EUROPE, MIDDLE EAST & AFRICA

Epoxy Curing Agents

Diluents | Accelerators | Adhesion
Promoters | Specialty Resins | Additives
EPOXY CURING AGENTS – PRODUCT GUIDE EMEA 2|3

CONTENT

ABOUT US
EVONIK IS ONE OF THE
WORLD LEADERS IN Product Categories 4

SPECIALTY CHEMICALS.
General Performance 6
Ambient Cure Amine Curing Agents 8
Waterborne Amine Curing Agents 16
Amine Curing Agents for Heat-Cure 18
Dicyandiamide, Catalysts & Accelerators 22

Evonik’s Crosslinkers Business Line Specialty Resins, Diluents and Modifiers 26

Adhesion Promoters for PVC Plastisols 28

offers a broad range of products and Definitions & Calculations 30

Product Index 31

competences for coatings and adhe-

sives, as well as for high-performance FOOTNOTES

1 Used with standard, undiluted liquid

elastomers and composites. Besides Bisphenol-A-epoxy, EEW 182-192.

2 phr: parts curing agent by weight per

products based on isophorone chemis- 3

100 parts by weight of epoxy resin.

Gel time or pot life in 150g mass at 25°C

try, the portfolio contains a full range

for room temperature cures.

4 Beck-Koller thin film set timer

(75 micron wet film) at 25°C phase III.

of high quality epoxy curing agents 5 Heat distortion temperature (HDT)

to ASTM D648.

and modifiers for a wide range of a) System cured at ambient

temperature for 7 days.

applications, including marine and

b) System cured 2 hours at 100°C.

6 AHEW = Equivalent Weight per active H.

protective coatings, civil engineering,

adhesives and composites.
EPOXY CURING AGENTS – PRODUCT GUIDE EMEA 4|5

PRODUCT CATEGORIES
OVERVIEW
Recommended
Category Brand names Chemical nature application fields

Modified polyamides;
Ancamide® aliphatic amido amines All major epoxy applications
Ambient Cure Amine including solvent-borne and
Curing Agents Ancamine® Modified polyamines solvent-free systems

Protective and industrial

concrete coatings
Self-leveling and mortar
floors and grouts
Waterborne Amine Curing Anquamine®, Modified amines and Steel coatings
Agents Epilink® polyamines Anti-corrosive primers

Polyamides and
Ancamide® amidoamines

Structural composites
Ancamine® Aliphatic amines and adhesives

Amine Curing Agents for Modified

Heat-Cure VESTALITE® S Cycloaliphatic Amine Epoxy SMC Components

Ancamine®, Anchor®, Modified aliphatic

Amicure®, Curezol®, amines and catalysts such Structural composites
Catalysts and Accelerators Imicure® as dicyandiamide and adhesives

Specialty Resins, Diluents Mono- and difunctional

and Modifiers Ancarez®, Epodil® glycidyl ethers All major epoxy applications

Adhesion Promoters Adhesion promoting

for PVC Plastisols Nourybond® Modified polyamides additives for PVC plastisols
EPOXY CURING AGENTS – PRODUCT GUIDE EMEA 6|7

GENERAL PERFORMANCE
WORKING EXAMPLES USED FOR ABOVE KEY

SIMPLISTIC COMPARISON:

Polyamide: Ancamide® 3030 A: Adduct-type

COMPARISON SUMMARY Amidoamine: Ancamide® 506

Cycloaliphatic-A: Ancamine® 2759

S: Solution

MB: Mannich-base type

Waterborne-S: Anquamine® 721 D: Dispersion

Waterborne-D: Anquamine® 100

Aliphatic-MB: Ancamine® 2432

Colour and Colour Stability Viscosity Pot Life Low Temperature Cure Surface Film Appearance Film Flexibility Adhesion Chemical Resistance

Acids Solvents

Excellent Low Long Good Gloss Excellent Excellent Excellent Very good

Waterborne - D Waterborne - D Waterborne - D Aliphatic-MB Waterborne - D Waterborne - S

Amidoamine Waterborne - S Polyamide Polyamide Cycloaliphatic-A Aliphatic-MB

Cycloaliphatic-A Cycloaliphatic-A Waterborne - D Waterborne - D

Waterborne - S Cycloaliphatic-A Amidoamine Amidoamine

Polyamide

Waterborne - S Waterborne - D Waterborne - S Aliphatic-MB Cycloaliphatic-A

Cycloaliphatic-A Waterborne - S

Amidoamine Cycloaliphatic-A Aliphatic-MB

Waterborne - D

Cycloaliphatic-A Aliphatic-MB Waterborne - D Waterborne - S

Aliphatic-MB

Polyamide

Aliphatic-MB Cycloaliphatic-A Polyamide

Amidoamine Waterborne - S

Polyamide Polyamide

Amidoamine Waterborne - S

Aliphatic-MB

Polyamide Aliphatic-MB Amidoamine

Amidoamine Amidoamine

Polyamide

Moderate High Short Poor Grease Fair Moderate Fair Fair

EPOXY CURING AGENTS – PRODUCT GUIDE EMEA 8|9

AMBIENT CURE AMINE

* With bisphenol-A/F diglycidylether blend, Epodil® 748 reactive diluent diluted, EEW 190-200, viscosity ca. 1,000 mPa.s

** Measured at 75 °C

CURING AGENTS
*** With bisphenol-A diglycidyl ether epoxy resin solution, EEW 500

Specific
Max Colour Viscosity Amine Value Gravity Loading 1, 2 Gel Time 3 Thin Film Set 4 Tg or Civil Metal
Curing Agent Generic Type (Gardner) (mPa.s@25°C) Solids (%) (mgKOH/g) (@25°C) AHEW 6 (PHR) (min@25°C) Time (h) HDT 5 (°C) Benefits Engineering Coatings Adhesives

