Hdpe HCH 5110

Uploaded by

mohamad mostafavi
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
You are on page 1/ 4

HDPE HCH 5110

Properties Unit Typical value Test Method


Polymer Properties
MFI(190 0C /21.6 Kg ) Dg/min 10 ISO 1133
Density Kg/m3 951 ISO 1133
Mechanical properties
Tensile Modulus of elasticity MPa 1050 ISO527-1,2
Max. Tensile Strength (MD) MPa 55 ISO 527-1;3
Max. Tensile Strength (TD) MPa 55 ISO 527-1;3
Tensile Stress at break (TD) % 580 ISO 527-1
Tensile Stress at break (MD) % 620 ISO 527-1
Elemendorf tear strength(MD) mN 26 ISO 6383-2
Elemendorf tear strength(TD) mN 10 ISO 6383-2
Failure energy J/mm 250 DIN 53373
Dart Drop Impact g 800 ASTM D 1709
Thermal Properties
oC 132 ISO 3146
Melting Point
oC 127 ISO 306
Vicat Temp , (A50,50 oC /h , 10 N)

Additives :Antioxidant -Heat stabilizer

Notes:
Typical values; not to be construed as specifications
Blown film: thickness 20 μm, extruded at melt temperature of 220°C, long stalk process, blow
up ratio 4:1
HDPE HCH 5110

Application
HCH 5110 is suitable for Film, Bags, Products for Use in Property Modification

General information
HCH5110 has been manufactured using Basell Lupotech G licensed technology

Processing:
Recommended melt temperatures: 180 - 240°C
Recommended film thickness: 10 – 50 μm

Packaging
Supplied in pellet form and can be packaged in 25kg bags, 1 ton semi bulk or 17 ton bulk.

Food packaging
The above mentioned grade meets the relevant requirements of plastics directive 2002/72/EC
(06-08-2002) and its amendments till directive 2008/39EC relating to plastic materials and
articles intended to come into contact with foodstuffs .

Pharmaceutical Application
The above mentioned grade meets the requirements of the European pharmacopeia version 6
section 3.1.5 for pharmaceutical application.

Conveying
Conveying equipment should be designed prevent accumulation of fines and dust particles can,
under certain conditions, pose an explosion hazard. We recommend that the conveying system
used:
1. be equipped with adequate filters
2. is operated and maintained in such a manner to ensure no leaks develop
3. that adequate grounding exists at all times

We further recommended that good housekeeping will practiced throughout the facility
HDPE HCH 5110

Storage
As ultraviolet light may cause a change in the material, all resins should be protected from
direct sunlight and/or heat during storage. The storage location should also be dry, dust Free
and the ambient temperature should not exceed 50 0C. It is also advisable to process
polyethylene resins (in pelletized or powder from) within 6 months after delivery, this because
also excessive aging of polyethylene can lead to a deterioration in quality.

Handling
Minimal protection to prevent possible mechanical or thermal injury to the eyes. Fabrication
areas should be ventilated to carry away fumes or vapors.

Combustibility
Polyethylene resins will burn when supplied adequate heat and oxygen. They should be
handled and stored away from contact with direct flames and/or other ignition sources .in
burning; polyethylene resins contribute high heat and may generate a dense black smoke. Fires
can be extinguished by conventional means with water and mist preferred. In enclosed areas,
fire fighters should be provided with self contained breathing apparatus.
HDPE HCH 5110