material specifications

Dec 2011 METAL

MECHANICAL PROPERTIES OF TEST BARS Mild Steel
Temper F1
Tensile Strength 190 MPa min. Type Flat bars and Sections
Elongation on 50mm 7% min. Standard AS 3679.1
Grade 300 MPa
Minimum yield stress 300 MPa (11 to 17mm
PHYSICAL PROPERTIES thickness)
Thermal conductivity at 25oC 142 W/m.k Minimum yield stress 300 MPa (11 to 17mm
Density 2.65/m3 x 103 thickness)
Average coefficient of thermal 20.8 x 10-6 per oC Minimum tensile stress 440 MPa
expansion Minimum elongation 22% (on gauge length of 5.65 SO)

Type Plate
Aluminium sheet / plate Standard AS 3678.1
Grade 300 MPa
AS/NZS 1734 "Aluminium and aluminium alloys - Flat sheet, Minimum yield stress 300 MPa (12 to 20mm thickness)
coiled sheet and plate" Minimum tensile strength 430 MPa
Alloy 5052 Minimum elongation 21% (on gauge length of 5.65 SO)
Temper H32
Ultimate tensile stress 215 MPa minimum Type Round and square bars
Yield tensile stress 160 MPa minimum Standard AS 3679.1
Elongation (3mm thick) 7% minimum (on gauge Grade 300 MPa
length of 5.65 A) Minimum yield stress 290 MPa (50 to
100mm thickness)
Minimum tensile strength 440 MPa
Aluminium Extrusion Minimum elongation 22% (on gauge length of 5.65 SO)

AS/NZS 1734 “Aluminium and alloys – Flat sheet, coiled sheet Type Tube
and plate” Standard AS 1751)
Alloy 6060 Minimum yield stress 290 MPa (50 to
Temper T5 100mm thickness)
Ultimate tensile stress 150 MPa minimum Minimum tensile strength 440 MPa
0.2% proof stress 150 MPa minimum Minimum elongation 22% (on gauge length of 5.65 SO)
Elongation (on gauge length of 5.65 SO)
Type Hollow Bar
Stainless Steel for Spinnings Standard ISO 2938
AS 1449 “Wrought alloy steels – Stainless and heat-resisting Grade 300 MPa
steel plate, sheet and strip” Minimum yield stress 290 MPa (50 to 100mm
Material 316SS thickness)
Thickness 0.9mm Minimum tensile strength 440 MPa
Finish Bright annealed Minimum elongation 22% (on gauge length of 5.65 SO)

Welding
Stainless Steel sheet/ plate
ASTM-A240/ 480 Stainless Steel tube Types Gas metal-arc welding (GMAW, or MIG)
Alloy grades T304/L, T316L Gas tungsten-arc welding (GTAW or TIG)
Tensile stress 545 MPa, 558 MPa
Standards AS/NZS 1554.1 "Structural steel welding
Yield stress 228 MPa, 290 MPa
- welding of steel structures" AS 1665
Hardness B79, B79
"Welding of aluminium structures"

1800 027 799 streetfurniture.com

PAGE 1 OF 3
 material specifications
Dec 2011 CASTINGS | FIXINGS

Castings Cast Aluminium (high pressure die casting)

