PRODUCT DATA SHEET

STOPAQ® OUTERWRAP HTPP

Product properties of Stopaq® Outerwrap HTPP
Product Information Colour Black
Thickness Backing 0.25 mm [10 mils]
Product description: Stopaq® Outerwrap HTPP is a high temperature Total 0.63 mm [25 mils]
Temperature range Buried and immersed conditions:
polymeric tape that is an integral part of Stopaq® non-crystalline low-
 Operational: -35°C [-49°F] to +95°C [+203°F]
viscosity coating systems that further comprises Stopaq®
Atmospheric and CUI conditions:
Wrappingband. Stopaq® Outerwrap HTPP provides protection of the  Operational: -35°C [-49°F] to +120°C [+248°F]
coating system against mechanical forces like impact, indentation, and Peel strength layer to Before ageing
A)

shear. Furthermore it provides circumferential compression to the layer before and after  Peel strength (P0)
Stopaq® Wrappingband material, thereby accelerating the bond to the accelerated ageing  @+23°C [+73°F] ≥ 0.2 N/mm [≥ 18 oz/in] (typical
substrate and also supporting self-healing of the coating. tests 1.7 N/mm [155 oz/in])
 @+95°C [+203°F] ≥ 0.02 N/mm [≥ 1.8 oz/in] (typical
Stopaq® Outerwrap HTPP is made of a radiation cross-linked high 0.135 N/mm [12 oz/in])
density polyethylene backing (HDPE) and a cross-linked elastomeric A)
After thermal ageing for 100 days at +115°C [+239°F]
adhesive, provided with a release liner for proper unwinding of the roll.
 Peel strength: 1.0 N/mm [91 oz/in] (typical)
Stopaq® Outerwrap HTPP is very suitable for use on buried and
 P100 / P0: 0.6 (typical)
immersed pipes, for use on pipes and risers in offshore atmospheric
conditions, and for use on pipes susceptible for corrosion under After hot water immersion 100 days at +95°C [+203°F] A)
insulation. The heavy-duty adhesive layer provides good adhesion to the  Peel strength: 3.3 N/mm [301 oz/in] (typical)
outer surface of Stopaq® Wrappingband as well as to its own backing.  P100 / P0: 1.9 (typical)
Stopaq® Outerwrap HTPP is a highly flexible UV-resistant tape that also Peel strength to plant Before ageing A)
has good resistance to various chemicals. coating PP before and  Peel strength (P0)
after accelerated  @+23°C [+73°F]:1.7 N/mm [155 oz/in](typical)
ageing tests  @+95°C [+203°F]: 0.10 N/mm [≥ 9 oz/in] (typical)
Features:
After thermal ageing for 100 days at +115°C [+239°F] A)
 Provides excellent impact and indentation resistance.  Peel strength: 0.70 N/mm [64 oz/in] (typical)
 Very high resistance to ageing, even when exposed to maximum or  P100 / P0: 0.4 (typical)
minimum temperature for longer periods of time.
 Suitable for continuous use at high service temperatures. After hot water immersion 100 days at +95°C [+203°F] A)
 UV-resistant and good resistance to various chemicals.  Peel strength: 2.4 N/mm [219 oz/in] (typical)
 Good adhesion to Stopaq® Wrappingband as well as to its own  P100 / P0: 1.4 (typical)
Peel strength to plant Before ageing A)
backing.
coating FBE before  Peel strength (P0)
 Cold applied, good conformability and after accelerated  @+23°C [+73°F]::2.5 N/mm [228 oz/in](typical)
ageing tests  @+95°C [+203°F]: 0.11 N/mm [10 oz/in](typical)
Benefits:
 Very suitable for manual application After thermal ageing for 100 days at +115°C [+239°F] A)
 Fast and easy field application.  Peel strength 0.80 N/mm [64 oz/in] (typical)
 Resists impacts and indentations which may occur during installation  P100 / P0: 0.3 (typical)
and backfilling.
After hot water immersion 100 days at +95°C [+203°F] A)
 Peel strength: 3.0 N/mm [274 oz/in] (typical)
 P100 / P0: 1.2 (typical)
Application examples Elongation at break Before ageing
before and after  Elongation (E0): 792% (typical)
®
Buried and immersed pipes: As Outerwrap tape on Stopaq corrosion accelerated ageing
preventing Wrappingband, applied on buried and immersed pipes, tests After thermal ageing for 100 days at +115°C [+239°F]
fittings and field joints made of carbon steel, alloy steel or ductile iron.  E100 / E0 ≥ 0.9 (typical)
Elastic modulus before Before ageing A)
Above ground and offshore pipes and risers: As Outerwrap tape on and after accelerated  Elastic modulus (Emod0): 0.074 GPa (typical)
Stopaq® corrosion preventing Wrappingband, applied on carbon steel, ageing tests
alloy steel and ductile iron pipes, field joints and fittings exposed to After thermal ageing for 100 days at +115°C [+239°F] A)
extreme atmospheric conditions.  Emod100 / Emod0 ≥ 0.63 (typical)
Corrosion Under Insulation: As Outerwrap tape on Stopaq® corrosion Properties of coating system comprising Stopaq® Wrappingband
preventing Wrappingband applied on thermally insulated pipes, field CZHT and Stopaq® Outerwrap HTPP
joints and fittings made of carbon steel, alloy steel pipes and ductile Impact resistance Tested at 15 J [132 in.lbf] A) and at 40 J [354 in.lbf]
iron..  @+23°C [+73°F]: no holidays A)
 @+95°C [+203°F]: no holidays
Pipe coating repair and rehabilitation: As Outerwrap tape on Stopaq® Indentation resistance Tested with 10 N/mm² [1450 psi] A) @ +23°C [+73°F] and
corrosion preventing Wrappingband, applied as repair or rehabilitation of @ +95°C [+203°F]:
pipeline coating defects.  no holidays, residual thickness ≥ 0.6 mm [24 mils] B)
Cathodic disbondment Tested @ +23°C [+73°F] and @ +95°C [+203°F] A)
resistance  Disbondment 0 mm, no holiday. Defect Ø 6mm [1/4”]
self-healed within 24 hours.
General order information Self-healing test Tested @ +23°C [+73°F] and @ +95°C [+203°F]
Product Stopaq® Outerwrap HTPP is available in rolls,  Completed < 24 hours, no holiday.
wound on cardboard cores, packed in cardboard Ageing resistance test Acc. ISO 20340:2009 Annex A (4200 h), tested on
boxes: carbon steel (St 3, Sa 2 ½), on 304 stainless steel, and
Art. Nr.: Product dimensions (W x L) and contents: on existing liquid epoxy coating over carbon steel
1249-03048 2 inch x 100 ft  Corrosion creep from scribe: M ≤ 8.0 mm
1250-03048 4 inch x 100 ft  ISO 4628-2 Blistering: 0(S0)
 ISO 4628-3 Rusting: Ri 0
Handling Handle with care. Keep boxes upright.
 ISO 4628-4 Cracking: 0(S0)
Storage Store indoor, clean and dry, away from direct  ISO 4628-5 Flaking: 0(S0)
sunlight in a cool place below +40°C [104°F].  ISO 4628-6 Chalking: 0
A)
According to ISO 21809-3:2016 (2nd ed.) for coating type 13
B)
(within 1 hour after removal of load)

