CHAPTER 10

SECTION 10.1
Promat FENDOLITE®-MII
Cementitious fire protection spray system

General description

Promat FENDOLITE®-MII is an easy to

apply, extremely effective and durable
cementitious fireproofing spray. It is
designed specifically for steel and
concrete structures in the oil and gas
and petrochemical industry. All thin and
lightweight Promat FENDOLITE®-MII
solutions are fully weatherproof, can
withstand thermal shocks and will not
crack or spall under impact.

MATERIAL PROPERTIES Promat FENDOLITE®-MII offers a reliable

protection during and even after a fire,
Colour and finish Off-white, monolithic, spray texture
blast or explosion. It creates an efficient
Alkalinity 12.0 - 12.5 pH barrier that will last up to 240 minutes in
Sound absorption 0.35 Noise reduction coefficient (NRC) the event of hydrocarbon pool fire and up
to 120 minutes in the event of a jet fire.
Cure By hydrolic set

Initial set 2 to 6 hours at 20°C (68°F) and 50% RH Our global team of experts can offer you
dedicated technical and commercial
Minimal practicial 8mm (5/16”) unreinforced, 15mm (5/8”)
thickness Reinforced support at each stage of your project.
Theoretical coverage 62m2/tonne (15 Bd. Ft/Bag) at 25mm (1”)
thickness Promat FENDOLITE®-MII has
PHYSICAL TESTING PERFORMANCE been rigorously tested and
Physical property Test method Test results certified for a variety of fire
Density ASTM E605 775 kg/m3 (48.4pcf) ± 15% performance protocols.
Durometer ASTM D2240 40 (Shore D)
hardness USA – UL 1709 (Design No. XR719),
UL 263 and ASTM E119
Compressive ASTM E761 3778 kPa (548 psi) UK – BS 476 (Parts 20-21: 1987
strength
Appendix D) Hydrocarbon Ratings
ASTM E136
Combustibility Non-combustible International Standards ISO 834
BS476
Germany – DIN 4102
0 flame spread, 0 smoke
Surface burning ASTM E84 France – Hydrocarbon Modified
development
No cracking, delamination or
HCM
Deflection ASTM E759 Italy – UNI 11076
spalling
No cracking, delamination or UL Environmental Testing
Impact resistance ASTM E760
spalling Blast from Gas Explosion Test (more
Thermal 1.5 BTU in/hr ft2 (0.216 W/mK) than 3 bar overpressure)
ASTM C518
conductivity at 75°F (24°C) ISO 22899-1: 2007 – Resistance to
Corrosion Does not promote corrosion Jet Fires
ASTM E937
resistance of steel ISO 22899-1: 2007 – Resistance to
Fungal resistance ASTM G21 0 Rating - No fungus growth Jet Fires Following Gas Explosion
 Promat FENDOLITE®-MII

Promat has tested Promat FENDOLITE®-MII according Application

to a wide range of standards and regulations, such as
Initial steps
UL1709, UL2431, EN 13381-4, ISO 22899-1 and ISO
20088-1. Application of Promat FENDOLITE®-MII must be carried
out by an applicator recognized by Promat and applied
in accordance with the installation guides available from
The Promat FENDOLITE®-MII system is assessed
Promat.
and certified by the following institutes and notified
bodies for the performance of blast, cryogenic and fire Methods
resistance with ISO, hydrocarbon and RWS fire curves:
Mix Promat FENDOLITE®-MII with potable water in a
UL, Lloyds, Efectis, Warrington suitable mixer and apply using equipment approved
by Promat. Promat FENDOLITE®-MII may also be float
Fully waterproof or roller finished or left. A hand applied patching mix is
Thin and lightweight available for minor repairs.
Resistant to thermal shock
Does not crack or spall under impact Limitations
Maintains its integrity during and after a fire, Promat FENDOLITE®-MII may be applied when the
blast or explosion substrate and air temperatures is at least 2°C (36ºF)
Service life exceeding 30 years and rising, but should not be applied if the substrate
Applied by Promat licensed installers or air temperatures is less than 4ºC (39ºF) and falling.
Maximum substrate and air temperature should not
Expert technical and commercial advice
exceed 50ºC (122ºF). Substrate should be at least 2°C
(36ºF) above dew point temperature.
The application areas of Promat
FENDOLITE®-MII Top coating
Refineries and petrochemical facilities Under certain circumstances Promat TOPCOAT® 200
Steel and concrete structures and/or other nominated top coatings may be used as
Spheres, tanks and barrels protection from frequent wash down, long term chemical
Vessels and vessel skirts spills, or for improved resistance to fungal, algal and
bacterial growth.
Preparation
Typical substrate Packaging
Concrete and steel 20 kg bags.

