Scribd
Upload
60 views2 pages

Eco SZ3 EX EN

Uploaded by

chuot Cong1
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
60 views2 pages

Eco SZ3 EX EN

Uploaded by

chuot Cong1
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
You are on page 1/ 2

eco SZ3 ®

CuZn40SiP | lead-free brass according to RoHS

Material designation Material properties and typical applications


EN not standardized eco SZ3® is a material with good machinability despite being lead-free. It can th-
erefore be used as a replacement for conventional leaded free-cutting brasses if
UNS C68330
a lead content of max. 0.1 % is required.
Its mechanical properties and corrosion resistance are comparable to those of
Chemical composition* leaded brasses such as CuZn39Pb3 or CuZn40Pb2.
Cu 59.5 %
Pb max. 0.100 % The material is lead-free in accordance with RoHS and ELV.

Si 0.2 %
Hygienic approval for drinking water applications is being sought.
P 0.15 %
Zn balance
*Reference values in % by weight

Physical properties* Types of delivery


Electrical MS/m 13.2 The BU Extruded Products supplies bars, wire, sections and tubes. Please
conductivity %IACS 23 get in touch with your contact person regarding the available delivery forms,
Thermal conductivity W/(m·K) 104 dimensions and tempers.
Thermal expansion
coefficient
Fabrication properties
(0–300 °C) 10-6/K 21.7
Forming Surface treatment
Density g/cm3 8.21
Machinability 90 % Polishing mechanical good
Moduls of elasticity GPa 107
(CuZn39Pb3 = 100 %) electrolytic poor
*Reference values at room temperature Capacity for being poor excellent
Electroplating
cold worked
Capacity for being
excellent
hot worked

Corrosion resistance Joining Heat treatment


Machining brass is generally quite Resistance welding
fair Melting range 870 - 900 °C
resistant against organic substances (butt weld)
as well as neutral or alkaline Inert gas shielded arc
fair Hot working 550 - 650 °C
compounds. welding
Stress corrosion cracking should 450 - 500 °C,
Gas welding poor Soft annealing
be taken into account, especially 2-3h
in an ammoniacal atmosphere and 200 - 300 °C,
whilst under mechanical stress. Hard soldering good Thermal stress-relieving
1-3h
Dezincification in warm, acidic
waters should also be taken into Soft soldering excellent
consideration.

Product standards Trademarks


no EN standard yet

eco SZ3® I BU Extruded Products I Wieland Group


eco SZ3 ®

CuZn40SiP | lead-free brass according to RoHS

Dimensions and mechanical properties according to standards

Round rods / polygonal rods


Temper Diameter Width across flat Tensile strength Yield strength Elongation
Rm Rp0.2 A100 A11.3 A
mm mm mm mm MPa MPa % % %
from to from to min. min. max. min. min. min.
M all all as manufactured
W-R400* 6 80 5 60 400 – 360 – 15 20
W-R460* 2 40 2 35 460 240 – 4 6 10
W-R520* 2 16 2 10 520 380 – – 2 4

*factory standard, intended for standardization

03.24 I EX.ZMZ.UL/Er (MC.ED.UL)

Wieland-Werke AG I Graf-Arco-Straße 36 I 89079 Ulm I Germany


[email protected] I wieland.com
Characteristics and properties of products / materials in this document are generic and provided solely for general information purposes. Any statement regarding the suitability of products / materials for
certain types of applications is based on typical requirements and does not replace expert advice. Wieland disclaims all liability arising from any reliance on these documents.