CAMPUS® Datasheet

Ultradur® B 4406 G6 Q798 sw 15138 - PBT-GF30 FR

BASF

Product Texts
Injection molding grade with 30 % glass fibers for parts requiring enhanced fire resistance (eg potentiometer parts, plug-and-socket
connectors, switches).

Abbreviated designation according to ISO 1043-1: PBT FR(17)

Rheological properties Value Unit Test Standard
Melt volume-flow rate, MVR 6 cm³/10min ISO 1133
Temperature 275 °C ISO 1133
Load 2.16 kg ISO 1133
Molding shrinkage, parallel 0.4 % ISO 294-4, 2577
Molding shrinkage, normal 1.2 % ISO 294-4, 2577

Mechanical properties Value Unit Test Standard

Tensile modulus 11000 MPa ISO 527-1/-2
Stress at break 150 MPa ISO 527-1/-2
Strain at break 2.1 % ISO 527-1/-2
Charpy impact strength, +23°C 50 kJ/m² ISO 179/1eU
Charpy notched impact strength, +23°C 6 kJ/m² ISO 179/1eA

Thermal properties Value Unit Test Standard

Melting temperature, 10°C/min 220 °C ISO 11357-1/-3
Temp. of deflection under load, 1.80 MPa 205 °C ISO 75-1/-2
Temp. of deflection under load, 0.45 MPa 220 °C ISO 75-1/-2
Burning Behav. at thickness h V-0 class IEC 60695-11-10
Thickness tested (h) 0.8 mm IEC 60695-11-10

Electrical properties Value Unit Test Standard

Dissipation factor, 1MHz 150 E-4 IEC 62631-2-1
Volume resistivity >1E13 Ohm*m IEC 62631-3-1
Comparative tracking index 200 - IEC 60112

Other properties Value Unit Test Standard

Water absorption 0.4 % Sim. to ISO 62
Humidity absorption 0.2 % Sim. to ISO 62
Density 1650 kg/m³ ISO 1183

Material specific properties Value Unit Test Standard

Viscosity number 110 cm³/g ISO 307, 1157, 1628

Test specimen production Value Unit Test Standard

Injection Molding, melt temperature 250 °C ISO 294
Injection Molding, mold temperature 80 °C ISO 294
Injection Molding, injection velocity 200 mm/s ISO 294

Last update: 2020-11-18 Source: https://www.campusplastics.com Page: 1/5

Ultradur® B 4406 G6 Q798 sw 15138 - PBT-GF30 FR
BASF

Diagrams

Viscosity-shear rate Shearstress-shear rate

Viscosity-shear rate Shearstress-shear rate
Ultradur® B 4406 G6 Q798 sw 15138 Ultradur® B 4406 G6 Q798 sw 15138

1E4 245 °C 1E6 245 °C

257 °C 257 °C
270 °C 270 °C

Shearstress in Pa
Viscosity in Pa s

1E3 1E5

1E2 1E4

www.campusplastics.com www.campusplastics.com
1E1 1E3
1E-1 1E0 1E1 1E2 1E3 1E4 1E5 1E-1 1E0 1E1 1E2 1E3 1E4 1E5

Shear rate in 1/s Shear rate in 1/s

Stress-strain Secant modulus-strain

Stress-strain Secant modulus-strain
Ultradur® B 4406 G6 Q798 sw 15138 Ultradur® B 4406 G6 Q798 sw 15138

250 -40 °C 14000 -40 °C

0 °C 0 °C
B 23 °C 12000 23 °C
40 °C 40 °C
200
60 °C 60 °C
B 100 °C 10000 100 °C
Secant modulus in MPa

160 °C 160 °C
B
Stress in MPa

150
B - Break
8000 B B - Break
Y B
Y - Yield Y - Yield
6000 B
100 Y
Y
B 4000

50 B
2000 Y
B
www.campusplastics.com B
www.campusplastics.com
0 0
0 2 4 6 8 10 0 2 4 6 8 10

Strain in % Strain in %

Last update: 2020-11-18 Source: https://www.campusplastics.com Page: 2/5

Ultradur® B 4406 G6 Q798 sw 15138 - PBT-GF30 FR
BASF

Tensile modulus-temperature
Tensile modulus-temperature
Ultradur® B 4406 G6 Q798 sw 15138