Substrate preparation
Storage
The substrate must be clean, dry and free from visible
moisture (including condensation), concrete laitance, Off the ground and kept dry until ready for use.
formwork release oils, loose millscale, loose rust
and any other condition preventing good adhesion.
Concrete curing agents should not be used.
Shelf life
Max. 18 months.
Mesh reinforcement
Most fire tests conducted have been carried out
without mesh reinforcement, to demonstrate the
ability of Promat FENDOLITE®-MII to stay in place
under the most severe fire conditions. However, for
maximum long-term service durability, the use of mesh
is recommended. The use of mesh is mandatory where
resistance to gas explosion is required.

All specified technical data are mean values from the production which are subject to the usual fluctuations and do not represent guaranteed properties in the sense of a guarantee. All
information corresponds to the current state of the art and has been presented and described to the best of our knowledge. Changes due to new findings are possible, errors and misprints are
not excluded. With regard to any liability, our delivery and payment terms apply exclusively. Request safety datasheet. With the publication of this edition, all previously published datasheets
are invalid. © Copyright Etex NV, Brussels, Belgium. All rights reserved. 2021-05
Etex Industry c/o Microtherm N.V., Industriepark-Noord 1, 9100 Sint-Niklaas, Belgium | T +32 (0)3 760 19 80 | F +32 (0)3 760 19 99
[email protected] | www.promat.com/industry

1
SECTION 10.2
 KÖCO PT DIN EN ISO 13918




Gewindebolzen mit Flansch und Zündspitze

Threaded stud with flange and ignition tip



Goujon fileté avec collerette et pointe



d’amorçage
Espárrago roscado con collarín y punta de 


cebado 


d1 l1 d2 d4 l3 max. h1 Artikel-Nr. 1 Masse Bolzenhalter

h2 Part-no. Mass Chuck
No. d’article Poids Mandrin
Nº de artículo Peso Porta espárrago
kg/100
M3 6 4,5 0,6 0,55 0,6 100-0001-103 0,031
8 100-0003-103 0,039
10 100-0005-103 0,047
351-7003-000
12 100-0006-103 0,056
16 100-0008-103 0,072
20 100-0009-103 0,089
M4 8 5,5 0,65 0,6 100-0032-103 0,067
10 100-0033-103 0,082
12 100-0034-103 0,097 351-7004-000
16 100-0036-103 0,127
20 100-0038-103 0,156
25 100-0039-103 0,193
0,7 – 1,4
M5 10 6,5 0,75 0,8 1 100-0067-103 0,130
12 100-0068-103 0,153
16 100-0071-103 0,201
351-7005-000
20 100-0072-103 0,248
25 100-0073-103 0,307
mit/with/avec/con
30 100-0074-103 0,366
M6 10 7,5 1 100-0101-103 0,186
12 100-0103-103 0,220
44 Bauregelliste (DIBt)
16 100-0105-103 0,287
351-7006-000
20 100-0106-103 0,355
25 100-0108-103 0,439
30 100-0109-103 0,523
M8 12 9 0,85 1,5 100-0136-103 0,387
16 100-0138-103 0,509
20 0,8 – 1,4 100-0139-103 0,632 351-7008-000
25 100-0140-103 0,789
30 100-0142-103 0,938