V 4 / 20160426 (EN) Page 1 / 2

 ®
PRODUCT DATA SHEET STOPAQ OUTERWRAP HTPP

Application instruction - Job preparation Example - After application of the circumferential wraps,
Tools, equipment  Scissors, knife and measuring tape Pipe wrapping consecutive spiral wraps should have an
and auxiliaries (continued) overlap of ≥ 50%
Additional coating Stopaq® Outerwrap HTPP is applied as integral Avoid air inclusions. Avoid tenting and bridging
materials part of a coating system that consists of other Continue spiral wrapping until reaching the
Stopaq® coating materials, e.g. boundary of the area to be coated, leaving 3 mm
Corrosion preventing materials: of the previously applied Stopaq® Wrappingband
 Stopaq® Wrappingband CZHT visible at the boundary.
 Stopaq® Paste CZHT
Additional mechanical protective layers may When more than one roll of Outerwrap HTPP is
also be applied over the complete coating, e.g. needed to continue wrapping, an overlap on the
 Stopaq® Polyester end of the previously applied Outerwrap HTPP
should be created of at least 100 mm.
 Stopaq® Vinylester
 Stopaq® Outerglass Shield XT End wrapping with two full circumferential wraps
High humidity Stopaq® Outerwrap HTPP can be applied in a perpendicular to the pipe. End with a quarter
humid atmosphere. The substrate should be circumferential wrap of Outerwrap HTPP without
free from condensing water which can be tension. In case of wrapping on horizontal pipes,
reached by keeping the temperature at least 3°C the tape end should face downwards ending at 3
[6°F] above dew point. o’clock position. Cut off in a tie-form.
Work area and The substrate should be dry, clean and The applied Outerwrap HTPP must look smooth
substrate protected against negative weather influences. and tight and should be shaped around all
Temperature of the substrate should preferably details and into corners..
be between +10°C and +50°C.
Product conditions Stopaq® Outerwrap HTPP should be dry and the Handling and commissioning
temperature should preferably be between +10° Exposure to loads Objects coated with Stopaq® Outerwrap HTPP
C [+50°F] and +30°C [+86°F] for the ease of should not be exposed to excessive loads e.g.
application. from supports- or lifting equipment.
Immersion or Immersion or burying is possible immediately
burying after completion of the coating application.
Application instruction - Brief version Consult data sheets for specific instructions of
General Specific application instructions are available at additional materials used. Backfill and compact
Seal For Life Industries, e.g. for wrapping of with clean sand and filling material without sharp
pipes, field joints, fittings, etc. stones or hard lumps of soil.
Example - Horizontal pipelines should be spirally wrapped
Pipe wrapping from left-to-right or from right-to-left. Pipelines Information
positioned with an angle deviating from Documentation Extensive information is available on our web-
horizontal should be wrapped from bottom to top site. Application instructions and other
(e.g. risers). documentation can be obtained by contacting
In general Stopaq® Outerwrap HTPP should be our head office, from our local distributor or by
applied with tension by gently pulling the roll of sending email to [email protected]
material, unless stated otherwise in specific Certified staff Application of the described coating system
application instructions. should be carried out by certified personnel.
Start wrapping Outerwrap HTPP with two full
circumferential wraps perpendicular to the pipe,
leaving 3 mm of the previously applied Stopaq®
Wrappingband visible at the boundary.

Seal For Life Industries LLC Seal For Life Industries Mexico Seal For Life Industries Seal For Life Industries BVBA Seal For Life India Private Ltd.
Franklin, MA, USA S de R.L. de C.V. Stopaq B.V. Westerlo, Belgium Baroda, India
Tel: +1 508 918 1600 Tijuana, Mexico Stadskanaal, the Netherlands Tel: +32 14 722 500 Tel: +91 2667 264 721
Toll Free: +1 800 248 7659 Tel USA: +1 858 633 9797 Tel: +31 599 696 170 Fax: +32 14 722 570 Fax: +91 2667 264 724
Fax:+1 508 918 1905 Fax USA: +1 858 633 9740 Fax: +31 599 696 177 [email protected] [email protected]
[email protected] Tel Mx: +52 664 647 4397 [email protected]
Fax Mx: +52 664 607 9105
[email protected]

Anodeflex® - Stopaq® - Polyken® - Covalence® - Powercrete® - Sealtaq® - Blockr® - Easy.Qote® - SynergyQ®

DISCLAIMER: Seal For Life Industries warrants that the product(s) represented within conform(s) to its/their chemical and physical description and is appropriate for the use as stated on the respective technical data sheet when used in
compliance with Seal For Life Industries written instructions. Since many installation factors are beyond the control of Seal For Life Industries, the user is obligated to determine the suitability of the products for the intended use and assume all
risks and liabilities in connection herewith. Seal For Life Industries liability is stated in the standard terms and conditions of sale. Seal For Life Industries makes no other warranty either expressed or implied. All information contained in the
respective technical data sheet(s) should be used as a guide and is subject to change without notice. This document supersedes all previous revisions. Please see revision date on the left. Stopaq® is a registered trademark of Seal For Life
Industries.

V 4 / 20160426 (EN) Page 2 / 2