkel Europe Henkel Asia Pacific
+860.571.5100 +49.89.320800.1800 +86.21.2891.8859
For the most direct access to local sales and technical support visit: www.henkel.com/industrial