l2≈ l1 - 0,3 mm

1
Artikel-Nr. gilt für Werkstoff 4.8 ver-
kupfert, andere Ausführungen siehe
Tabelle Seite 7.
1
Part-no. applies to steel, grade 4.8,
uncoated, other types see chart
page 8.
1
No. d’article valable pour acier, ca-
tégorie 4.8, sans revêtement, autres
types voir tableau page 9.
1
El Nº de artículo es válido para acero,
resistencia 4.8, brillante. Otras com-
posiciones ver Tabla página 10.
SECTION 10.3
 Technical Submittal: PLASTERING ACCESSORIES

Part 1. GENERAL

1. DESCRIPTION
Plastering accessories composed of beads and expanded metal lath used to reinforce the plaster and
preventing it from cracking.

2. REFERENCE STANDARDS

MATERIAL COATING PRODUCT SPECIFICATIONS

PRE-GALVANIZED: BEADS:
BS EN 10346 (replaced BS EN 10327) BS EN 13658-1&2 (replaced BS 6452-1)
ASTM A 653 ASTM C 1063
STAINLESS STEEL: QCS 2014 (QATAR CONSTRUCTION SPECIFICATION)
BS EN 10088 – sheets, strips, coils LATH:
ASTM A 240 – sheets, strips, coils BS EN 13658-1&2 (replaced BS 1369-1)
ASTM C 1063
ASTM C 847
QCS 2014 (QATAR CONSTRUCTION SPECIFICATION)

3. DELIVERY, HANDLING AND STORAGE

A. Delivery – Materials are to be delivered in original packages, containers or bundles containing the
manufacturers or suppliers identification.
B. Transportation – In transportation or lifting, handle products with care avoiding excessive stress and
preventing damages.
C. Storage – Store materials with cover and keep them dry and protected against damage due to
weather condition, corrosion and surface contamination.

Part II. PRODUCTS

2.1 MANUFACTURER AND SUPPLIER

Expanded Metal Manufacturing
Zone 81, St. 15, Plot 15, New Industrial Area
Doha, Qatar
Email: [email protected]
Website: www.exmetco.com

MATERIAL
A. BEAD
1. ANGLE BEAD

Angle Bead – used for reinforcement and protection of plaster from cracking especially
where a true straight outside corners are required in a building.

Type Code Wings (mm) Length (m) Material

AB – 48 gs / ss 48 x 48 2.7 – 2.9 galvanized steel / stainless steel
AB – 52 gs / ss 52 x 52 2.7 – 2.9 galvanized steel / stainless steel
AB – 63 gs / ss 63 x 63 2.7 – 2.9 galvanized steel / stainless steel
AB – 70 gs / ss 70 x 70 2.7 – 2.9 galvanized steel / stainless steel

Expanded Metal Manufacturing Co.

Zone 81, St. 15, Plot 15, New Industrial Area
Tel: +974 44603826 Fax No. +974 44601724
[email protected] / www.exmetco.com Page 1 of 4
 Technical Submittal: PLASTERING ACCESSORIES

6. CONTROL JOINT BEAD

Control Joint Bead – used for normal plastering to divide between different wall
segments or to make a joint for plastering areas where the works needs to be done
on several stages.

Depth Groove Length

Type Code Material
(mm) Width (mm) (m)
CJ – 10 gs / ss 13 10 3.0 galvanized steel / stainless steel
CJ – 15 gs / ss 13 15 3.0 galvanized steel / stainless steel

B. EXPANDED METAL LATH

1. CORNER MESH
Corner Mesh – used for reinforcement of plaster for inside corners to prevent
cracks and give corner a straight finish
Wings
Type Code Length (m) Material
(mm)
CM50 gs / ss 50 x 50 2.7 / 2.44 galvanized steel / stainless steel
CM75 gs / ss 75 x 75 2.7 / 2.44 galvanized steel / stainless steel
CM100 gs / ss 100 x 100 2.7 / 2.44 galvanized steel / stainless steel

