Requirement as per Test Method

S. No Test JSS SPECIFICATION NO Test Result

JSS:8405-25:2010
Revision No.1
A. Body Material
1. Weight 220 gm 223 IS:1964:1970
2. Composition Cloth plain weave polyester: Cotton 67:33 IS :667
blend 67:33 Disruptive
3. Thread Density IS 1963:1981 (RA
-End /dm 290+/- 5% 292.70 2018)
-Picks/dm 220+/- 5% 219.20
4. Breaking Strength IS 1969 (Part 1 )
-Warp 1100 Min 1221.20 2018 (RA 2023)
-Weft 800 Min 902.50 (05cm X 20 Cm )
(Ravelled Strip
Method)
5. Ph Value of Aqueous 6.0 To 8.5 No 7.5 IS 1390:2022
Extract
-Avg
6. Dimensional Change Due
to Relaxation IS 2977:1989
- -Warp 1 Max % (-)0.4 (RA2020)
- -Weft 1 Max % (-)0.4
7. Color Fastness to Washing
-Change In Color
Black 4 Or Better Grade 4.50 IS/ISO 105
Green 4 Or Better Grade 4.50 C10:2016/
Khaki 4 Or Better Grade 4.50 (superseding IS
Brown 4 Or Better Grade 4.50 764:1979)
Staining on Polyester 4 Or Better Grade 4.50
Staining on Cotton 4 Or Better Grade 4.50
7. Color Fastness to
Crocking/Rubbing

Black 3 Or Better Grade Dry Wet IS/ISO 105 X 12

Green 3 Or Better Grade 4.50 4.50 C10:2016/
Khaki 3 Or Better Grade 4.50 4.50 (superseding IS 766)
Brown 3 Or Better Grade 4.50 4.50
4.50 4.50
8. Color Fastness to
Perspiration Acidic Alkaline

Black 4 Or Better Grade 4.50 4.50 IS/ISO105 E04:2013

Green 4 Or Better Grade 4.50 4.50 (SUPERSEDING IS
Khaki 4 Or Better Grade 4.50 4.50 971)
Brown 4 Or Better Grade 4.50 4.50
Staining on Wool 4 Or Better Grade 4.50 4.50
Staining on Acrylic 4 Or Better Grade 4.50 4.50
Staining on Polyester 4 Or Better Grade 4.50 4.50
Staining on Nylon 4 Or Better Grade 4.50 4.50
Staining on Cotton 4 Or Better Grade 4.50 4.50
Staining on Acetate 4 Or Better Grade 4.50 4.50

7. Color Fastness to Light

IS/ISO 105-
Black 5 Or Better Grade 5 B02:2014(RA 2022 )
Green 5 Or Better Grade 5 Exposure Cycle
Khaki 5 Or Better Grade 5 A1(superseding IS
Brown 5 Or Better Grade 5 2454:1985 )

8. Water Repellency 80 or Above 90 IS:390

1. Spraying
B. Cloth Calico Cotton 91 cm Khaki
1 End/ dm 268±5% 270 IS:1963:1969
2 Picks/ dm 220±5% 221
Weight per m2 120+5% IS:1964:1970
3 122
(gm/m2) -2.5%
4 Color Fastness to 4 or better Rating 4 IS:765:1966
Washing
5 Breaking Load in kg on 5.0cmX 20 cm strain 0IS 1969:1968
A Warp 36.0 37.3
B Weft 22.0 22.3

6 Weave Plain Plain Visual

7 Scouring Loss % 2.0 Max 1.13 IS:1983:1960
8 pH value 6.0—8.5 6.56 IS:1390:1961
 TEST REPORT

Requirement as per Test Method

S. No Test JSS SPECIFICATION NO Test Result
JSS:8405-25:2010
B. Cloth Calico Cotton 91 cm Khaki
1 End/ dm 268±5% 270 IS:1963:1969
2 Picks/ dm 220±5% 221
2
Weight per m 120+5% IS:1964:1970
3 122
(gm/m )2
-2.5%
4 Color Fastness to Washing 4 or better Rating 4 IS:765:1966

5 Color Fastness to Light 4 or better Rating 4 IS:2454:1967

6 Scouring Loss % Max 2 2 IS:1383:1960

7 Ph Value Cold Method 6.0 to 8.5 7.70 IS:1390:1961

8 Shrinkage or Elongation 2 Max 2 IS:2977:1964

%
5 Breaking Load in kg on 5.0cmX 20 cm strain IS 1969:1968
A Warp 36.0 37.3
B Weft 22.0 22.3
6 Weave Plain Plain Visual
7 Scouring Loss % 2.0 Max 1.13 IS:1983:1960
8 pH value 6.0—8.5 6.56 IS:1390:1961
 TEST REPORT

