1K-STP-U Adhesive, Desmoseal S XP 2458, 75 Shore A (BBB 7006)

This document provides a formulation for a 1K STP-U adhesive with a silane-terminated polyurethane basis. The formulation lists the components by part weight and suppliers. The preparation instructions specify mixing the components in two steps under vacuum and cooling. Key properties of the adhesive include a hardness of 75 Shore A, tensile strength of 6.3 MPa, and lap shear strength values ranging from 5.5-7.1 MPa over 7 and 28 days.

Uploaded by

Jhon Alexander Isaza Jimenez
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
216 views2 pages

1K-STP-U Adhesive, Desmoseal S XP 2458, 75 Shore A (BBB 7006)

This document provides a formulation for a 1K STP-U adhesive with a silane-terminated polyurethane basis. The formulation lists the components by part weight and suppliers. The preparation instructions specify mixing the components in two steps under vacuum and cooling. Key properties of the adhesive include a hardness of 75 Shore A, tensile strength of 6.3 MPa, and lap shear strength values ranging from 5.5-7.1 MPa over 7 and 28 days.

Uploaded by

Jhon Alexander Isaza Jimenez
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
You are on page 1/ 2

Guide Formulation - page 1 of 2

1K STP-U adhesive, Desmoseal S XP 2458


75 Shore A

Basis: silane-terminated polyurethane

Start formulation of Covestro BBB 7006 (01/16)


Step 1 Desmoseal S XP 2458 (1) 36.43
Mesamoll (2) 4.88
Irganox 1135 (3) 0.49
Fibadur 04007284 (4) 0.10
CAB-O-SIL TS-720 (5) 1.97
SILLITIN Z 86 (6) 51.63
Dynasylan VTMO (7) 2.20
DBU (Diazabicycloundecene) (8) 0.10

Step 2 Dynasylan 1146 (7) 1.10


Dynasylan 1505 (7) 1.10
Total parts by weight 100.00

Preparation For the production of this adhesive a vacuum dissolver with side scraper is needed
(vacuum dissolver PC-LBDV 7, PC Laborsystem).

Step 1:
The components are homogenized successively under stirring; if necessary the filler
may be added in several portions. The drying agent VTMO and the catalyst are added
shortly before dispersion.
The dispersion has to be made under cooling (inside temperature: < 70 °C) under
static vacuum (< 200 mbar) for:
- aaprox. 10 min at 2500 rpm (dissolver) + 250 rpm (butterfly) and
- approx. 10 min at 1000 rpm (dissolver) + 100 rpm (butterfly)
The water content after dispersion should be < 200 ppm.

Step 2:
The components are homogenized with the mixture from step1.
The dispersion has to be made under cooling (inside temperature: < 70 °C):
- approx. 10 min at 1000 rpm (dissolver) + 100 rpm (butterfly)
under static vacuum (< 200 mbar)
- approx. 5 min at 1000 rpm (dissolver) + 100 rpm (butterfly)
under dynamic vacuum

Remarks The adhesive should be filled only into plastic cartridges or into inside coated
aluminum cartridges.

Our applications engineering advice and the information contained in this formulation are based on experience and are made to the best of
our knowledge and belief, they must be regarded however as non-binding advice without guarantee. Working and employment conditions
over which we have no control exclude any damage claim arising from the use of our data and recommendations. Furthermore we cannot
assume any responsibility for patent infringements, which might result from the use of our information. VM-0/0817/08.2017

HOFFMANN MINERAL GmbH • P. O. Box 14 60 • D-86619 Neuburg (Donau) • Phone (+49 84 31) 53-0 • Fax (+49 84 31) 53-3 30
Internet: www.hoffmann-mineral.com • e-Mail: [email protected]
Guide Formulation - page 2 of 2

BBB 7006 (01/16)

Technical Data Film drying time (drying recorder 100 µm wet) h 2:30

Hardness acc. to DIN ISO 7919-1 Shore A 75


Tensile strength acc. to DIN 53504 MPa 6.3
Elongation at break acc. to DIN 53504 % 85

Lap shear strength beech/beech, acc. to DIN EN 205


without layer gap, 7d MPa 5.5
without layer gap, 28d MPa 6.9
with 1 mm layer gap, 7d MPa 5.9
with 1 mm layer gap, 28d MPa 7.1

Suppliers (1) Covestro


(2) Lanxess
(3) BASF
(4) Finke Colors
(5) Cabot
(6) HOFFMANN MINERAL
(7) Evonik Industries
(8) Sigma Aldrich

Our applications engineering advice and the information contained in this formulation are based on experience and are made to the best of
our knowledge and belief, they must be regarded however as non-binding advice without guarantee. Working and employment conditions
over which we have no control exclude any damage claim arising from the use of our data and recommendations. Furthermore we cannot
assume any responsibility for patent infringements, which might result from the use of our information. VM-0/0817/08.2017

HOFFMANN MINERAL GmbH • P. O. Box 14 60 • D-86619 Neuburg (Donau) • Phone (+49 84 31) 53-0 • Fax (+49 84 31) 53-3 30
Internet: www.hoffmann-mineral.com • e-Mail: [email protected]