Product Data Sheet: Transocean Cold Zinc Primer 10.16

This document summarizes the product data sheet for Transocean Cold Zinc Primer 10.16, which is a single component zinc metal coating containing 95% pure zinc dust. It can be used as a primer on steel structures and damaged hot-dip galvanized steel to protect against corrosion. The primer dries through solvent evaporation, leaving a dry film containing 95% zinc that provides corrosion protection comparable to hot-dip galvanizing. It can be overcoated with specific Transocean epoxy coatings and is suitable for application by airless spray, air spray, brush, or roller within the listed temperature and humidity conditions.

Uploaded by

rimshadtp
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
104 views

Product Data Sheet: Transocean Cold Zinc Primer 10.16

This document summarizes the product data sheet for Transocean Cold Zinc Primer 10.16, which is a single component zinc metal coating containing 95% pure zinc dust. It can be used as a primer on steel structures and damaged hot-dip galvanized steel to protect against corrosion. The primer dries through solvent evaporation, leaving a dry film containing 95% zinc that provides corrosion protection comparable to hot-dip galvanizing. It can be overcoated with specific Transocean epoxy coatings and is suitable for application by airless spray, air spray, brush, or roller within the listed temperature and humidity conditions.

Uploaded by

rimshadtp
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
You are on page 1/ 3

Product Data Sheet

Transocean Cold Zinc Primer


10.16
Product description.
A single component zinc metal coating with pure zinc dust in a special binder for the protection of steel
structures against corrosion in industrial and marine environments. It dries by solvent evaporation and the
dry film contains 95 + 2% zinc and hence is an excellent alternative to hot dip galvanizing. 10.16 can be
used as a touch-up primer on damaged areas of hot dip galvanized steel and also on bare steel surfaces
subjected to abrasive blasting to Sa 2.5 standard. Metallic luster of pure zinc metal appears when
scratched on the surface. It can be overcoated by Transpoxy Masterbond 4.67 or 4.68. For overcoating
with other products, consult the nearest Transocean Man.
Physical properties.
Colour/Texture Grey/Matt
Volume Solids 52%
Specific gravity 2.41 gr/ml
Flashpoint >22°C

Dry film thickness per Wet film thickness per Theoretical spreading
coat (µ) coat (µ) rate (m2/l)
Range 40 – 75 77 –144 13 – 14.4
Recommended 50 96 10.4

Application data.

Guiding data Airless spray Pressure at nozzle: 140 -180 bar. Nozzle size: 0.38 - 0.53 mm.
Spray angle: 40 - 80 degrees.
Volume of thinner: 0 – 3%.
Guiding data Airspray Pressure. 3 - 5 bar. Nozzle size: 1.2 - 2.0 mm.
Volume of thinner: 0 – 10%.
Brush/Roller Suitable. Volume of thinner: 0 – 5%.

Thinner/Cleaner Transocean Special Thinner 6.01

Conditions Humidity: below 85% RH


Temperature of the paint before application: min: 5°C, max: 30°C.
Substrate temperature: min: 10°C, max: 35°C.
The temperature of the substrate should be at least 3°C above the dew point
of the air. Air temperatures and relative humidity must be measured in the
vicinity of the substrate.

Drying and recoating times.


Substrate Touch dry Dry to handle Dry to recoat
temperature Minimum Maximum (1)
10 °C 40 minutes 8 hours 16 hours Indefinite
23 °C 20 minutes 4 hours 6 hours Indefinite
30 °C 15 minutes 2 hours 4 hours Indefinite

TO 1.55 Page 1 of 2.
TO 1.55 Page 2 of 2.
Surface preparation.
Steel Oil and grease should be removed by solvent cleaning according to SSPC-SP1.
Remove weld spatter and smooth weld seams and sharp edges as applicable.
New steel should be blasted to Sa 2.5 standard.
Apply Transocean Cld Zinc Primer 10.16 immediately after the steel has been
cleaned and the quality of preparation has been approved.

Repair Damages to the hot dip galvanized surface should be power tool cleaned to
ISO-St3. Surface should be dry and free from loose paint, salt, grease and other
contaminants prior to touch-up with Transocean Cold Zinc Primer 10.16.

Recommended paint system.


Transocean Cold zinc Primer 10.16 1 x 50 µ dft.

Health and safety.


Observe the precautionary notices on the label of the container. A material safety data sheet is available
upon request and national or local safety regulations should be followed. This product is intended for use
by professional applicators.
As a general rule, avoid skin- and eye contact by wearing overalls, gloves, goggles, mask, etc. Spillage on
the skin should immediately be removed by thorough washing with lukewarm water and soap or a suitable
industrial cleaner. Eyes should be flushed with fresh water and medical attention sought immediately.
Spraying should be carried out under well-ventilated conditions. Avoid inhalation of solvent vapours and
paint mist by wearing an air mask.
This product contains flammable materials and should be kept away from sparks and open flames.
Smoking in the area should not be permitted.

Disclaimer
The information in this data sheet is provided to the best of our knowledge. However, we have no control
over either quality or condition of the substrate and other factors affecting the use and application of this
product.
Therefore, we cannot accept any liability whatsoever or howsoever arising from the performance of the
product or for any loss or damage arising from the use of this product.
We reserve the right to change the product without notice.

Date of issue: November, 12.

TO 1.55 Page 3 of 2.