Δ˰˰˰˰˰ϳΩϭόγϟ΍Δ˰˰˰˰˰ϳΑέόϟ΍Δ˰˰˰ϛϠϣϣϟ΍

KINGDOM OF SAUDIA ARABIA

ΓΩϭ˰˰˰˰˰˰Οϟ΍ϭα˰˰ϳ˰˰˰ϳΎϘϣϟ΍ϭΕΎ˰˰˰ϔλ΍ϭϣϠϟΔ˰˰˰˰ϳΩϭ˰ό˰γϟ΍Δ˰˰˰΋ϳϬ˰ϟ΍
Saudi Standards, Metrology and Quality Org.(SASO)

Standard Specification Δ˰ϳγΎϳ˰ϗΔ˰ϔλ΍ϭ˰ϣ

Standard No. SASO-ISO-11833-2 Δϔλ΍ϭϣϟ΍ϡϗέ

Reference No. ISO-11833-2 Δϔλ΍ϭϣϟ΍ϊΟέϣ

Issue Year 1998 έ΍Ωλϻ΍Δϧγ
Adoption Year 2008 ΩΎϣΗϋϻ΍Δϧγ

ϝϗ΃΢΋Ύϔλϟ΍ϙϣγ2˯ίΟϟ΍±Ε΍ίϳϣϣϭΩΎόΑ΃ϭω΍ϭϧ΃±ϥΩϠϣέϳϐϟ΍ ϝϳϧϳϔϟ΍ΩϳέϭϠϛ ΩϳΩϋ±ϙϳΗγϼΑϟ΍

ϡϣ1ϥϣ

Plastics - Unplasticized poly(vinyl chloride) sheets - Types, dimensions

and characteristics ±Part 2: Sheets of thickness less than 1 mm

ΔϳΩϭόγϟ΍ΔϳγΎϳϘϟ΍ΕΎϔλ΍ϭϣϟ΍
Saudi Standards
 ϲϧρϭϡϳΩϘΗ

Δ˰ϳϟΎ˰˰Ηϟ΍Δ˰˰ϳϟϭΩϟ΍ΔϳγΎ˰ϳϘϟ΍Δ˰ϔ˰λ΍ϭϣϟ΍ϲ˰ϧΑΗΑΓΩϭ˰˰˰Οϟ΍ϭα˰˰ϳϳΎϘϣϟ΍ϭΕΎ˰˰ϔλ΍ϭϣϠϟΔ˰˰ϳΩϭόγϟ΍Δ˰˰΋ϳϬϟ΍Ε˰˰ϣΎϗ
Ύ˰˰ϬϳϠϋΔ˰˰ϳ˰ϧϓΕϼ˰ϳΩόΗϱ΃ϝΎ˰˰ΧΩ΍ϥϭΩ

1998 έ΍Ωλ΍ ISO-11833-2

ϥϣϝϗ΃΢΋Ύϔλϟ΍ϙϣγ2˯ίΟϟ΍±Ε΍ίϳϣϣϭΩΎόΑ΃ϭω΍ϭϧ΃±ϥΩϠϣέϳϐϟ΍ ϝϳϧϳϔϟ΍ΩϳέϭϠϛ ΩϳΩϋ±ϙϳΗγϼΑϟ΍

ϡϣ1

NATIONAL FOREWORD
The Saudi Standards, Metrology and Quality (SASO) has adopted without any
technical changes the International Standard:

ISO-11833-2 Issue Year 1998

Plastics - Unplasticized poly(vinyl chloride) sheets - Types, dimensions and

characteristics ±Part 2: Sheets of thickness less than 1 mm

ΔϳΩϭόγϟ΍ΔϳγΎϳϘϟ΍ΕΎϔλ΍ϭϣϟ΍
Saudi Standards
 Δ˰˰˰˰˰ϳΩϭόγϟ΍Δ˰˰˰˰˰ϳΑέόϟ΍Δ˰˰˰ϛϠϣϣϟ΍
KINGDOM OF SAUDIA ARABIA

ΓΩϭ˰˰˰˰˰˰Οϟ΍ϭα˰˰ϳ˰˰˰ϳΎϘϣϟ΍ϭΕΎ˰˰˰ϔλ΍ϭϣϠϟΔ˰˰˰˰ϳΩϭ˰ό˰γϟ΍Δ˰˰˰΋ϳϬ˰ϟ΍
Saudi Standards, Metrology and Quality Org.(SASO)