1E5
Tensile modulus in MPa

1E4

www.campusplastics.com
1E3
-50 0 50 100 150 200

Temperature in °C

Characteristics

Processing Special Characteristics

Injection Molding Light stabilized or stable to light, U.V. stabilized or stable to
weather, Heat stabilized or stable to heat
Delivery form
Pellets Regional Availability
North America, Europe, Asia Pacific, South and Central America,
Additives Near East/Africa
Lubricants

Other text information

Injection molding
PREPROCESSING
Pre/Post-processing, max. allowed water content: .04 %
Pre/Post-processing, Pre-drying, Temperature: 80 - 120 °C
Pre/Post-processing, Pre-drying, Time: 4 h

PROCESSING
injection molding, Melt temperature, range: 250 - 275 °C
injection molding, Melt temperature, recommended: 260 °C
injection molding, Mold temperature, range: 60 - 100 °C
injection molding, Mold temperature, recommended: 80 °C
injection molding, Dwell time, thermoplastics: 10 min

Chemical Media Resistance

Acids
Acetic Acid (5% by mass) (23°C)
Citric Acid solution (10% by mass) (23°C)
Lactic Acid (10% by mass) (23°C)

Bases
Sodium Hydroxide solution (35% by mass) (23°C)
Ammonium Hydroxide solution (10% by mass) (23°C)

Alcohols

Last update: 2020-11-18 Source: https://www.campusplastics.com Page: 3/5

Ultradur® B 4406 G6 Q798 sw 15138 - PBT-GF30 FR
BASF

Isopropyl alcohol (23°C)

Methanol (23°C)
Ethanol (23°C)

Hydrocarbons
n-Hexane (23°C)
Toluene (23°C)
iso-Octane (23°C)

Ketones
Acetone (23°C)

Ethers
Diethyl ether (23°C)

Mineral oils
SAE 10W40 multigrade motor oil (23°C)
SAE 10W40 multigrade motor oil (130°C)

Standard Fuels
Diesel fuel (pref. ISO 1817 Liquid F) (23°C)

Salt solutions
Sodium Carbonate solution (2% by mass) (23°C)

Other
Ethyl Acetate (23°C)
Water (23°C)
The data contained in this publication are based on our current
knowledge and experience. In view of the many factors that may affect
processing and application of our product, these data do not relieve
processors from carrying out their own investigations and tests. Any
descriptions, drawings, photographs, data, proportions, weights etc.
given herein may change without prior information and do not constitute
the agreed contractual quality of the product. It is the responsibility
of the recipient of our products to ensure that any proprietary rights
and existing laws and legislation are observed. NO WARRANTIES OF ANY
KIND, EITHER EXPRESS OR IMPLIED, INCLUDING WARRANTIES OFMERCHANTABILITY
OR FITNESS FOR A PARTICULAR PURPOSE, ARE MADE REGARDING PRODUCTS
DESCRIBED OR DESIGNS, DATA OR INFORMATION SET FORTH, OR THAT THE
PRODUCTS, DESIGNS, DATA OR INFORMATION MAY BE USED WITHOUT INFRINGING
THEINTELLECTUAL PROPERTY RIGHTS OF OTHERS.

In order to check the availability of products please contact us or our

sales agency.

For more information about our products contact your local BASF
representative or

BASF SE
Dept. PM/K
Fax: 0621-60-49497
e-mail: e-mail

CAMPUS® is a registered trademark of CWFG (Chemie

Last update: 2020-11-18 Source: https://www.campusplastics.com Page: 4/5

Ultradur® B 4406 G6 Q798 sw 15138 - PBT-GF30 FR
BASF

Wirtschaftsfoerderungsgesellschaft GmbH, Frankfurt)

Last update: 2020-11-18 Source: https://www.campusplastics.com Page: 5/5