• Industry standard
Ancamide® 260A Polyamide 10 35-45 Pa.s 100 330-360 0.96 110 60 200 10 - • Medium viscosity polyamide X X

• Low viscosity, long pot life curing agent that allow

latitude with regards to mixing ratios
Aliphatic • It is ideal for bonding old to new concrete, crack injection,
Ancamide® 500 Amidoamine 11 200-450 100 420-480 0.95 90 50 180 12 45 electrical encapsulation and for use in general adhesives X

• Low viscosity, with moderately fast cure

Aliphatic • Ideal for bonding old to new concrete, crack injection,
Ancamide® 503 Amidoamine 10 300-500 100 490-520 0.95 95 50 70 9 48 electrical encapsulation and for use in general adhesives X

• Very long pot life and good through cure with low
exotherm
Aliphatic • In high-solids coatings, often mixed with cyclo-aliphatic
Ancamide® 506 Amidoamine 13 200 – 500 100 410 – 440 0.93 110 55 385 23 45 curing agents X

• Good adhesion and cure under adverse conditions of high

Polyamide humidity and low temperature
Ancamide® 700B75 Adduct ≤8 4000 – 8000 75 240 0.96 170 90 200 – 250 - - • No induction time required. Product at 75% in butanol X

• Outstanding flexible/peel strength, excellent thermal

shock resistance and good electrical properties
Ancamide® 910 Polyamide 6 6000 - 118 0.99 230 110 – 125 120 8 - • Lower viscosity than conventional polyamides X X

• With liquid epoxy resin, it achieves high gloss, flexibility,

hardness, and reverse impact resistance comparable to tra-
ditional solvent-cut polyamide/solid epoxy resin systems
Polyamide • No induction required
Ancamide® 2050 Adduct 12 2000 – 5000 100 210 – 230 1.02 150 70 – 100 140 7 (70PHR) - • Non Critical Loading (70-100phr) X

Modified • Good low temperature cure

Ancamide® 2353 Polyamide 9 2800 – 3500 100 300 – 360 1.01 114 60 65 5 - • The best chemical resistance from our range of polyamides X X

• Low bloom tendency, high gloss and good low

temperature cure compared to other amidoamines
Modified • Commonly used in crack injection, primers and
Ancamide® 2386 Amidoamine 10 170 – 520 100 245 – 385 1.00 93 49 135 8 51 anti-corrosive primers X X

• A plasticizer-free curing agent

• Long pot life with excellent blush resistance
• Excellent hardness development and good resistance to
Modified aqueous reagents
Ancamide® 2426 Amidoamine 8 500 – 750 100 360 – 400 0.96 93 49 285 13 46 • Good color stability X

• A very low-viscosity, plasticizer-free amidoamine with

long pot life and good blush resistance
• Develops good adhesion to concrete and poorly prepared
substrates
Modified • Also ideal for use as a viscosity reducer or pot life
Ancamide® 2443 Amidoamine 9 30 – 100 100 510 – 560 0.97 86 45 250 11 56 extender for other systems X

• With excellent flexibility, impact resistance and low

temperature cure profile, ideal for use in high solids
industrial maintenance and marine coatings
Modified • Also suitable for use in adhesives, putties, sealants and
Ancamide® 2445 Polyamide 7 4500 – 6500 100 180 – 220 1.03 133 70 – 100 90 5 - flexible cable jointing X
EPOXY CURING AGENTS – PRODUCT GUIDE EMEA 10 | 11

Specific
Max Colour Viscosity Amine Value Gravity Loading Gel Time Thin Film Set Tg or Civil Metal
Curing Agent Generic Type (Gardner) (mPa.s@25°C) Solids (%) (mgKOH/g) (@25°C) AHEW (PHR) (min@25°C) Time (h) HDT (°C) Benefits Engineering Coatings Adhesives

• This low viscosity curing agent exhibits fast cure at

low temperatures and offers good adhesion onto damp
concrete
Modified • Ideal as a surface tolerant primer and for use in industrial/
Ancamide® 2573 Polyamide 8 1200 – 2200 100 275 – 290 1.01 115 60 80 6 - marine coatings X X

• Modified polyamide for cost effective protective coatings

Reactive and interior pipeline solvent based systems
Polyamide • This grade offers good cure speed, high corrosion/
Ancamide® 2634 Solution 7 1700 80 335 0.96 90 50 >180 7 - chemical and cathodic disbondment X

Modified Depends on Depends on • Provides long overcoatability with epoxy and polyurethanes
Ancamide® 2652 Polyamide 8 2000 80 132 0.99 250 90 – 130 solvent blend solvent blend - • Maintaining the performance properties from a polyamide X

• Low viscosity
Modified • Plasticiser-free curative that delivers polyamide
Ancamide® 2769 Polyamide 10 100 – 160 100 400 – 440 0.97 150 65 – 80 120 9 - performance X X

• Industry standard
• Well-balanced property profile
Ancamide® 3030 Polyamide 10 300 – 600** 100 370 – 410 0.96 95 50 80 – 140 10 - • Low viscosity, moderate pot life and good adhesion X X

• Long pot life version of Ancamide® 3030

Ancamide® 3130 Polyamide 10 750 – 950** 100 300 – 340 0.97 95 50 >250 - - • Medium viscosity X X

Modified Po- • Excellent adhesion to damp substrates, good corrosion

Ancamide® 3200 lyamide Adduct 10 1000 – 2000 100 250 – 290 1.01 115 60 75 – 80 - - protection, rapid property development X X

• Low viscosity amidoamine offering long pot life and high

Aliphatic temperature performance. Raw materials are included on
Ancamide® 3419 Amidoamine 10 50 – 160 100 180 – 300 0.94 140 75 500 – 550 - - the KTW positive list X X