Standard Specification Δ˰ϳγΎϳ˰ϗΔ˰ϔλ΍ϭ˰ϣ

Standard No. SASO-ISO-11833-2 Δϔλ΍ϭϣϟ΍ϡϗέ

Reference No. ISO-11833-2 Δϔλ΍ϭϣϟ΍ϊΟέϣ

Issue Year 1998 έ΍Ωλϻ΍Δϧγ
Adoption Year 2008 ΩΎϣΗϋϻ΍Δϧγ

Numeric Coding 922-11833-2 ϲ˰ϣ˰ϗέϟ΍ί˰ϳϣέ˰Ηϟ΍

ϝϗ΃΢΋Ύϔλϟ΍ϙϣγ2˯ίΟϟ΍Ε΍ίϳϣϣϭΩΎόΑ΃ϭω΍ϭϧ΃ϥΩϠϣέϳϐϟ΍ ϝϳϧϳϔϟ΍ΩϳέϭϠϛ ΩϳΩϋϙϳΗγϼΑϟ΍

ϡϣ1ϥϣ

Plastics -- Unplasticized poly(vinyl chloride) sheets -- Types,

dimensions and characteristics -- Part 2: Sheets of thickness less than
1 mm

ΔϳΩϭόγϟ΍ΔϳγΎϳϘϟ΍ΕΎϔλ΍ϭϣϟ΍
Saudi Standards
 ϲϧρϭϡϳΩϘΗ

Δ˰ϳϟΎ˰˰Ηϟ΍Δ˰˰ϳϟϭΩϟ΍ΔϳγΎ˰ϳϘϟ΍Δ˰ϔ˰λ΍ϭϣϟ΍ϲ˰ϧΑΗΑΓΩϭ˰˰˰Οϟ΍ϭα˰˰ϳϳΎϘϣϟ΍ϭΕΎ˰˰ϔλ΍ϭϣϠϟΔ˰˰ϳΩϭόγϟ΍Δ˰˰΋ϳϬϟ΍Ε˰˰ϣΎϗ
Ύ˰˰ϬϳϠϋΔ˰˰ϳ˰ϧϓΕϼ˰ϳΩόΗϱ΃ϝΎ˰˰ΧΩ΍ϥϭΩ

1998 έ΍Ωλ΍ ISO-11833-2

ϥϣϝϗ΃΢΋Ύϔλϟ΍ϙϣγ2˯ίΟϟ΍Ε΍ίϳϣϣϭΩΎόΑ΃ϭω΍ϭϧ΃ϥΩϠϣέϳϐϟ΍ ϝϳϧϳϔϟ΍ΩϳέϭϠϛ ΩϳΩϋϙϳΗγϼΑϟ΍

ϡϣ1

NATIONAL FOREWORD
The Saudi Standards, Metrology and Quality (SASO) has adopted without any
technical changes the International Standard:

ISO-11833-2 Issue Year 1998

Plastics -- Unplasticized poly(vinyl chloride) sheets -- Types, dimensions and

characteristics -- Part 2: Sheets of thickness less than 1 mm

ΔϳΩϭόγϟ΍ΔϳγΎϳϘϟ΍ΕΎϔλ΍ϭϣϟ΍
Saudi Standards
 INTERNATIONAL ISO
STANDARD 11833-2

First edition
1998-07-15

Plastics — Unplasticized poly(vinyl

chloride) sheets — Types, dimensions and
characteristics —
Part 2:
Sheets of thickness less than 1 mm
Plastiques — Feuilles en poly(chlorure de vinyle) non plastifié — Types,
dimensions et caractéristiques —
Partie 2: Feuilles et films d'épaisseur inférieure à 1 mm

IN ADDITION TO THEIR EVALUATION AS

A
BEING ACCEPTABLE FOR INDUSTRIAL,
TECHNOLOGICAL, COMMERCIAL AND USER
PURPOSES, DRAFT INTERNATIONAL STAND-
ARDS MAY ON OCCASION HAVE TO BE
CONSIDERED IN THE LIGHT OF THEIR
POTENTIAL TO BECOME STANDARDS TO
WHICH REFERENCE MAY BE MADE IN Reference number
NATIONAL REGULATIONS. ISO 11833-2:1998(E)
ISO 11833-2:1998(E)

Foreword

ISO (the International Organization for Standardization) is a worldwide

federation of national standards bodies (ISO member bodies). The work of
preparing International Standards is normally carried out through ISO
technical committees. Each member body interested in a subject for which
a technical committee has been established has the right to be represented
on that committee. International organizations, governmental and non-
governmental, in liaison with ISO, also take part in the work. ISO
collaborates closely with the International Electrotechnical Commission
(IEC) on all matters of electrotechnical standardization.