S. No. Test Parameters Requirement as per Result Test

JSS:8405-25:2010 Method
Revision No.1
CLOTH CALICO COTTON 91 CM KHAKI
(A)
1 Count of Yarn
a Warp 23 tex 24tex IS:3442
b Weft 23 tex 23 tex
2 Color Fastness to Light 4 or better Rating 4 IS 2454
SPUN POLYESTER THREAD OF VARIETY NO 5 ( NM 70/3) 145 D TEX X 3
(B)
1. Color fastness to light 4 or better Rating 4 IS:2454-1967
2. Color fastness to washing
A For light shade 3 or better Rating 3 IS:764-1979
b For medium and heavy shade 3 or better Rating 3
3. Count of Yarn 145d tex X3 145d tex X3
(C) CAP, FS DISRUPTIVE SIZE 6 JSS:8405-25:2010
1 Stitching Lock stitch with 4 to 5 stitches Lock stitch with 4 to Visual
per cm 5 stitches per cm
2 Ventilation Holes One Ventilation hole of 4 mm One Ventilation hole Visual
Dia finished with Buttonhole of 4 mm Dia
stitching finished with
Buttonhole stitching
3 Size 6.0 6.0 Measurement
4 Internal Circumference 600±5 mm 603 Method
5 Length of panel 170±5 mm 172
6 Circumference of Peak(a)-outer 360±3 mm 361
7 Circumference of Peak(a)-Inner 220±2 mm 221
8 Length of Forehead piece 220 mm 220
9 Width of Forehead Piece at 80 mm 81
Center
10 Distance of Ventilation of Hole 60 MM 60
 TEST REPORT
S.No. Test Parameters Requirement as per Result Test Method
JSS:8405-25:2010
Revision No.1
(E) LOW DENSITY POLYETHYLENE SHEET
1 Material Low Density virgin Low Density Schedule No .1
polyethylene virgin Tex-1/1299/82/1
polyethylene Appendix B
1a Peak Material Piece of LDPE sheet Piece of LDPE Visual
encased in casing of sheet encased
body material in casing of
body material
2. Density Apparent (g/ml) 0.95 0.95

3 Tensile Strength 830 min 832

( Newton/cm2)

4 Elongation At Break 125 Min % 139

5 Thickness (Under 200 g/cm2 Load, 1.7+/-0.1 1.7

mm)

6 Mass (kg/m2) 1.6+/-0.1 1.5

7 Workman ship and finish The LDPE sheet shall be Complies

made from virgin material and
shall bw free from the holes
embedded matters, surface
imperfections. Cuts and other
defects
 TEST REPORT

S.No. Test Parameters Requirement as per Result Test Method

JSS:8405-25:2010
Revision No.1
(F) HDPE WOVEN FABRIC
1 Material Virgin color HDPE Virgin color Schedule No .1
monofilament of HDPE Tex-1/1299/82/1
suitable Tenacity. monofilament Appendix c
of suitable
Tenacity.
1(b) Forehead Piece material layers of HDPE woven layers of HDPE Visual
fabric covered on one woven fabric
side with a layer of covered on one
Calico Cotton Khaki side with a layer
of Calico Cotton
Khaki
2. Filament Diameter(mm) 0.30+/-0.3 0.31

3 Mass(g/m2) 180+/-10 189

4 Thickness of Fabric (mm) under 0.80+/- 0.05 0.81

200g/cm2 Load

5 Average Number of Filament (end 24+/-2 25

& picks ) per 2.5 Cm

6 Breaking load of single Filament 9.8 minimum 10.2

(20 cm between grips) (Newton)

2 Workman ship and finish The HDPE woven fabric shall Complies
be woven from HDPE
monofilament of suitable
tenacity and diameter . The
Fabric shall be reasonably
free from all the
manufacturing /weaving
defects such as uneven
surface cuts and other visual
defects.
 TEST REPORT

S.No. Test Parameters Requirement as per Result Test Method

JSS:8405-25:2010
Revision No.1
(G) FLEXIBLE POLYURETHANE FROAM SHEET
1 Material Flexible Polyurethane Flexible Schedule No .1
foam Polyester or Polyurethane Tex-1/1299/82/1
polyether type of foam Polyester or Appendix D
open or inter polyether type of
open or inter
connecting cells
connecting cells
1a 2mm Strip of Visual
Cushioning Lining Material 2mm Strip of Polyurethane foam Polyurethane
foam
2. Thickness(mm) 2+/-0.02 2 As Per IS 7883