Modified Po- • Excellent adhesion to damp substrates, good corrosion

Ancamide® 3444 lyamide Adduct 10 500 – 1500 100 280 – 330 1.03 115 60 40 – 50 - - protection, rapid property development X X

• Recommended for use in marine and industrial

Polyamide maintenance coatings, the product requires no induction
Ancamide® 3622 Adduct 10 4000 – 12000 70 140 – 175 0.96 340 50*** 500 – 1000 - - time and cure is unaffected by humidity up to 70% X

Modified
Cycloaliphatic • Balance of fast cure speed, high resistance to carbamation
Polyamine and waterspotting
Ancamine® 2759 Adduct 2 250 – 400 100 290 – 320 1.04 95 50 20 – 25 4 - • Also offering high chemical resistance X

Modified
Cycloaliphatic • Ambient temperature curing agent providing an excellent
Polyamine balance of properties in terms of handling, cure speed and
Ancamine® 2760 Adduct 2 300 – 600 100 235 – 275 1.02 115 60 50 – 60 7 - UV durability X X

• Flexible curative for use in adhesives, coatings and

Modified floorings
Ancamine® 3456 Polyamine 6 500 – 1500 100 160 – 190 0.97 250 125 – 135 35 8 - • Free from benzyl alcohol, alkyl phenols and bisphenol A X X

Modified
Cycloaliphatic • Good color and color stability
Amine • Produces high-gloss, non-blushing films with good
Ancamine® 1618 Adduct 2 300 – 600 100 260 – 285 1.03 115 60 40 7 46 chemical resistance X X

• Designed for use in potting, adhesives, gel-coats, small

and heavily filled castings
Modified • Offering low vapour pressure, low shrinkage and reduced
Ancamine® 1769 Adduct 4 600 – 900 100 975 1.01 48 25 24 4 53 – 99 skin irritation X X

Modified • An ultra-low-viscosity modified aliphatic amine designed

Aliphatic for use with diluted liquid epoxy resins in crack injection,
Ancamine® 2165 Amine 2 20 100 690 – 720 1.04 50 25 50 8 - concrete impregnation, and patch repair mortars X
EPOXY CURING AGENTS – PRODUCT GUIDE EMEA 12 | 13

Specific
Max Colour Viscosity Amine Value Gravity Loading Gel Time Thin Film Set Tg or Civil Metal
Curing Agent Generic Type (Gardner) (mPa.s@25°C) Solids (%) (mgKOH/g) (@25°C) AHEW (PHR) (min@25°C) Time (h) HDT (°C) Benefits Engineering Coatings Adhesives

Modified • Offers high chemical resistance similar to some aromatic

Polycycloa- systems
liphatic • Ideal for industrial chemical resistant flooring and
Ancamine® 2280 Amine 13 360 – 700 100 230 – 260 1.08 110 58 50 7 50 secondary containment X X

• An isolated adduct with low odour and low free amine

content, for use in FDA compliant coatings, tank linings
and other chemical resistant systems; offers both fast dry
speeds and good chemical resistance
Isolated • Due to its high viscosity this curing agent is commonly
Ancamine® 2410 Adduct 3 20500 100 444 – 480 1.17 85.5 45 - - - used as a co-curative or in its solvented form X

• A high functional phenol free aliphatic amine imparting good

working time with multi-functional / novolac epoxy resins
• Provide high chemical resistance against most aggressive
reagents making it ideal for tank linings and secondary
containment
Modified • This product requires plasticisation or heat cure to achieve
Ancamine® 2422 Amine 3 2000 – 2500 100 665 – 690 1.12 49 26 - - - full properties X

• Outstanding resistance to a wide range of chemicals

Modified • A fast-curing amine with good working life
Aliphatic • Rapid development of properties at low temperature
Ancamine® 2432 Amine 4 200 – 400 100 350 – 380 1.10 88 46 27 2 55 • Phenol-free and low viscosity X X

• A low viscosity curing agent which exhibits good carbam-

Modified ation resistance at temperatures down to 10˚C
Cycloaliphatic • It can be used to formulate high solids coatings, self leve-
Ancamine® 2519 Amine Adduct 2 100 – 300 100 300 – 330 1.01 95 50 23 4 45 ling and screed floors with good all round performance X X

• Low viscosity Mannich base curing agent that is moisture

tolerant
Ancamine® 2609W Mannich Base 5 300 – 600 100 360 – 420 1.01 75 40 15 2 - • Suitable for potable water and food contact coatings X X

Modified
Polycycloa- • Provides good low temperature reactivity, low viscosity
liphatic and high acid resistance, making it the ideal choice for
Ancamine® 2672 Amine 5 100 – 300 100 280 – 340 1.06 95 50 30 5 48 chemically resistant primers, mortar floors and tank linings X X

Modified
Polycycloa- • Ideally used in cost-effective primers and grouts
liphatic • The product delivers high mechanical build, rapid cure
Ancamine® 2686 Amine 12 100 – 400 100 300 – 350 1.02 95 50 30-35 4 45 and is suitable for lower temperature use X

Modified
Polycycloa- • Balance of high mechanical build, rapid cure and lower
liphatic temperature use
Ancamine® 2692 Amine 4 100 – 400 100 300 – 350 1.02 95 50 35 4 50 • Positioned for primer and non-colour sensitive coatings X

• Balance of fast cure speed, high resistance to carbamation

and waterspotting, while also offering high mechanical
Modified and low emissions properties
Ancamine® 2712M Polyamine 7 350 – 650 100 500 – 560 1.00 95 50 * 30 – 35* 7* - • Can be used for anti-corrosion primers X X

• Nonyl- and p-tert-butyl phenol free aliphatic polyamine

Mannich base curing agent
Ancamine® 2719 Mannich Base 14 300 – 500 100 340 – 380 1.03 75 40 20 3 - • Suitable for potable water and food contact coatings X X

