Union S 1 CrMo 5 - UV 420 TT
SAW wire/flux combination, low-alloyed, creep resistant
Classifications
EN ISO 24598-B AWS A5.23 / SFA-5.23
S 49 2 FB SU 5CM F7P0-EB6-B6
Characteristics and typical fields of application
Union S 1 CrMo 5 - UV 420 TT is a wire flux combination for submerged arc welding creep resistant steel grades with 5% Cr and
0,5% Mo. The weld deposit exhibits good mechanical properties. Easy slag detachability and smooth bead surface are additional quality
features.
UV 420 TT is an agglomerated fluoride-basic flux with high basicity and neutral metallurgical behaviour. For information regarding this
welding flux see our detailed data sheet.
Base materials
Creep resistant and steels resistant to hydrogen such as 12CrMo19-5 and similar steels (type 6% Cr 0,5% Mo).
1.7362 – X12CrMo5
ASTM A 182 Gr. F5; A 193 Gr. B5; A 213 Gr. T5; A217 Gr. C5; A 234 Gr. WP5; A 314 Gr. 501; A335 Gr. P5 u. P5c; A 369 Gr. FB 5; A 387 Gr.
5; A 426 Gr. CP5
Typical analysis
wt.-% C Si Mn Cr Mo
wire 0.08 0.3 0.5 5.8 0.6
all-weld metal 0.06 0.5 0.7 5.4 0.6
Mechanical properties of all-weld metal - typical values (min. values)
Condition Yield strength Rp0.2 Tensile strength Rm Elongation A (L0=5d0) Impact energy ISO-V KV J
MPa MPa % -25°C 0°C
a1, DC+ 430 (≥400) 570 (≥520) 28 (≥ 22) 190 (≥ 27) 210 (≥ 47)
a1 = 1 hour 745 °C
Operating data
Polarity DC + Dimension mm
2.5
3.0
4.0
Preheating and interpass temperature 200 – 250ºC. The recommended PWHT weld heat treatment is annealing at 740ºC/min. 2 hrs.
Approvals
-
All information provided is based upon careful investigation and intensive research. 1 / 1 02/2021