Draft International Standards adopted by the technical committees are

circulated to the member bodies for voting. Publication as an International
Standard requires approval by at least 75 % of the member bodies casting
a vote.

International Standard ISO 11833-2 was prepared by Technical Committee

ISO/TC 61, Plastics, Subcommittee SC 11, Products.

ISO 11833 consists of the following parts, under the general title
Unplasticized poly(vinyl chloride) sheets — Types, dimensions and
characteristics :

— Part 1: Sheets of thickness not less than 1 mm

— Part 2: Sheets of thickness less than 1 mm

© ISO 1998
All rights reserved. Unless otherwise specified, no part of this publication may be reproduced
or utilized in any form or by any means, electronic or mechanical, including photocopying and
microfilm, without permission in writing from the publisher.
International Organization for Standardization
Case postale 56 • CH-1211 Genève 20 • Switzerland
Internet [email protected]
Printed in Switzerland

ii
INTERNATIONAL STANDARD © ISO ISO 11833-2:1998(E)

Plastics — Unplasticized poly(vinyl chloride) sheets — Types,

dimensions and characteristics —
Part 2:
Sheets of thickness less than 1 mm

1 Scope

1.1 This part of ISO 11833 specifies requirements for sheets and films of unplasticized poly(vinyl chloride)
(PVC-U) and the test methods to be used to measure the required values.

1.2 It applies only to sheets of thickness less than 1,0 mm.

1.3 It does not cover thermoshrinkable or biaxially stretched PVC-U sheets and films.

2 Normative references

The following standards contain provisions which, through reference in this text, constitute provisions of this part of
ISO 11833. At the time of publication, the editions indicated were valid. All standards are subject to revision, and
parties to agreements based on this part of ISO 11833 are encouraged to investigate the possibility of applying the
most recent editions of the standards indicated below. Members of IEC and ISO maintain registers of currently valid
International Standards.

ISO 75-2:1993, Plastics — Determination of temperature of deflection under load — Part 2: Plastics and ebonite.

ISO 291:1997, Plastics — Standard atmospheres for conditioning and testing.

ISO 306:1994, Plastics — Thermoplastic materials — Determination of Vicat softening temperature (VST).

ISO 527-3:1995, Plastics — Determination of tensile properties — Part 3: Test conditions for films and sheets.

ISO 1163-1:1995, Plastics — Unplasticized poly(vinyl chloride) (PVC-U) moulding and extrusion materials — Part 1:
Designation system and basis for specifications.

ISO 2818:1994, Plastics — Preparation of test specimens by machining.

1)
ISO 2859-1:— , Sampling procedures for inspection by attributes — Part 1: Sampling plans indexed by acceptable
quality level (AQL) for lot-by-lot inspection.

ISO 8256:1990, Plastics — Determination of tensile-impact strength.

ISO 11501:1995, Plastics — Film and sheeting — Determination of dimensional change on heating.

1) To be published. (Revision of ISO 2859-1:1989)

1
ISO 11833-2:1998(E) © ISO

3 Material

Sheets shall be fabricated from unplasticized PVC compounds as defined in ISO 1163-1:1995, subclause 1.3.
Compounds may contain additives such as stabilizers, lubricants, processing aids, impact modifiers, flame
retardants and colourants. Compounds and additives of unknown identity and composition shall not be used for the
processing of sheets.

NOTE — Legal considerations may cause a specific choice of compound.

4 Classification

Sheets are classified into four groups (three of which are subdivided into two classes) by the numerical values of
the two most important properties, i.e. the tensile impact strength and the Vicat softening temperature (see table 3).

5 Requirements

5.1 Appearance

The surface shall be free of noticeable flaws, cracks, mottling, voids, bubbles, impurities and other defects which
are not acceptable for the application envisaged. The sheet shall have a smooth surface, except for embossed
sheets which shall have a uniform pattern. Any further requirements concerning appearance shall be agreed
between the interested parties.

5.2 Colour

Colourants shall be distributed uniformly throughout the material. Admissible differences in colour within a sheet and
amongst sheets shall be agreed between the interested parties as required.

5.3 Dimensions

5.3.1 Length, width and rectangularity

The length and width of sheets shall be agreed between the interested parties. The tolerances on the dimensions
and the rectangularity shall be as specified in table 1.

Table 1 — Tolerances on length, width and rectangularity

Dimensions in millimetres

Dimension/rectangularity Tolerance

+ 20
Length Flat sheet 0

Rolled sheet Minus not accepted

+5
Width 0

Rectangularity Flat sheet D l < 4 mm per 1 000 mm of

side

2
© ISO ISO 11833-2:1998(E)

5.3.2 Thickness

The tolerance on the thickness shall be as specified in table 2.