Modified Cy- • The product offers an excellent balance of properties for

cloaliphatic Po- use in protective primers and coating onto metal and con-
Ancamine® 2726 lyamine Adduct 2 300 – 600 100 240 – 290 1.03 115 50 – 60 40 – 50 8 - crete substrates X

Modified
Aliphatic Po- • Fast cure under adverse conditions of high humidity and
Ancamine® 2728 lyamine Adduct 7 1000 – 2500 59 – 61 250 – 290 1.02 233 80 – 120 95 5 - low temperature X
EPOXY CURING AGENTS – PRODUCT GUIDE EMEA 14 | 15

Specific
Max Colour Viscosity Amine Value Gravity Loading Gel Time Thin Film Set Tg or Civil Metal
Curing Agent Generic Type (Gardner) (mPa.s@25°C) Solids (%) (mgKOH/g) (@25°C) AHEW (PHR) (min@25°C) Time (h) HDT (°C) Benefits Engineering Coatings Adhesives

• Free of alkyl-substituted phenols, facilitating in low vola-

tile organic component coating and flooring formulations
and allows the use in emission compliant systems
• Fast cure and development of properties at ambient and
Modified 70 – 90 * low temperature
Ancamine® 2739 Polyamine 3 350-650 100 525-575 1.00 95 45 – 50 * @ 23°C 9* - • High resistance to carbamation and water-spotting X X

Modified
Polyamine • Ambient temperature curing agent with excellent UV
Ancamine® 2802 Adduct 3 450 – 650 100 410 – 475 1.02 87 45 – 50 35 – 40 10 - durability and can be used in low emission coatings X

Modified
Cycloaliphatic • Ambient temperature curative to enhance pot life of
Polyamine cycloaliphatic amine or for use in warmer climate
Ancamine® 2806 Adduct 2 30 – 100 100 310 – 340 1.00 76 40 100 – 120 12 - conditions X

• Free of alkyl-substituted phenols and provides rapid

Modified and excellent property development when cured at both
Ancamine® 2878 Polyamine 5 1000 – 2000 100 235 – 275 1.09 130 65 – 70 12 2 - ambient and at low temperature conditions (5 °C) X X

• Very fast curing agent for electronics, structural and

general purpose adhesives
Modified • Alternative to Mercaptan curing agent, reduced yellowing
Ancamine® 2914 UF Polyamine 5 300 – 2000 100 485 – 525 1.08 95 50 8 (20 g) - 50 – 65 • Low viscosity, zero VOC and phenol-free X

• Industry standard accelerator for Marine, Protective

Coating and Flooring markets
• Provides effective acceleration of cure at ambient and low
Ancamine® K54 Tertiary Amine 6 120 – 250 100 610 – 635 0.98 - 1–5 - - - temperature with use level of 1-5 PHR X X X

Epoxy EDA
isolated • Isolated amine adduct with very low odour, free-amine
Adduct content, and irritation potential
Solution in • Non-yellowing, bloom-free films. Improved cure
EDA Adduct Butanol/ under adverse conditions without induction. Good
870-XB-50 Xylene 5 1500 – 4000 50 76 – 104 0.99 370 80 – 100 - - - water resistance X
EPOXY CURING AGENTS – PRODUCT GUIDE EMEA 16 | 17

WATERBORNE AMINE
* Loading (PHR) for Anquamine® 419 has been calculated when used in combination with a solid epoxy resin dispersion

such as Ancarez® AR-555.

CURING AGENTS
Specific
Max Colour Viscosity Amine Value Gravity Loading 1,2 Pot Life 3
Curing Agent Generic Type (Gardner) (Pa.s@25°C) Solids (%) (mgKOH/g) (@25°C) AHEW 6 (PHR) (Hour) Benefits Civil Engineering Metal Coatings

• Provides 6 – 8 hours pot life with liquid epoxy resins

• Addresses the typically short pot life of 1 – 2 hours from current two
Aqueous Dispersion component, water-based systems
of Modified Amine • Extremely low viscosity, low color, and good retention of color upon
Anquamine® 100 Adduct Dispersion 0.2 53 – 57 100 1.05 350 180 6 UV exposure X

• Mannich base adduct specifically developed for concrete primer

applications and cement-based systems
Aqueous Solution • Primers exhibit fast drying time, quick return to service, zero-VOC
of Modified Amine • The product easily mixes with water and resin, can be brushed,
Anquamine® 287 Adduct 12 0.4 – 1 49 – 51 155 – 175 1.08 240 125 1 rolled or spray applied X

• A high solids, rapid curing hardener that can be used with both liquid
Aqueous Solution epoxy resin and solid epoxy resin dispersions for concrete/metal
of Modified Amine coatings and primers
Anquamine® 401 Adduct 12 25 – 40 69 – 71 240 – 260 1.09 166 60 – 90 1 – 1.5 • Anquamine® 401 can also be used for ECC (epoxy cement concrete) X X

• Designed for use with solid epoxy resin dispersions to give fast dry
Aqueous Solution times, and excellent corrosion and humidity resistance
of Modified Amine • Exhibits good gloss and good gloss retention
Anquamine® 419 Adduct 7 8 – 12 59 – 61 150 – 190 1.08 284 20 – 32* 4–6 • Excellent adhesion to steel makes it an ideal product for metal primers X

• Specifically developed for cost effective concrete floor coatings at

Aqueous Solution up to 300 micron applied film thickness
of Modified Amine • It easily emulsifies standard liquid epoxy resins, offers excellent
Anquamine® 721 Adduct 5 25 – 45 48 – 52 150 – 190 1.08 300 140 – 180 2–3 adhesion to damp conrete and has universal pigment acceptance X

