ASTM B 117 Trivalent & Chrome Free Finsihes Hour To Whie Corrosion Comparison

This document from Modern Plating Corporation compares the corrosion resistance of various chrome-free and trivalent metal finishes in a salt spray test. It lists the types of finishes tested and provides a chart showing the number of hours before each sample exhibited white corrosion in the salt spray test. The document notes that salt spray testing provides a controlled corrosive environment to compare finishes but does not predict real-world performance, and actual testing in applications is needed to confirm performance.

Uploaded by

vichun sakunyong
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
111 views1 page

ASTM B 117 Trivalent & Chrome Free Finsihes Hour To Whie Corrosion Comparison

This document from Modern Plating Corporation compares the corrosion resistance of various chrome-free and trivalent metal finishes in a salt spray test. It lists the types of finishes tested and provides a chart showing the number of hours before each sample exhibited white corrosion in the salt spray test. The document notes that salt spray testing provides a controlled corrosive environment to compare finishes but does not predict real-world performance, and actual testing in applications is needed to confirm performance.

Uploaded by

vichun sakunyong
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
You are on page 1/ 1

Modern Plating Corporation

Trivalent & Chrome Free Finishes


Hours to White Corrosion Comparison

.0003/8um Tin Zinc Clear GMW3200


.0003/8um Zinc Nickel Black PS8955
.0002/5um Zinc Iron Clear PS8955
.0003/8um Zinc Iron Black, Topcoat PS8955
.0003/8um Zinc Nickel Clear PS8955
.0002/5um Zinc Nickel Clear PS8955
.0003/8um Zinc Nickel Black, Topcoat PS8955
.0003/8um Zinc Iron Clear, Topcoat PS8955
.0002/5um Zinc Iron Clear, Topcoat PS8955
.0003/8um Zinc Iron Black PS8955
.0003/8um Zinc Nickel Clear, Topcoat PS8955
.0002/5um Zinc Nickel Clear, Topcoat PS8955
.0003/8um Zinc Iron Clear PS8955
.0003/8um Zinc Clear, Clearcoat, Wax GMW3044-G
.0003/8um Zinc Clear, Clearcoat, Wax FordS437
.0003/8um Zinc Clear GMW3044-N
.0005/12um Zinc Clear
.0005/12um Zinc Black
.0003/8um Zinc Black
.0002/6um Tin Zinc Clear PS8956
.0005/12um Tin Zinc Clear PS8956
.0004/10um Tin Zinc Clear PS8956
.0003/8um Tin Zinc Clear PS8956
.0003/8um Zinc with HC3 Black
.0003/8um Zinc Plus3 Black
.0003/8um Zinc Clear JS500
.0005/12um Zinc Clear Clearcoat Wax
.0002/5um Sharperize Zinc Nickel WSS-M21 P25-B1
.0003/8um Zinc Clear Clearcoat GMW3044-X
.0005/12um Zinc Clear, Clearcoat
.0003/8um Zinc Plus3 Clear
.0003/8um Zinc Nickel Triclear WSS-M21 P44-A2
.0003/8um Zinc Nickel with Cathodic E-Coat WSS-M21 P44-A3

Zinc Alloy Finishes 0 50 100 150 200 250 300 350 400 450 500
Chrome Free
Hours to White Corrosion
All salt spray testing done in accordance with ASTM-B-117

Salt spray testing provides a controlled corrosive environment and is used to provide relative corrosion resistance comparisons of various finishes. Salt spray testing does not, by itself, provide an accurate prediction of how the finish will actually perform in
real world applications. Salt spray testing results should therefore not be used to predict actual finish performance. Testing in the application must be conducted to confirm actual performance. Variability of results can occur when similar parts are tested in
different salt spray chambers even though the testing conditions are nominally similar and within the ranges specified for such tests.