Table 2 — Tolerances on thickness

Nominal thickness, d Tolerance

mm %

d < 0,03 ± 40
0,03 < d < 0,05 ± 30
0,05 < d < 0,1 ± 20
0,1 < d < 0,3 ± 15
0,3 < d < 0,5 ± 13
0,5 < d < 1,0 ± 10

5.4 Properties

The properties of sheets of each group and class shall be as specified in table 3.

Table 3 — Properties of sheets

Property Test Unit Requirements See

method subclause
Group 1 Group 2 Group 3 Group 4
Class Class Class Class Class Class
1 2 1 2 1 2

Tensile stress ISO 527-3

at yield Type 1B MPa > 40 > 40 > 40 > 40 > 40 > 40 > 40 6.4.1
50 mm/min

Nominal strain ISO 527-3

at break Type 1B % > 20 > 20 > 20 > 20 > 20 > 20 > 20 6.4.1
50 mm/min

Tensile impact ISO 8256

strength Method A kJ/m2 — — > 300 > 300 > 400 > 400 — 6.4.2
Type 3

Vicat ISO 306

softening Method B °C > 60 > 70 > 60 > 70 > 60 > 70 > 90 6.5
temperature

The requirements for the optional properties given in table 4 shall be agreed between the interested parties as
required.

Table 4 — Optional properties

Property Test method Unit

Temperature of deflection under load ISO 75-2 °C

Method A

Dimensional change on heating ISO 11501 %

3
ISO 11833-2:1998(E) © ISO

5.5 Chemical and physiological properties

5.5.1 Flammability

Requirements for flammability shall be agreed between the interested parties as required. Relevant national and
international standards shall be considered in the agreement.

5.5.2 Chemical resistance

Requirements for chemical resistance for specific applications shall be agreed between the interested parties as
required.

5.5.3 Physiological behaviour

Requirements for physiological behaviour shall be agreed between the interested parties as required. The relevant
legislation shall be taken into consideration if the sheet will come into contact with food.

6 Test methods

6.1 General

6.1.1 Sampling

Take a sample sufficient to determine the compliance of the material with this specification. The sampling procedure
given in ISO 2859-1 is recommended.

6.1.2 Preparation of specimens

Prepare all specimens in accordance with ISO 2818. Prepare the specimens for tensile strength, tensile impact
strength and dimensional change on heating by stamping or cutting. The surface of the specimens shall be free of
any damage or faults in order to avoid notch effects. Should any burrs be present on a specimen, remove them
without damaging the surface.

6.1.3 Conditioning and testing of specimens

Unless otherwise specified in the applicable test method, carry out testing in one of the standard atmospheres
specified in ISO 291, after conditioning the specimens for at least 16 h in the same atmosphere.

6.2 Appearance examination

Examine the surfaces and cut edges with the naked eye from a distance of 60 cm for noticeable flaws, cracks,
mottling, voids, bubbles, impurities and other defects, inspecting the sheet in the direction opposite to that of the
incident light.

6.3 Dimensions

6.3.1 Measure the length, width and diagonals of the sheet to the nearest 1 mm, using a calibrated ruler.

6.3.2 Measure the thickness to the nearest 0,01 mm, using a calibrated thickness gauge.

4
© ISO ISO 11833-2:1998(E)

6.3.3 Rectangularity

Determine the rectangularity ∆ l as shown in figure 1.

Dimensions in millimetres

Figure 1 — Rectangularity

6.4 Mechanical properties

6.4.1 Tensile stress at yield and nominal strain at break

Determine the tensile stress at yield and the nominal strain at break in accordance with ISO 527-3, using at least
five type 1B specimens for each direction and a test speed of 50 mm/min.

6.4.2 Tensile impact strength

Determine the tensile impact strength in accordance with ISO 8256.

6.5 Vicat softening temperature

Determine the Vicat softening temperature in accordance with ISO 306, Method B.

7 Marking

The following information shall be marked on each package of sheets:

a) the number of this part of ISO 11833, the material and the product designation as shown below:

b) the dimensions;

c) the manufacturer's name and country, and the year and month of manufacture or lot number.

5
ISO 11833-2:1998(E) © ISO

ICS 83.140.10
Descriptors: plastics products, unplasticized polyvinyl chloride, plastic sheets, classification, specifications, dimensions, characteristics,
mechanical properties, physical properties, tests, dimensional measurements.