• Rapid dry speed at ambient and low temperatures

Aqueous Solution • Excellent adhesion to damp concrete and resistance to carbamation
of Modified Amine 125 – 130 • Excellent aesthetics as determined by UV durability,
Anquamine® 728 Adduct 5 5 – 15 53 – 57 160 – 220 1.07 250 34* 1–2 gloss and pigment acceptance over pot life X

Aqueous Solution
of Modified Amine • Designed for cost-effective high film build concrete coatings
Anquamine® 735 Adduct 4 20 53 – 57 175 1.08 200 100 1 • Particularly self-levelling systems of 1 – 3 mm film thickness X

Aqueous Solution of • Cost-effective primers with moderate cure speed and excellent adhesion
Epilink® 360 Modified Polyamide 16 30 – 50 49 – 51 150 – 190 1.05 240 100 – 150 1 • May be used with co-solvent for additional viscosity dilution X

• Fast film drying and cure with liquid epoxy

Aqueous Emulsion of • Excellent anti-corrosive and flash rust resistance
Modified Polyamine • Low temperature cure down to 5°C
Epilink® 701 Adduct Emulsion 5 – 10 53 – 57 130 – 165 1.08 300 140 – 170 2–4 • Water vapour permeability X X
EPOXY CURING AGENTS – PRODUCT GUIDE EMEA 18 | 19

AMINE CURING AGENTS

* Measured at 75 °C

FOR HEAT-CURE
Specific
Max Colour Viscosity Amine Value Gravity Use Level Gel Time
Curing Agent Chemical nature Appearance (Gardner) (mPa.s@25°C) (mgKOH/g) (@25°C) AHEW (PHR) (minutes) Tg or HDT(°C) Benefits Composites Adhesives

• Suitable for coatings and adhesives

30.000 – applications
Ancamide® 261A Polyamide Liquid 7 50.000 320 – 350 0.96 120 65 75 - • Offers high adhesion and good colour stability X

• Low viscosity hardener

• Offers a longer working time than traditional
amidoamines
• Recommended for use in CIPP, electronics
Ancamide® 2781 Polyamide Liquid 12 80 – 120 230 – 270 0.92 104 55 400 – 500 50 – 60 and industrial electrical applications X

• Offers low viscosity and enhanced reactivity

along with moderate pot life and low
exotherm
• Suitable for casting, wet lay-up laminating,
and filament winding
• Raw materials are listed on positive list for
Ancamide® 2798 Polyamide Liquid 10 100 – 200 300 – 350 0.93 86 46 130 – 150 55 – 65 coatings in drinking water (KTW) X

• General purpose polyamide for liquid epoxy

resins
• Offers low viscosity, moderate pot life and
Ancamide® 3030 Polyamide Liquid 10 300 – 600* 370 – 410 0.96 95 50 80 – 140 - good adhesion X

• Long pot life version of Ancamide® 3030

• Medium viscosity
Ancamide® 3130 Polyamide Liquid 10 750 – 950* 300 – 340 0.97 95 50 >250 - • Improved temperature resistance X

• Offers lower viscosity compared to

Aliphatic polyamides
Ancamide® 500 Amidoamine Liquid 11 200 – 450 420 – 480 0.95 90 50 180 45 • Exhibits long pot life and non-critical loading X X

• Offers longest pot life and lowest viscosity of

amidoamines
Aliphatic • Very low exotherm; -non-critical loading
Ancamide® 506 Amidoamine Liquid 13 200 – 500 410 – 440 0.93 110 55 385 45 • Suitable for casting and wet lay-up laminating X X

• Offers outstanding flexibility, peel strength

and thermal shock resistance
• Exhibits lower viscosity than standard
polyamides
• Suitable for general purpose applications,
Ancamide® 910 Polyamide Liquid 6 6000 118 0.99 230 110 – 125 120 25 especially two-component adhesives X

• Modified polyamine derived from

triethylenetetramine
• Minimized skin irritation potential due to
hydroxylation
• Excellent chemical resistance
Ancamine® 1769 Modified Amine Liquid 4 600 – 900 975 1.01 48 25 24 99 • Good mechanical properties X X

• Offers very low viscosity

• Gives excellent toughness and thermal shock
resistance
• Suitable for structural adhesives and
Ancamine® 1922A Polyetheramine Liquid 1 10 507 1.0 55 29 57 48 composite binders X
EPOXY CURING AGENTS – PRODUCT GUIDE EMEA 20 | 21

Specific
Max Colour Viscosity Amine Value Gravity Use Level Gel Time
Curing Agent Chemical nature Appearance (Gardner) (mPa.s@25°C) (mgKOH/g) (@25°C) AHEW (PHR) (minutes) Tg or HDT(°C) Benefits Composites Adhesives

• Solution for composite reinforced bars for

construction applications
• Low viscosity and high reactivity for high
Modified speed processing
Cycloaliphatic • Outstanding alkali and chemical resistance
Ancamine® R 215 Amine Liquid 1 14 655 – 665 0.92 42.5 23.5 190 150 and excellent mechanical performance X

• Offers good impact resistance, fracture

toughness and excellent thermal and chemical
Polycycloaliphatic resistance
Ancamine® 2167 Amine Liquid 3 210 520 0.98 53 28 210 161 • Suitable industrial composite applications X

• Ideal alternative to aromatic diamines

• Offers low viscosity and long pot life at
moderate temperatures
• Excellent mechanical properties and high heat
resistance
Polycycloaliphatic • Suitable for filament winding, laminating,
Ancamine® 2264 Amine Liquid 9 2600 520 1.00 54 29 195 162 casting and tooling X

• High functionality designed for use in two

package epoxy formulations
Ancamine® 2422 Aliphatic Amine Liquid 5 1500 – 2500 660 – 675 1.12 49 26 - - • Excellent chemical resistance and pot life X

