TDS - Pla Pro HT - Rev 2.0

This technical data sheet provides information on PLA PRO HT filament properties and recommended print settings. Key properties include a density of 1.25 g/cm3, tensile strengths between 22.7-40.8 MPa depending on infill percentage, and a glass transition temperature range of 55-60°C. Recommended print settings are a temperature of 190-220°C, speed of 40-85 mm/s, and optional bed temperature of 30-50°C.

Uploaded by

okta wijaya
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
63 views2 pages

TDS - Pla Pro HT - Rev 2.0

This technical data sheet provides information on PLA PRO HT filament properties and recommended print settings. Key properties include a density of 1.25 g/cm3, tensile strengths between 22.7-40.8 MPa depending on infill percentage, and a glass transition temperature range of 55-60°C. Recommended print settings are a temperature of 190-220°C, speed of 40-85 mm/s, and optional bed temperature of 30-50°C.

Uploaded by

okta wijaya
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
You are on page 1/ 2

TDS Rev. 2.

0
Update 31.05.2019

Technical Data Sheet

PLA PRO HT

IDENTIFICATION
Commercial name Fiber Force PLA PRO HT
Raw Material PLA Compound – Polylactid Acid Compound
Use 3D printing applications
Manufacturer FiberForce Italy srl – Vicolo Dotti 4, 31100 Treviso (ITALY)

PHYSICAL PROPERTIES VALUE STANDARD


Density 1,25 g/cm³ ASTM D729

MECHANICAL PROPERTIES
TENSILE TEST – STANDARD ISO 527
Test specimens printed on Ultimaker 2+ with
the following setup: xy
- Nozzle type: standard brass
- Nozzle Temperature: 210 ⁰C
- Heat bed Temp: 35 ⁰C
- Print speed: 50 mm/s
- Infill orientation: 45⁰

Infill 15% 50% 100%


Tensile strength (Mpa) 22,7 27 40,8
Elastic Modulus (Mpa) 1559 1748 2436
Elongation at break (%) 3,72 4,48 4,64
Energy at break (J) 2,46 3,78 5,84

FIBER FORCE ITALY SRL ~ 31100 TREVISO (TV) – Vicolo Dotti, 4 –


e-mail: [email protected] - REA TV 370002 - PIVA/C.F. 04683260261 – PEC: [email protected]
TDS Rev. 2.0
Update 31.05.2019

FLEXURAL TEST – STANDARD ISO 178


Test specimens printed on Ultimaker 2+ with zy- parallel xy- normal
the following setup:
- Nozzle type: standard brass
- Nozzle Temperature: 210 ⁰C
- Heat bed Temp: 35 ⁰C
- Print speed: 50 mm/s
- Infill orientation: 45⁰

Infill 50% 100% 50% 100%


Flexural strength (Mpa) 73,6 91,8 72,6 90,9
Flexural Modulus (Mpa) 2488 2820 2406 2828
Deformation (%) 3,25 4,06 3,93 4,23

IMPACT TEST IZOD – STANDARD ISO 180


zy- normal xy- parallel
Test specimens printed on Ultimaker 2+ with
the following setup:
- Nozzle type: standard brass
- Nozzle Temperature: 210 ⁰C
- Heat bed Temp: 35 ⁰C
- Print speed: 50 mm/s
- Infill orientation: 45⁰

Infill 50% 100% 50% 100%


Impact strength (KJ/m2) 14,35 23,70 14,08 25,31
Impact Energy (J) 0,57 0,98 0,56 1,01

THERMAL PROPERTIES VALUE STANDARD


Melting Point 165-180 ⁰C ASTM D3418
Heat Deflection Temperature > 100 ⁰C (after post-annealing) ASTM D684
Glass Transition Temperature 55-60 ⁰C ASTM D3518

REMARKS VALUE STANDARD


Post-annealing Guideline 20 minutes at 110 ⁰C N/A

FILAMENT SPECIFICATIONS AND PRINT SETTINGS


Diameter 1.75mm 1.75 ± 0.05 mm
Diameter 2.85mm 2.85 ± 0.05 mm
Roundness deviation max 2%
Suggested Print Temperature 190 – 220 ⁰C
Suggested Print Speed 40 – 85 mm/s
Suggested Bed Temperature 30 – 50 ⁰C (not necessary)

FIBER FORCE ITALY SRL ~ 31100 TREVISO (TV) – Vicolo Dotti, 4 –


e-mail: [email protected] - REA TV 370002 - PIVA/C.F. 04683260261 – PEC: [email protected]