2. STRIP / COIL MESH

Strip / Coil Mesh – used as background for plastering in walls and suspended
ceiling
Type Code Width (mm) Weight (kg / m²) Length (m)
SCM 4” 100 0.6 25 or 50 (coils)
SCM 6” 150 0.6 25 or 50 (coils)
SCM 7” 175 0.6 25 or 50 (coils)
SCM 8” 200 0.6 25 or 50 (coils)

3. DIAMOND METAL LATH SHEETS

Diamond Metal Lath Sheets – used as background for plastering in walls and
suspended ceiling

Weight Sheet Size

Type Code Material
(kg/m²) (cm)
ML –A 0.62 244 x 60 galvanized steel / stainless steel
ML – B 0.82 244 x 60 galvanized steel / stainless steel
Width 6”
ML – C 0.92 244 x 122 galvanized steel / stainless steel
7”
ML – D 1.05 244 x 60 galvanized steel / stainless steel
8”
ML – E 1.22 244 x 60 galvanized steel / stainless steel
10”
ML – F 1.62 244 x 60 galvanized steel / stainless steel
12”
ML – G** 1.92 244 x 60 galvanized steel / stainless steel
ML – H 1.82 244 x 60 galvanized steel / stainless steel

Expanded Metal Manufacturing Co.

Zone 81, St. 15, Plot 15, New Industrial Area
Tel: +974 44603826 Fax No. +974 44601724
[email protected] / www.exmetco.com Page 3 of 4
SECTION 10.4
Product Datasheet

GT Acryl PC60

One component elastomeric acrylic waterproofing coating

Description Additional Information

A single component coating based on high solids acrylic COVERAGE RATE* PACK SIZE SHELF LIFE

resin for waterproofing and protective coating

applications. The cured coating provides an excellent
barrier against water, chloride ions and corrosive
atmospheric gases into the coated substrate.

Uses 1.2 litre/sqm/coat 5 ltrs & 20 12 months from

(2 coats litres plastic date of
 Waterproofing coating on exposed and covered recommended) pail manufacture if
stored in shaded
roof slabs, domes, slanting roofs etc.,
and dry area.
 UV resistant flexible waterproofing and protective *Coverage rate mentioned above are theoretical and may
coating over metal roofing sheets, bitumen vary depending on the substrate condition.
membranes and coatings.
 Waterproofing and weatherproof coating on brick Properties
masonry, blockwork, cement and clay tiles.
 Protective coating over spray applied polyurethane Form Liquid
foam. Colours Grey, White
 Protective coating to structures exposed to marine Density 1.20 + 0.05
environment. Solid Content Min. 60%
Elongation (ASTM D638) 400%
Features & Benefits Application Temperature 5 to 45 deg C
Service Temperature 0‐90 deg C
 Excellent resistant to UV and long term weathering Solar Reflectance (white) Excellent
effects. UV Resistance Excellent
Toxicity Non toxic
 Flexible coating capable of bridging minor
Chemical Resistance Petrol, diesel, mild
substrate cracks.
acids and alkalis.
 Strong adhesion to cementitious and metal
substrates.
 Suitable for indoor and outdoor use including
exposed applications
 Excellent resistance against water, chloride ions
and atmospheric gases.
 Available in grey and white colours.