• Low viscosity for excellent impregnation

• Good processing by long pot life
• Recommended for manufacture of
Ancamine® 2919 Modified Amine Liquid 2 15 500 – 550 0.94 42 24 520 100 pressure vessels X X

• Leads to low viscosity and good balance of

long latency and reactivity
• Recommended for use in cured-in-place-pipe
Ancamine® 2927 Alipahtic Amine Liquid 12 100 – 220 230 – 270 1.02 26 15 46h 65 and composites applications X

Modified • Offers excellent flexibility

Ancamine® 3456 Polyamine Liquid 6 500 – 1500 160 – 190 0.97 250 125 – 135 35 - • Suitable for fast curing X

• Low initial viscosity during compounding for

excellent fiber wetting and high mechanical
properties
Modified • Offers high storage stability in B stage at
Cycloaliphatic 23°C and curing in 4 min at 150 °C
VESTALITE® S 101 Amine Liquid 3 20 670 – 710 0.91 49.6 26.1 340 120 • Designed for epoxy SMC applications X

• Low initial viscosity during compounding for

excellent fiber wetting and high mechanical
properties
Modified • Offers high storage stability in B stage at
Cycloaliphatic 23°C and curing in 3 min at 150 °C
VESTALITE® S 102 Amine Liquid 3 10 690 – 730 0.91 46.2 25.4 360 120 • Designed for epoxy SMC applications X
EPOXY CURING AGENTS – PRODUCT GUIDE EMEA 22 | 23

DICYANDIAMIDE,
* 30 min at 180°C

** 30 min at 150°C

CATALYSTS & ACCELERATORS

*** 4h at 140°C

DSC Activati- Latency

Melting Amine Value Use Level on Temperat. Tg or HDT (months
Curing Agent Generic Type Appearance Point (°C) (mgKOH/g) (sole) (sole) (°C) (sole) (°C) @40°C) Benefits Composites Adhesives

Amicure® • Particle size of 90% <30 microns with 1.5% flow aid
CG1200G Dicyandiamide White Powder 207 –211 - 4 – 15 165 121 * >6 • Recommended application fields: powder coatings, pre-pregs, adhesives and laminates X X

Amicure® CG • Particle size of 90% <10 microns with 3.5% flow aid
1400F Dicyandiamide White Powder 207 – 211 - 4 – 15 165 121* >6 • Finest particle size available for maximum reactivity X X

Light Yellow >24 • Diazabicycloundecene

Amicure® DBU-E Catalyst Liquid - - 1–5 95 - (20°C) • Highly effiecient accelerator suitable for phenolic novolacs, epoxy anhydride systems and other epoxies X

• 1,1’-(4 methyl-m-phenylene) bis (3,3-dimethyl) urea

• Substitute for chlorophenyl ureas
>24 • Combines excellent latency at ambient temperature with rapid heat cure X X
Amicure® UR2T Urea White Powder 182 – 190 - 0.5 – 3.0 141 - (20°C) • Accelerator for dicyandiamide cured epoxy resins

Modified • Sole curing agent or accelerator for latent amine curing agents (use level 2 – 7)
Ancamine® Aliphatic • Moderate reactivity and high shelf life
2014AS Amine White Powder 96 180 – 190 25 – 30 75 110** >3 • Excellent adhesion to metals and plastics X X

Modified
Ancamine® Aliphatic • Higher reactivity than Ancamine® 2014AS- Effective accelerator at moderate cure tmeperature (80 – 100°C)
2014FG Amine White Powder 96 180 – 190 25 – 30 75 110** 1 • Improved adhesion strength X X

Modified Light • Excellent low temperature reactivity above 70°C

Aliphatic Yellow >6 • Rapid development of green strength
Ancamine® 2337S Amine Powder 63 – 78 260 45 70 70 (20°C) • Suitable for 1k adhesives and hot-melt prepregs X X

Modified • Sole curing agent or accelerator for latent curing agents

Aliphatic • Improved adhesion strength
Ancamine® 2441 Amine White Powder 124 – 135 210 – 250 20 100 114 >3 • High Tg

Modified • Sole curing agent or accelerator for latent curing agents

Aliphatic • Improved adhesion strength
Ancamine® 2442 Amine White Powder 100 – 110 95 – 135 20 93 112 >3 • High Tg

• 2,4,6-Tri (dimethylaminomethyl) phenol

• Act as epoxy homopolymeriztion catalysts
>24 • Suitable for epoxy resins cured with a wide variety of hardener types
Ancamine® K54 Catalyst Amber Liquid - 610 – 635 1 – 15 - - (20°C) • Application in adhesives and high performance composites X X
EPOXY CURING AGENTS – PRODUCT GUIDE EMEA 24 | 25

DSC Activati- Latency

Melting Amine Value Use Level on Temperat. Tg or HDT (months
Curing Agent Generic Type Appearance Point (°C) (mgKOH/g) (sole) (sole) (°C) (sole) (°C) @40°C) Benefits Composites Adhesives

Modified Orange-red • Chemically modified amine complex of boron trifluoride

Amine Com- Liquid, visco- - 6 –10 • Good solubility in liquid epoxy resins
Anchor® 1040 plex of BF3 sity 20 Pa.s - 7 – 12 100 130 *** weeks • Long pot life X

Modified Dark Liquid, • Chemically modified amine complex of boron trifluoride

Amine Com- viscosity 1.7 - 6 –10 • Lower activation temperature
Anchor® 1115 plex of BF3 Pa.s - 5 – 10 75 140 *** weeks • Long pot life X

• P-toluenesulphonate salt of 2-amino-2-methyl-1-propanol

• 50wt% solution in butanol
Catalyst 1786B Catalyst Amber Liquid - - 1–4 - - - • Recommended application fields: white goods, OEM, drum and pail coatings X X

Micronised • Very long latency

Curezol® 2MZ Solid Pale Yellow • High heat distortion temperature
Azine 10µm Imidazole Powder 248 – 258 - 6–8 145 156 ** 45 days • Suitable as sole curing agents or to accelerate Dicy / anhydride formulations X X

• High reactivity
Liquid Pale Yellow • Medium viscosity
Imicure® EMI-24 lmidazole Liquid - - 1–4 95 156 ** 9 hours • Suitable as sole curing agents or to accelerate Dicy / anhydrides X X
EPOXY CURING AGENTS – PRODUCT GUIDE EMEA 26 | 27

SPECIALTY RESINS, DILUENTS

* Theoretical, as supplied. When EEW 1300 is assumed, the best overall results are obtained in the range of 0.8:1 to 1.2:1

(epoxy:amine) stoichiometry.

