List of ready tests

No. Test Standards Machine Sample Conditioning Time Conditioning Temperature Test Time Number of Sample Note Application constraints in indonesia Required Equipment
Cutting machines for
Cutting machines for sample finished finished product, and
ISO 6259-1 : 2015 Varies between 1-16 special machines for the
Varies between 2-5 products does not exist, and the machine
1 Tensile ISO 6259-2 : 2015 Roell Zwick Z10 Pipe hours, depending on 1-15 min/pcs production of sample raw
(23 ± 2) °C strips depending on to print raw materials sample is the same
ISO 6259-3 : 2015 Raw Materials the thickness of the material
pipe diameter as the machine for production, so it is not
GB/T 8804 : 2003 pipe
efficient

Cutting machines for

Cutting machines for sample finished finished product, and
This Test value is
products does not exist, and the machine special machines for the
2 Modulus of Elastisitas ASTM D1784-2011 Roell Zwick Z10 Pipe obtained when
to print raw materials sample is the same production of sample raw
Raw Materials performing a tensile
as the machine for production, so it is not material
test
efficient

ISO 306-2022 Pipe PVC : 50 ℃

3 Vicat Softening Vicat HDT Tester PVC : 5 min Min 2 pcs The Chiller is damage
ISO 2507-1:1995 Fittings PE and PP : T : 23 ± 2 °C
Temperature (VST) PE and PP : 16 h
ASTM D 648-2018 Raw Materials dan RH : 50 ± 10 %)
Special machines for the
The machine to print raw materials sample production of sample raw
4 Izod Impact ASTM D256-2023 Electronic izod impact Raw Materials 40 h T : 23 ± 2 °C and RH : 50 ± 10 1 h Min 5 pcs is the same as the machine for production, material
ISO 180-2019 testing machine %
so it is not efficient
Special machines for the
The machine to print raw materials sample production of sample raw
5 Charpy Impact ISO 179-1 : 2023 Automatic Pendulum Raw Materials 16 h T : 23 ± 2 °C and RH : 50 ± 10 1 h Min 5 pcs is the same as the machine for production, material
Impact Tester %
so it is not efficient

6 Particle size distribution ISO 8130-1:2019 Sieve size 0,3 mesh and 0,6 Raw Materials - T : 23 ± 2 °C and RH : 50 ± 10 1-15 min/pcs Min 20 gram The laboratory currently does not have a Sieve 0,3 mesh and 0,6
by sieving mesh % sieve 0.3 mesh and 0.6 mesh mesh

Digital Scales Sartorius,

ASTM D792-20 There is no adequate digital scale, no
7 Density Digital Scales Sartorius Pipe ASTM : 40 h T : 23 ± 2 °C and RH : 50 ± 10 1 h Min 3 pcs Immersion vessel,
ISO 1183-1:2019 stationary support, no immersion vessel,
Fittings ISO : No special time % stationary support,
GB/T 1033.1-2008 and also no hydrometer
hydrometer

ISO: varies between 1-

ISO 1167-1:2006 ISO: in a test Bath where the ISO :
16 h, depending on ISO : Minimal 3 pcs
ISO 1167-2:2006 temperature should not PVC : 1000 h
8 Hydrostatic Pressure Airless pipe tester Pipe pipe thickness ASTM : No special Machine not installed
ISO 1167-3:2006 exceed the temperature for PP : 140 h dan 1000 h
Fittings ASTM: 1 in Tub, 16 conditions
ISO 1167-4:2006 testing PE : 165 h dan 1000 h
hours at room
ASTM D1599-2018 ASTM : (23 ± 2) ℃ ASTM : 60-70 s
temperature

ISO 9969-2016 Pipe Testing Electronic

Roell Zwick Z10 and For fittings required load force of 11 KN,
9 Flattening ASTM D2412-2011 Pipe ISO : 24 h T : 23 ± 2 °C and RH : 50 ± 10 1-15 min/pcs Min 3 pcs Pipe : Length 200 mm Universal Testing Machines
Pipe Testing Electronic but the engine Roell Zwick Z10 only has a
(Deflection 50-60 %) ASTM D2665-2014 Fittings ASTM : 40 h % ± 10 mm with capasity more than 10
Universal Testing Machines max load of 10 KN
Q/LS 19-2023 KN

