04042016000000A - Avesta 307-Si - Solid Wire

Avesta 307-Si is a solid wire for welding stainless steel to mild steel or other difficult to weld steels. It has a fully austenitic structure and high corrosion resistance comparable to ASTM 304. The high manganese content gives it good ductility and resistance to hot cracking. It is primarily used for dissimilar welds between stainless and mild/low-alloy steels. Typical analysis shows it contains 0.09% carbon, 0.8% silicon, 7.0% manganese, 19.0% chromium, and 8.0% nickel. As-welded mechanical properties include a yield strength of 470 MPa, tensile strength of 710 MPa, and 42%

Uploaded by

Daniel Guerrero
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
34 views1 page

04042016000000A - Avesta 307-Si - Solid Wire

Avesta 307-Si is a solid wire for welding stainless steel to mild steel or other difficult to weld steels. It has a fully austenitic structure and high corrosion resistance comparable to ASTM 304. The high manganese content gives it good ductility and resistance to hot cracking. It is primarily used for dissimilar welds between stainless and mild/low-alloy steels. Typical analysis shows it contains 0.09% carbon, 0.8% silicon, 7.0% manganese, 19.0% chromium, and 8.0% nickel. As-welded mechanical properties include a yield strength of 470 MPa, tensile strength of 710 MPa, and 42%

Uploaded by

Daniel Guerrero
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
You are on page 1/ 1

Avesta 307-Si

Solid wire, high-alloyed, high corrosion resistant

Classification
EN ISO 14343-A AWS A5.9
G 18 8 Mn -

Characteristics and typical fields of application


Avesta 307-Si is an over-alloyed, fully austenitic consumable for welding stainless steel to mild
steel, low-alloy or Mn-steels. It is also suitable for the welding of some 14 % Mn-steels and other
difficult-to-weld-steels. The high manganese content makes the weld metal, even though it is purely
austenitic, very resistant to hot cracking with a good ductility.
Structure: Fully austenitic.
Scaling temperature: Approx. 850 °C (air).
Corrosion resistance:
Primarily intended for stainless to mild steel connections, however, the corrosion resistance
corresponds to ASTM 304.
Base materials
Avesta 307-Si is primarily used in dissimilar welding between stainless and mild steel or low-alloy
steels.
Typical analysis of the solid wire (wt.-%)
C Si Mn Cr Ni Ferrite
wt.-% 0.09 0.8 7.0 19.0 8.0 0 FN
Mechanical properties of all-weld-metal
Heat Yield Tensile Elongation Impact work
treatment strength strength (L 0 =5d 0 ) ISO-V KV J Hardness
R p0.2 Rm
MPa MPa % +20 °C -40 °C Brinell
u 470 710 42 120 110 220
u untreated, as welded – Shielding gas Ar + 2 – 3 % CO 2
Operating data
Polarity Shielding gas: ø (mm)
DC ( + ) Ar + 2 – 3 % CO 2 0.8
Ar + 2 % O 2 1.0
Gas flow rate: 12 - 16 l/min. 1.2
1.6
Preheating and Heat treatment are generally not necessary. Interpass temperature: Max. 150 °C.
Heat input: max. 2.0 kJ/mm. For constructions that include low-alloy steels in mixed-joints, stress-
relieving may be advisable. Always consult the supplier of the parent metal or seek other expert
advice to ensure that the correct heat treatment process is carried out.

Approvals
DB, TÜV