AND MODIFIERS
Epoxy
Max Colour Viscosity Specific Gravity Equivalent Free ECH Hydrolizable Moisture Civil
Curing Agent Generic Type (Gardner) (Pa.s@25°C) Solids (%) (@25°C) Weight (EEW) Content (PPM) Chlorine (%) Content (%) Benefits Engineering Metal Coatings Composites

• Zero-VOC, novel, low-viscosity, solid epoxy resin

dispersion (supplied at 55% solids)
• May be used with products such as our Anqua-
Water-based mine® 419, Anquamine® 401 and Anquamine®
Solid Epoxy 100 for rapid cure water based systems
Ancarez® Resin • It is ideal for concrete primers/coatings, industrial
AR-555 Dispersion Dispersion 150 – 300 55 1.09 550 * - - - maintenance primers/top coats X X

• General-purpose diluent
• Low toxicity and low vapor pressure
Alkyl • Slows reactivity
(C12–C14) • Good viscosity reduction
Epodil® 748 Glycidyl Ether 1 5 – 20 100 0.89 275 – 300 10 max 0.1 max 0.1 max • Improves flexibility and adhesion to nonpolar surfaces X X X

• Widely used in the civil engineering and composite

1-4 Butanediol sectors
Digylycidyl • Its combination of dilution profile and low vapour
Epodil® 750 Ether 1 15 – 20 100 1.11 120 – 130 10 max 0.1 max 0.1 max pressure make it the preferred choice X X X

• A chemically-inert, low-viscosity, liquid

hydrocarbon resin
Hydrocarbon • Acts as a surface tension reducer, as a pigment
Epodil® LV5 Resin <2 50 100 1.02 - - <5ppm 0,01% wetting aid, and as an adhesion promoter X X
EPOXY CURING AGENTS – PRODUCT GUIDE EMEA 28 | 29

ADHESION PROMOTERS
FOR PVC PLASTISOLS
Amine Value Viscosity
Adhesion Promoter Generic Type Appearance Colour (Gardner) (mgKOH/g) (Pa.s@25°C) Use Level (PHR) Typical Cure Schedule Benefits

• General purpose adhesion promoter

• Provides adhesion to a wide variety of automotive electrodeposition primers
Nourybond® 272 Modified Polyamide Liquid 10 185 – 200 15 – 35 1–4 30 min@130°C • Suitable for underbody coatings and non-visible seam sealers

• Allows low temperature cure (120°C)

• Offers excellent rheological properties, high strength and superior colour stability
• Suitable for anti-chip primers, visible seam sealers and low bake PVC plastisols
Nourybond® 276 Modified Polyamide Liquid 10 110 – 130 8 – 28 1–2 30 min@120°C • First choice for (ultra) low density plastisols

• Free of plasticizer (100% solid)

Nourybond® 301 Modified Polyamide Liquid 12 380 – 400 1 – 1.5@75°C 0.5 – 2 30 min@130°C • Improves coatability of PVC plastisol

• Highly effective adhesion promoter with low usage level

• Suitable for underbody coating and sealer, non visible seam sealers and anti-chip primers
Nourybond® 316 Modified Polyamide Liquid 14 260 – 310 1 – 2 @ 75°C 0.5 – 2 30 min@130°C • Non-phthalate plasticizer

• Offer good sag resistance

• Good rheological properties allow for broad applications
• Suitable for underbody coating and sealer and non visible seam sealer
Nourybond® 350 Modified Polyamide Liquid 10 130 – 170 0.5 – 2 @ 75°C 1–3 30 min@130°C • Non-phthalate plasticizer

• Offer good sag resistance

• Low viscosity
• Suitable for underbody coating and sealer and non visible seam sealer
Nourybond® 356 Polyamidoamide Liquid 12 185 – 200 1 – 4.5 0.5 – 2 30 min@130°C • Non-phthalate plasticizer

• Good rheological properties allow for broad application field

Nourybond® 368 Modified Polyamide Liquid 12 225 – 245 2–8 0.5 – 2 30 min@130°C • Non-phthalate plasticizer
EPOXY CURING AGENTS – PRODUCT GUIDE EMEA 30 | 31

DEFINITIONS & PRODUCT INDEX

CALCULATIONS
Amine Value The measurement by means of acid/base titration of the amine Amicure® CG1200G 22 I 23 Ancamine® 1922A 18 I 19 Ancamine® 3456 10 I 11; 20 I 21
nitrogen content in a curing agent. Amine value is expressed in
Amicure® CG 1400F 24 I 25 Ancamine® 2014AS 22 I 23 Ancamine® K54 14 I 15; 22 I 23
units of mg of KOH equivalent to the basic nitrogen content in a
Amicure® DBU-E 22 I 23 Ancamine® 2014FG 22 I 23 Ancamine® R 215 20 I 21
1g sample (mg KOH/g).
Pot Life The ‘working time’ that mixed resin and curing agent exhibits. Amicure® UR2T 22 I 23 Ancamine® 2165 10 I 11 Ancarez® AR-555 26 I 27

