Aluminum 6351-T6; 6351-T651 https://www.matweb.com/search/datasheet_print.aspx?

matguid=ca1cf891973c4745b41677780dad6240

Aluminum 6351-T6; 6351-T651

Categories: Metal; Nonferrous Metal; Aluminum Alloy; 6000 Series Aluminum Alloy

Material Notes: Data points with the AA note have been provided by the Aluminum Association, Inc. and are NOT FOR DESIGN.
Composition Notes:
Composition information provided by the Aluminum Association and is not for design.

Key Words: AA6351-T6; AA6351-T651, UNS A96351; ISO AlSi1Mg0.5Mn; Aluminum 6351-T651; Aluminium 6351-T6; Aluminium 6351-T651; Al6351-T6
Vendors: No vendors are listed for this material. Please click here if you are a supplier and would like information on how to add your listing to this material.

Physical Properties Metric English Comments

Density 2.71 g/cc 0.0979 lb/in³ AA; Typical

Mechanical Properties Metric English Comments

Hardness, Brinell 95 95 AA; Typical; 500 g load; 10 mm ball
Hardness, Knoop 130 130 Converted from Brinell Hardness Value
Hardness, Rockwell A 40 40 Converted from Brinell Hardness Value
Hardness, Rockwell B 60 60 Converted from Brinell Hardness Value
Hardness, Vickers 107 107 Converted from Brinell Hardness Value
Tensile Strength, Ultimate 310 MPa 45000 psi AA; Typical
Tensile Strength, Yield 283 MPa 41000 psi AA; Typical
Elongation at Break 14 % 14 % AA; Typical
@Thickness 1.59 mm @Thickness 0.0625 in
Modulus of Elasticity 68.9 GPa 10000 ksi AA; Typical; Average of tension and compression. Compression
modulus is about 2% greater than tensile modulus.
Poissons Ratio 0.33 0.33 Estimated from trends in similar Al alloys.
Fatigue Strength 89.6 MPa 13000 psi completely reversed stress; RR Moore machine/specimen
@# of Cycles 5.00e+8 @# of Cycles 5.00e+8
Shear Modulus 26.0 GPa 3770 ksi Estimated from similar Al alloys.
Shear Strength 200 MPa 29000 psi AA; Typical

Electrical Properties Metric English Comments

Electrical Resistivity 0.00000382 ohm-cm 0.00000382 ohm-cm AA; Typical
@Temperature 20.0 °C @Temperature 68.0 °F

Thermal Properties Metric English Comments

CTE, linear 23.4 µm/m-°C 13.0 µin/in-°F AA; Typical; average over range
@Temperature 20.0 - 100 °C @Temperature 68.0 - 212 °F

1 of 2 22-02-2023, 07:00 pm
Aluminum 6351-T6; 6351-T651 https://www.matweb.com/search/datasheet_print.aspx?matguid=ca1cf891973c4745b41677780dad6240

25.0 µm/m-°C 13.9 µin/in-°F

@Temperature 20.0 - 300 °C @Temperature 68.0 - 572 °F
Specific Heat Capacity 0.890 J/g-°C 0.213 BTU/lb-°F Estimated from trends in similar Al alloys.
Thermal Conductivity 176 W/m-K 1220 BTU-in/hr-ft²-°F AA; Typical at 77°F
Melting Point 554 - 649 °C 1030 - 1200 °F AA; Typical range based on typical composition for wrought
products >= 1/4 in. thickness
Solidus 554 °C 1030 °F AA; Typical
Liquidus 649 °C 1200 °F AA; Typical

Processing Properties Metric English Comments

Annealing Temperature 349 °C 660 °F hold at temperature for about 4 hr
Solution Temperature 504 °C 940 °F
Aging Temperature 170 °C 338 °F hold at temperature for 6 hr

Component Elements Properties Metric English Comments

Aluminum, Al 95.9 - 98.5 % 95.9 - 98.5 % As remainder
Copper, Cu <= 0.10 % <= 0.10 %
Iron, Fe <= 0.50 % <= 0.50 %
Magnesium, Mg 0.40 - 0.80 % 0.40 - 0.80 %
Manganese, Mn 0.40 - 0.80 % 0.40 - 0.80 %
Other, each <= 0.05 % <= 0.05 %
Other, total <= 0.15 % <= 0.15 %
Silicon, Si 0.70 - 1.3 % 0.70 - 1.3 %
Titanium, Ti <= 0.20 % <= 0.20 %
Zinc, Zn <= 0.20 % <= 0.20 %

References for this datasheet.

Some of the values displayed above may have been converted from their original units and/or rounded in order to display the information in a consistent format. Users requiring more precise data for scientific or engineering
calculations can click on the property value to see the original value as well as raw conversions to equivalent units. We advise that you only use the original value or one of its raw conversions in your calculations to minimize rounding
error. We also ask that you refer to MatWeb's terms of use regarding this information. Click here to view all the property values for this datasheet as they were originally entered into MatWeb.

2 of 2 22-02-2023, 07:00 pm