C R E AT I O N WILLI GELLER I N T E R N AT I O N A L – S I M P LY BRILLIANT

INSTRUCTIONS FOR USE

C R E A PA S T
TECHNICAL HINTS

· Make certain that the Creapast brush is only very slightly

moist. After cleaning the brush dry it.
Never dilute Creapast with water!
· The consistency of Creapast can only be adjusted slightly with
Universal Fluid (UF).
Avoid drying the material too quickly prior to and after placing it
in the firing chamber (bubbles due to boilling)!
Pre-drying time: 6 minutes.
· Preheating temperature is dependig on the furnace in use
400 – 550 °C.
· Once it has dried out, Creapast cannot be adjusted.
· Extruded material must not be drawn up into the syringe again.
· Ensure that Creapast is applied in uniform thickness.
· Creapast is compatible with Creation CC powder opaque.
 M E TA L F R A M E W O R K
The metal framework should be finished and oxidized according
to the manufacturer‘s instructions.

MIXING
1 2 Mix the paste opaque well with an agate spatula to an homoge-
neous consistency.

O PA Q U E M O D I F I E R
You have the choice out of four opaque modifiers. They can be
used pure or mixed into the paste opaque.

A P P LY I N G
3 4 Use the Creapast brush to apply the paste opaque to the metal
framework, ensuring that the brushstrokes are even and that
the metal is masked by approximately 75%.

1st O PA Q U E F I R I N G
Imprint
Pre-drying time: 6 minutes. The first firing is carried out at 980 °C,
Editor: Creation Willi Geller International AG in vacuum.
Content: ZTM Patrick Boche, ZTM Oliver Heinzle
Picture credits: ZTM Oliver Heinzle
Layout: hellblau. visuelle kommunikation Non-precious alloys: 1.000 °C!
 2nd O PA Q U E A P P L I E D
The second coating of the opaque should mask the metal com-
pletely. If necessary, the opaque shade can be adjusted slightly
with Opaque Intensive.

5 6 2nd O PA Q U E F I R I N G
The second opaque firing is carried out at 950 °C, in vacuum.
Once the final temperature has been attained, the firing chamber
is vented once again.

Holding time: 1 minute

Pre-drying time: 6 minutes

7 After the second firing, the opaque should have an eggshell finish.

C R E A PA S T A S S O R T M E N T
- 16 opaque pastes, Vita® Classic shades (3 g each)
- 4 opaque modifier pastes
- 1 flat brush

Vita® is a registrated Trademark of VITA Zahnfabrik, H. Rauter GmbH & Co. KG,
Bad Säckingen, Germany
FIRING INSTRUCTIONS

03/09
Preheating Raise of
Drying Time V Final Holding Time Appearance
Temperature Temperature Temperature
Wash

910251
WOP Opak 550 °C 6 min. 80 °C/min. + 950 °C 1 min.
Lightly shining
Creapast * 550 °C 6 min. 80 °C/min. + 980 °C 1 min.

© Creation Willi Geller International GmbH

Powder Opaque * 600 °C 2 min. 80 °C/min. + 980 °C 1 min.
Opaque Firing
Creapast 550 °C 6 min. 80 °C/min. + 950 °C 1 min. Eggshell
shining
Powder Opaque 600 °C 2 min. 80 °C/min. + 950 °C 1 min.
1st and 2nd 600 °C 2 min. 80 °C/min. + 950 °C 1 min.
Shoulder Firing
1st Dentine Firing 580 °C 6 min. 55 °C/min. + 920 °C 1 min. Lightly shining
2nd Dentine Firing 580 °C 4 min. 55 °C/min. + 910 °C 1 min.
Glaze Firing 600 °C 2 min. 55 °C/min. – 930 °C - Shining
* When firing non-precious alloy: final temperature 1.000 °C.

The firing parameters given above are gidelines, which always need Distributor
Creation Willi Geller International GmbH
to be adjusted to the furnace used for firing and the situation of the furnace.
Koblacherstraße 3, 6812 Meiningen, Austria
The important thing is to obtain the right firing result. Tel. +43 (0)5522 76784
Fax. +43 (0)5522 73699
Errors and printing errors excepted. Subject to change at any time. [email protected]
www.creation-willigeller.com
Technical inquiries: [email protected] Manufacturer
KLEMA Dentalprodukte GmbH 0483
Koblacherstr. 3a, 6812 Meiningen, Austria