Carbamation The surface defect of a coating that can occur when curing at Ancamide® 260A 8I9 Ancamine® 2167 20 I 21 Anchor® 1040 24 I 25
too high a humidity or too low a temperature. It is the reaction
Ancamide® 261A 18 I 19 Ancamine® 2264 20 I 21 Anchor® 1115 24 I 25
of carbon dioxide in the air with amine.
EEW Epoxide Equivalent Weight. Ancamide® 500 8 I 9; 18 I 19 Ancamine® 2280 10 I 11 Anquamine® 100 16 I 17

AHEW Amine Hydrogen Equivalent Weight. Ancamide® 503 8I9 Ancamine® 2337S 22 I 23 Anquamine® 287 16 I 17

Part A Epoxy resin component. Part B Curing Agent component. Ancamide® 506 8 I 9; 18 I 19 Ancamine® 2410 12 I 13 Anquamine® 401 16 I 17
PHR Parts per Hundred of Resin (100g)
Ancamide® 700B75 8I9 Ancamine® 2422 12 I 13; 20 I 21 Anquamine® 419 16 I 17

Ancamide® 910 8 I 9; 18 I 19 Ancamine® 2432 12 I 13 Anquamine® 721 16 I 17

Ancamide® 2050 8I9 Ancamine® 2441 22 I 23 Anquamine® 728 16 I 17

Ancamide® 2353 8I9 Ancamine® 2442 22 I 23 Anquamine® 735 16 I 17

Ancamide® 2386 8I9 Ancamine® 2519 12 I 13 Catalyst 1786B 24 I 25

Ancamide® 2426 8I9 Ancamine® 2609W 12 I 13 Curezol® 2MZ Azine 10µm 24 I 25

Ancamide® 2443 8I9 Ancamine® 2672 12 I 13 EDA Adduct 870-XB-50 14 I 15

Ancamide® 2445 8I9 Ancamine® 2686 12 I 13 Epilink® 360 16 I 17

Ancamide® 2573 10 I 11 Ancamine® 2692 12 I 13 Epilink® 701 16 I 17

Ancamide® 2634 10 I 11 Ancamine® 2712M 12 I 13 Epodil® 748 26 I 27

Ancamide® 2652 10 I 11 Ancamine® 2719 12 I 13 Epodil® 750 26 I 27

Calculating the quantity of curing agent required to cure 100g of epoxy resin (PHR):
Ancamide® 2769 10 I 11 Ancamine® 2726 12 I 13 Epodil® LV5 26 I 27

Ancamine® 2728 12 I 13 Imicure® EMI-24 24 I 25

Amine Hydrogen Equivalent Weight (AHEW) Ancamide® 2781 18 I 19
x 100 = PHR
Ancamide® 2798 18 I 19 Ancamine® 2739 12 I 13 Nourybond® 272 28 I 29
Epoxy Equivalent Weight (EEW)
Ancamide® 3030 10 I 11; 18 I 19 Ancamine® 2759 10 I 11 Nourybond® 276 28 I 29

Ancamide® 3130 10 I 11; 18 I 19 Ancamine® 2760 10 I 11 Nourybond® 301 28 I 29

Calculating the Amine Hydrogen Equivalent Weight for a blend of curing agents:
Ancamide® 3200 10 I 11 Ancamine® 2802 14 I 15 Nourybond® 316 28 I 29

Total Weight of Curing Agent (g) Ancamide® 3419 10 I 11 Ancamine® 2806 14 I 15 Nourybond® 350 28 I 29

( )( )
Ancamide® 3444 10 I 11 Ancamine® 2878 14 I 15 Nourybond® 356 28 I 29
Weight (g) of Curing Agent1 Weight (g) of Curing Agent2
+ = AHEW 1+2 Ancamide® 3622 10 I 11 Ancamine® 2914 UF 14 I 15 Nourybond® 368 28 I 29
AHEW1 AHEW2
(curing agent blend)
Ancamine® 1618 10 I 11 Ancamine® 2919 20 I 21 VESTALITE® S 101 20 I 21

Ancamine® 1769 10 I 11; 18 I 19 Ancamine® 2927 20 I 21 VESTALITE® S 102 20 I 21

EVONIK OPERATIONS GMBH
Business Line Crosslinkers
Paul-Baumann-Straße 1
45764 Marl
Germany
Phone +49 2365 49-9011
www.evonik.com/crosslinkers

 is a registered trademark of EVONIK CORPORATION

EVONIK INDUSTRIES AG Business Line Crosslinkers
or one of its subsidiaries. 7201 Hamilton Blvd.
Curezol is a registered trade- Allentown, PA 18195
mark of Shikoku Chemical 1 800 345-3148
Corporation. Outside U.S. and
Canada 1 610 481-6799
This information and all further
technical advice are based on our
present knowledge and experi- EVONIK SPECIALITY
ence. However, it implies no lia- CHEMICALS CO. LTD.
bility or other legal respon­sibility Business Line Crosslinkers
on our part, including with regard 55, Chundong Road
to existing third party intellectual Xinzhuang Industry Park
property rights, especially patent Shanghai, 201108
rights. In particular, no warranty, China
whether express or implied, or Phone +86 21 6119-3056
guarantee of product properties
in the legal sense is intended or
implied. We reserve the right to For further information on
make any changes according to products and availability visit:
technological progress or further www.evonik.com/crosslinkers
developments. The customer is
not released from the obligation
to conduct careful inspection
and testing of incoming goods.
Performance of the product
described herein should be veri-
fied by testing, which should be
carried out only by qualified
experts in the sole responsibility For contacts in your country,
of a customer. Reference to trade please visit:
names used by other companies is www.evonik.com/
neither a recommendation, nor crosslinkers-contacts
does it imply that similar products
could not be used.