AS 1874 "Aluminium and alloys - ingots and castings"
Cast Aluminium (gravity die casting)
AS 1874 "Aluminium and alloys - ingots and castings" Alloy ADC 12
CHEMICAL COMPOSTION
Silicon (Si) 9.6 - 12.0%
Alloy CA 401
Iron (Fe) 0.9%
CHEMICAL COMPOSITION
Copper (Cu) 1.5 - 3.5%
Silicon 12.0 - 13.0% Manganese (Mn) 0.5%
Iron 0.40% Magnesium (Mg) 0.3%
Copper 0.10% Chromium (Cr) 0%
Manganese 0.10% Nickel (Ni) 0.5%
Magnesium 0.05% Zinc (Zn) 1.0%
Chromium - Tin (Sn) 0.3%
Nickel 0.05% Lead (Pb) 0%
Zinc 0.10% Titanium 0%
Other elements (each) 0%
Tin -
Other elements (total) -
Lead -
Aluminium Remainder
Titanium 0.20%
Other elements (each) 0.05 Fixings
Other elements (total) 0.15
Aluminium Remainder Type Metric socket head cap screws
Threads/ standard ANSI BI, 13M, ISO 261
Cast Aluminium (sand casting) Property class / standard 12.9-ISO 898/1
AS 1874 "Aluminium and alloys - ingots and castings" Material ASTM A574M, DIN912 alloy steel
Hardness Rc 38-43
Alloy DA 601 Tensile strength 1300 MPa thru M16 size
CHEMICAL COMPOSITION Yield stress 1170 MPa thru M16 size
Silicon 6.5 - 7.5% Thread class 4g 6g
Iron 0.15%
 Corrosion protection Zinc (mechanically plated)
Copper 0.015%
Manganese 0.03% Type Metric hexagon set screws
Magnesium 0.45 - 0.7% Property / class standard 4.6-AS 111/AS 4291.1
Chromium - Material / standard 304SS – ASTM 304L, 304,
Nickel - 304LN 316SS – ASTM 316L, 316
Zinc 0.35% Tensile strength 400 MPa minimum
Tin - Yield stress 240 MPa minimum
Lead - Proof load stress 225 MPa minimum
Titanium 0.25% Finish Black Zinc plated
Other elements (each) 0.05%
Other elements (total) 0.15% Powder coating
Aluminium Remainder
Brand Dulux Powder Coating by Orica
MECHANICAL PROPERTIES OF TEST BARS Product type TGIC-free powder coating
Temper T1 Performance standards AS 3715 "Metal finishing -
Tensile strength 130 MPa minimum Thermoset powder coating for
Elongation on 50 mm 3% minimum architectural applications of
aluminium and aluminium alloys
PHYSICAL PROPERTIES Colour As per order
Thermal conductivity Pre-treatment Acid etch; water wash; yellow
at 25O C 151 W/m.K chromate conversion; water
Density 2.68 kg/m3 x 103 wash; dry
Average coefficient of dry
thermal expansion 21.4 x 103 per O C Thickness 50-80 m average (to significant
surfaces)

1800 027 799 streetfurniture.com

PAGE 2 OF 3
 material specifications
Dec 2011 HARDWOOD | WPC COMPOSITE

Wood-plastic Composite (WPC) Hardwood

Neowood is a sustainable timber composite product - Species Eucalyptus marginata

► Made from 70% recycled hardwood waste and 30% PVC; Green Density (GD) 1170 kg/m
► 100% recyclable; Air Dry Density (ADD) 820 kg/m
► No glues or epoxy used; Durability Class 2 (heartwood)
► No oils or stains needed to maintain finish; Strength group SD4
 Modulus of rupture (ADD) 112 MPa
Property Standard Result Modulus of elasticity (ADD) 13 GPa
Specific Density AS/NZS 4266.4:2004 822.37 kg/m Maximum crushing strength
Moisture Content AS/NZS 4266.3:2004 1.31% (ADD) 61 MPa
Tensile Strength AS/NZS 4266.6:2004 1.36 MPa = Impact (lzod value) J (ADD) 10
N/mm Hardness (Janka) (ADD) 8.5 kN
Modulus of
Elasticity AS/NZS 4266.5:2004 1534.7 MPa = Timber Plywood
N/mm
Nail Withdrawal AS 1649:2001 91.85 N Part type Moulded plywood
Linear thermal Standards AS 2270 Plywood and
expansion coefficient Manufacturer's test + 0.3% blockboard for interior use
Formaldehyde Thickness 12mm nominal
Release Manufacturer's test <0.5 mg/L Face veneer grade Veneer quality (Jarrah)
Softening Back veneer grade C
Temperature AS/NZS 1462.5:2002 83O C
Surface Water EARLY FIRE HAZARD INDEX
Absorption AS/NZS 4266.12:2004 2.0 g/m2 Ignitability index (0-20) 14
Fire Hazard Spread of flame index (0-10) 8
Property BCA Specification Heat evolved index (0-10) 9
C1.10 Toxicity Index 5.038- Smoke developed index (0-10) 2
safe levels*
(*considered low when compared with wood products)
Fire Retardant AS/ NZS 3837 Non
combustible*
(*self extinguishing; suitable for all major class types - 2, 3,5, 6,

8 or 9b; Cladding - group 3)
Colour fading due
to oxidisation Manufacturer's test 15-20 % then
stabilises*
(*compared to 50% colour fading with natural timber)

1800 027 799 streetfurniture.com

PAGE 3 OF 3