Roell Zwick Z10 and

10 Ring Stiffness ISO 9969-2016
Pipe Testing Electronic Pipe 24 h T : 23 ± 2 °C and RH : 50 ± 10 1-15 min/pcs Min 3 pcs Pipe : Length 200 mm -
(Deflection 5 %) % ± 10 mm
Universal Testing Machines

Roell Zwick Z10 and

11 Ring Flexibibility ISO 13968 - 2008 Pipe Testing Electronic Pipe 24 h T : 23 ± 2 °C and RH : 50 ± 10 1-15 min/pcs Min 3 pcs Pipe : Length 200 mm -
(Deflection 30 %) % ± 10 mm
Universal Testing Machines

Varies between 1-6

Varies between 1-2 hours, It takes a stainless tray to place the sample
12 Longitudinal Reversion ISO 2505-2005 High temperature test Pipe hours, depending on (23 ± 2) °C Pipe : Length 200 mm
depending on the thickness Min 3 pcs that has been in the oven, rack, iron ruler, Tacl Powder, tray, rack
chamber the thickness of the ± 10 mm
of the pipe and talc powder
pipe

The size of the pipe

diameter, each pipe
diameter produces For impact machine indonesia is not
Varies between 1-4 the number of holes
Resistance to external adequate for testing with this method
13 blows - Round the clock ISO 3127:1994 Falling Weight Impact Pipe hours, depending on 0 °C ± 1 °C 10 - 30 min 10-20 pcs to be done, and there because it takes a quick time for each
Falling Weight Impact
GB/T 14152-2001 Tester for Plastic Pipes the thickness of the are at least 25 blows Tester for Plastic Pipes
method collision against the sample, and need a
pipe for each Sample cooling machine for sample conditioning
length 200 mm ± 10
mm

Micro Computer RCT-ECT Micro Computer RCT-ECT

14 Edgewise Crush ISO 3037-2022
and Paper label crimping
Fibberbox 24 h T : < 40 °C and RH : 10% - 35 10 - 30 min 10 pcs specimen Specimen size : 10 cm No Micro Computer ECT-ECT machine and
and Paper label crimping
Resistance GB/T 6546-2021 (Carton dus) % x 5 cm Paper label crimping and cutting machine
and cutting machine and cutting machine

15 Bursing Strenght ISO 2759-2014 Automatic Bursting Strenth Fibberbox - T : < 40 °C and RH : 10% - 35 10 - 30 min 1 pcs carton No automatic bursting strength testing Automatic Bursting Strenth
GB/T 6545-1998 Tester (Carton dus) % machine Tester
 Specification standard for USA Fitting testing (ASTM)
No. Standard Sample Test Application constraints in indonesia Required Equipment
The machine to print raw materials sample is Special machines for the
Izod Impact the same as the machine for production, so it is production of sample raw
not efficient material

Cutting machines for

Cutting machines for sample finished products finished product, and
does not exist, and the machine to print raw special machines for the
Tensile Strength production of sample raw
materials sample is the same as the machine
ASTM D1784-2011 : Standard Specification for for production, so it is not efficient material
1 Rigid Poly(Vinyl Chloride) (PVC) Compounds and Raw Materials
Chlorinated Poly(Vinyl Chloride) (CPVC) Compounds
Cutting machines for
Cutting machines for sample finished products finished product, and
does not exist, and the machine to print raw special machines for the
Modulus Elastisitas production of sample raw
materials sample is the same as the machine
for production, so it is not efficient material

VST The Chiller is damage

Pipe Testing Electronic
For fittings required load force of 11 KN, but the
ASTM D2465-2020 : Standard Specification for Universal Testing Machines
Flattening engine Roell Zwick Z10 only has a max load of
2 Poly(Vinyl Chloride) (PVC) Plastic Drain, Waste, and Vent Pipe Finish Product with capasity more than 10
10 KN
and Fittings KN
Impact Resistance -

ASTM D2466-2017 : Standard Specification for

3 Finish Product Internal Pressure/Burst Pressure Machine damaged / not installed
Poly(Vinyl Chloride) (PVC) Plastic Pipe Fittings, Schedule 40

