M24X70 GR8.8 HDG

Bolt24*70

Uploaded by

mohamed.elkazazqc
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
36 views1 page

M24X70 GR8.8 HDG

Bolt24*70

Uploaded by

mohamed.elkazazqc
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
You are on page 1/ 1

NINGBO NINGLI HIGH-STRENGTH FASTERNER CO.

,LTD
ADD:XIHE,LUOTUO,ZHENHAI DISTRICT NINGBO
ZHEJIANG PROV.CHINA
TEL:0086-574-56535666 FAX:0086-574-86531668
TEST REPORT
BUYER: Alex Fasteners Co. DATE: 2023.04.10
P/I NO : 16AC0118 INVOICE NO: 16AC003
TEST DATE: 2023.04.13 LABORATORY USED:NINGLI TEST LABORATORY
SPECIFICATION:
DIN933 8.8 24*70 H.D.G. 900.000 KG
CHARCTERISTIC STANDRD RESULT ACCEPT
WIDTH ACROSS FLATS
35.40 ~ 36.0 35.44-35.48 O.K.
SAMPLE PIECES 80(s)
WIDTH ACROSS CORNERS
40.0 min 40.14 O.K.
SAMPLES PIECES 80(e)
HEIGHT OF HEAD
14.8 ~ 15.2 14.96-15.12 O.K.
SAMPLES PIECES 80(k)
HEAD SOUNDNESS NO FRACTURE OK O.K.
LENGTH(L)
69.25~70.0 69.42-69.86 O.K.
SAMPLES PIECES 80
LENGTH OF THREAD (b)
~ O.K.
SAMPLES PIECES 80
TENSILE STRENGTH
830 MPa 932 O.K.
SAMPLES PIECES 3(Rm MPa)
CORE HARDNESS
HRC 23 ~ HRC 34 30-32 O.K.
SAMPLES PIECES 8(HRC)
PROOF LOAD
600 MPa OK O.K.
SAMPLES PIECES 3(MPa)
ELONGATION
12 13.2 O.K.
SAMPLES PIECES 3(A%)
MINIMUM HEIGHT OF
1/2H1 mm OK O.K.
NON-DECARBURIZED THREAD ZON3(E)
MAXIMUM DEPTH OF
0.015 mm / O.K.
COMPLETE DECARBURIZATION3(G)
PlATION THICKNESS
min:55um 59 O.K.
SAMPLES PIECES 80
THREAD "GO"
/ / O.K.
SAMPLES PIECES 80(T)
THREAD "NOT GO"
/ / O.K.
SAMPLES PIECES 80(Z)
CHEMICAL CPMPOSITION(%) C Si Mn P S Cr Mo Ti B
0.35 ~ 0.17 ~ 0.60 ~ 0.030 0.035
38K 0.40 0.37 0.90 max max

0.36 0.18 0.77 0.011 0.006


CONCLUSION:
THIS IS TO CONFIRM THAT THE GOODS WERE TESTED IN THE PRESENCE OF THE
INSPECTOR AND FOUND TO BE IN CONFORMITY WITH DIN933 STANDARD.