3 Density Apparent (kg/m2) 180+/-10 189 As Per IS 7883

4 Tensile Strength (Newton/cm2) 9.8 minimum 10.2 As Per IS 7883

5 Elongation (%) 300+/-30 306 As Per IS 7883

6 Compression Set (%) 20(max) 19.8 As Per IS 7883

2 Workman ship and finish The Polyurethane flexible foam Complies

sheet shall be of polyester type
which is defined as expended
cellular product produced by
inter action of polyhydroxy
compounds water and
iseocyanate .The foam shall
consists of cell of uniform
characteristics which shall be
essentially open and inter
connecting type .
The polyurethane foam sheet
shall be uniform in thickness and
shall be free from defects such as
holes stain cuts etc.
 S.No Test Parameters REQUIREMENT AS PER Test Results Test Method
. PER U-11-98
(spec)/2022-2023-prov-
(Dis/Pattern)-14
Dated 04-07-2023 vide
Issued Letter Dated 01-09-
2023
4 (1) COLOUR
(a) Colour BROWN BROWN CCM
(b) System CIELCH CIELCH Macbeth 3100CIE LCH
(c) Illuminant observer D 65 D 65 (CMC 2:1) AATCC
(d) Standard observer 10 degree 10 degree TEST METHOD
(e) Tristimulus values 173:2009 & AATCC
X 9.306 9.859 EVALUATION
9.309 9.777 PROCEDUR E 7:2009
Y
Z 6.422 6.559
(f) LCH
L 36.060 37.447
C 13.122 14.208
H 61.441 70.479
(g) CMC (l:c) 2:1 2:1
(h) Colour difference ≤ 3.0 2.18
S.N Test Parameters REQUIREMENT AS PER Test Results Test Method
o. PER U-11-98
(spec)/2022-2023-prov-
(Dis/Pattern)-14
Dated 04-07-2023 vide
Issued Letter Dated 01-09-
2023
5 COLOUR
(a) Colour GREEN GREEN CCM
(b) System CIELCH CIELCH Macbeth 3100
(c) Illuminant observer D 65 D 65 CIE LCH (CMC
(d) Standard observer 10 degree 10 degree
2:1) AATCC
(e) Tristimulus values TEST METHOD
X 4.860 4.868 173:2009 &
Y 5.563 5.568 AATCC
Z 4.540 4.548 EVALUATION
(f) LCH PROCEDUR E
L 28.283 28.287 7:2009
C 8.400 8.409
H 127.577 127.579
(g) CMC (IiC) 2:1 2:1
(h) Colour difference ≤ 3.0 2.09
6 COLOUR
(a) Colour KHAKI KHAKI CCM Macbeth
(b) System CIELCH CIELCH 3100 CIE LCH
(c) Illuminant observer D 65 D 65 (CMC 2:1)
(d) Standard observer 10 degree 10 degree
AATCC TEST
(e) Tristimulus values METHOD
X 30.582 30.589 173:2009 &
Y 30.673 30.678 AATCC
Z 24.273 24.278 EVALUATION
(f) LCH PROCEDURE
L 62.231 62.238 7:2009
C 14.229 14.229
H 66.174 66.178
(g) CMC (l:c) 2:1 2:1
(h) Colour difference ≤ 3.0 2.10
S.N Test Parameters (REQUIREMENT AS PER PER Test Results Test Method
o. U-11-98 (spec)/2022-2023-prov-
(Dis/Pattern)-14
Dated 04-07-2023 vide
Issued Letter Dated 01-09-2023
5 COLOUR
(a) Colour BLACK BLACK CCM
(b) System CIELCH CIELCH Macbeth 3100
(c) Illuminant observer D 65 D 65 CIE LCH (CMC
(d) Standard observer 10 degree 10 degree
2:1) AATCC
(e) Tristimulus values TEST METHOD
X 3.041 3.049 173:2009 &
Y 3.178 3.179 AATCC
Z 3.151 3.159 EVALUATION
(f) LCH PROCEDUR E
L 20.744 20.746 7:2009
C 1.649 1.648
H 88.991 88.998
(g) CMC (IiC) 2:1 2:1
(h) Colour difference ≤ 3.0 2.19

Remarks : The above tested parameters meet the requirement as per QRs Specification