www.asas-ccf.com
GT / TDS/ 19/ - Rev.0
1
PAGE
Product Datasheet

GT Acryl PC60

One component elastomeric acrylic waterproofing coating

Application Methodology Application

Surface Preparation Mixed GT Acryl PC60 shall be applied using brush,

roller or airless spray machine over the primed
Surface must be prepared by grinding, wire brushing substrate. Minimum two coats are recommended.
followed by cleaning with air blower or compressed air to The second coat must be applied after the first coat
remove loose materials, mortar splashes and other is fully dry and in right angle to the first coat.
contaminants. Substrate damages such as cracks, pin holes
and honeycombs must be repaired using suitable GT Crete GT Acryl PC60 coating shall be reinforced using a
cementitious repair mortar. Wash the surface with clean open weave glass fibre mesh of minimum 50gsm or
water prior to applying the coating. geotextile membrane of 100 gsm placed between the
first and second coat, whilst the first coat is wet. Use
Metal and PU foam surfaces must be cleaned well to of glass fibre mesh is recommended on substrate
remove loose particles, paint splashes etc., with cracks, coating transition at upstands and
around penetrations such as pipes, ducts etc., Glass
Priming fibre width shall be minimum 200mm and the overlap
must be 50mm.
Primer coat is recommended on highly porous substrate
and vertical surface to seal pores and stabilize the For Roof Waterproofing applications : Apply GT Acryl
substrate. Application of primer must be carried out PC60 at 1.2 ltr/sqm/coat. Minimum 2 coats
preferably on a damp substrate. Dilute GT Acryl PC60 recommended.
coated with equal part of clean water by volume (1 part GT
Acryl PC60 : 1 part of water by volume). The coverage rate For Protection applications : Apply GT Acryl PC60 at
of primer shall be 5 sqm/litre/coat. Allow the primer to 0.85 ltrs/sqm/coat. Minimum 2 coats recommended
become completely dry prior to application of top coat. to achieve dry film thickness of 1mm. Application
This will take approx.. 6‐12 hours depending on ambient include as protective coating over blockwork, plaster
temperature and porosity of substrate. and PU foam surfaces.

Mixing Allow the applied coating to dry for 24 hours prior to

exposing to subsequent activities.
Mixing of GT Acryl PC60 must be carried out after opening
the pail using a slow speed drilling machine fitted with Clean the applications tools using water. Dried
paddle. This will ensure an even consistency material material shall be removed mechanically.
without any lumps or sediments. Mix for 3‐5 minutes to
get a uniform consistency mix.

www.asas-ccf.com
GT / TDS/ 19/ - Rev.0
2
PAGE
Product Datasheet

GT Acryl PC60

One component elastomeric acrylic waterproofing coating

Application Restrictions General Terms & Conditions

 Do not apply when rain is imminent within 24 Users must always refer to the most recent data
hours of application. sheet. Upon request, additional copies will be
 Check compatibility and adhesion prior to provided. This technical data sheet is given in good
application over existing paint. faith and does not guarantee the optimum utility of
 Do not apply on very dry and hot surface. This may the product always. The information contained
affect coating performance. herein is believed to be reliable to the best of our
knowledge. ASAS is exempted from all legal liability in
case of injury incurred from product handing without
appropriate technical precautions. ASAS reserves the
Health & Safety right to change the product specifications or
properties. All orders are considered based on
current delivery and sale infrastructures.
GT Acryl PC60 is nontoxic. However, it should not
come in contact with eyes or to be swallowed.
The contents of this document are pertaining to the
Always ensure adequate ventilation and avoid
application and usage of Gulftight products, are given
inhalation of vapours. The applicator should wear
based on the technical expertise of capable personnel
appropriate clothes, gloves and goggles. Use of
concerning the product. The handling and storage of
barrier cream is recommended to provide
the item has been kept under supervision,
additional skin protection. If comes in contact with
observation and extensive research has been
eyes, flush with plenty of fresh water and seek
conducted to ensure its efficiency under normal
medical advice.
conditions
Consult ASAS Technical Department prior to using
the product beyond the purview stated in this
product datasheet.

Disposal of GT ACRYL PC60 blended waste material

and spillages must be strictly carried out as per
local environmental regulations.

Refer Material Safety Data Sheet or consult ASAS

technical department for further details.

www.asas-ccf.com
GT / TDS/ 19/ - Rev.0
3
PAGE
Product Datasheet

GT Acryl PC60

One component elastomeric acrylic waterproofing coating

www.asas-ccf.com
GT / TDS/ 19/ - Rev.0
4
PAGE