ASTM D2467-2020 : Standard Specification for

4 Finish Product Internal Pressure/Burst Pressure Machine damaged / not installed
Poly(Vinyl Chloride) (PVC) Plastic Pipe Fittings, Schedule 80

ASTM D2464-2015 : Standard Specification for

5 Threaded Poly(Vinyl Chloride) (PVC) Plastic Pipe Fittings, Finish Product Internal Pressure/Burst Pressure Machine damaged / not installed
Schedule 80

Additional testing for finished products fittings

No. Standard Sample Test Application constraints in indonesia Required Equipment

ASTM F610/F610M-2010 : Standard Test Method for Evaluating

1 the Quality of Molded Poly(Vinyl Chloride) (PVC) Plastic Pipe Finish Product Heat Reversion Need a rack to cool the sample Rack
Fittings by the Heat Reversion Technique
 Specification standard for Local Fitting testing (JIS)
No. Standard Sample Test Application constraints in indonesia Required Equipment

There is no specification for product approval

Flattening
requirements for this test in standard JIS K 6743

Cooling machine that can

Impact Resistance Requires cooling machine for conditioning reach temperature 0 ℃
±1℃
JIS K 6743 : 2016 : Unplasticied poly(vinyl
Hot internal pressure Creep test /
1 chloride) (PVC-U) pipe fittings for water Finish Product Machine damaged / not installed
Burst Pressure
supply
Thermal Relaxation -
Pressure Resistance *
VST *
Waterquality *
Compresibility *
Tensile *

* Not done this test for local fitting products

Additional testing for finished products fittings

No. Standard Sample Test Application constraints in indonesia Required Equipment
ISO 580-2015 : Plastics piping and ducting
systems — Injection-moulded thermoplastics
1 Finish Product Heat Reversion Need a rack to cool the sample Rack
fittings — Methods for visually assessing the
effects of heating

JIS S 3200-1 : 1997 : Water supply equipment Pressure resistance

2 Finish Product Machine damaged / not installed
- Pressure resistance test method (Burst/Hydrostatic Pressure)
 Specification standard for Pipes testing (ISO)
No. Standard Sample Pengujian Application constraints in indonesia Required Equipment

For impact machine indonesia is not adequate

for testing with this method because it takes a
Falling Weight Impact Tester
Impact Strength quick time for each collision against the sample,
for Plastic Pipes
and need a cooling machine for sample
conditioning

Resistance to internal pressure Machine not installed

BS EN 1452-2 : 2000 : Plastics pipping systems for water supply -
1 Finish Product It takes a stainless tray to place the sample that
unplasticizied poliy (vinyl chloride) (PVC-U) Part 2 : Pipes
Longitudinal Reversion has been in the oven, rack, iron ruler, and talc Tacl Powder, tray, rack
powder
VST *
Resistance to dichloromethane at
elevated temperature *
Gas-fhase chromatography *
Ring Stiffness -

For impact machine indonesia is not adequate

for testing with this method because it takes a
Falling Weight Impact Tester
Impact Strength quick time for each collision against the sample,
for Plastic Pipes
Finish Product (Generals) and need a cooling machine for sample
conditioning

Ring Flexibility -
Creep Ratio *
Tensile Strength of seam *
Resistance to internal pressure Machine not installed
VST *
It takes a stainless tray to place the sample that
Longitudinal Reversion has been in the oven, rack, iron ruler, and talc Tacl Powder, tray, rack
Finish Product (PVC-U) powder
ISO 21138-2 : 2020 : Plastics pipping systems for non-pressure Resistance to dichloromethane at
underground drainage and sewerage - structure wall pipping systems elevated temperature *
2
of unplasticizied poliy (vinyl chloride) (PVC-U), polyppropylene (PP)
and polyethylene (PE) Uniaxial tensile test *
DSC *
Resistance to internal pressure Machine not installed
MFR *
Thermal Stability *
Finish Product (PE) Density
It takes a stainless tray to place the sample that
Longitudinal Reversion has been in the oven, rack, iron ruler, and talc Tacl Powder, tray, rack
powder
Resistance to internal pressure Machine not installed
MFR *
Thermal Stability *
Finish Product (PP)
It takes a stainless tray to place the sample that
Longitudinal Reversion has been in the oven, rack, iron ruler, and talc Tacl Powder, tray, rack
powder

* Not done this test for pipe products