Pitting

Pitting corrosion is a localized form of corrosion that occurs in small areas but can penetrate deeply below the surface. It is difficult to detect and can cause equipment to fail with little visible corrosion. Pitting is caused by environments containing chlorides or other agents that attack the passive oxide layer on metals like stainless steel. It occurs most often on upward facing horizontal surfaces due to gravitational effects. Within pits, the metal is anodic and dissolves rapidly while the area outside the pit acts as a cathode.

Uploaded by

rizky febrian
Copyright
© Attribution Non-Commercial (BY-NC)
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PPT, PDF, TXT or read online on Scribd
210 views

Pitting

Pitting corrosion is a localized form of corrosion that occurs in small areas but can penetrate deeply below the surface. It is difficult to detect and can cause equipment to fail with little visible corrosion. Pitting is caused by environments containing chlorides or other agents that attack the passive oxide layer on metals like stainless steel. It occurs most often on upward facing horizontal surfaces due to gravitational effects. Within pits, the metal is anodic and dissolves rapidly while the area outside the pit acts as a cathode.

Uploaded by

rizky febrian
Copyright
© Attribution Non-Commercial (BY-NC)
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PPT, PDF, TXT or read online on Scribd
You are on page 1/ 14

UN1001: REACTOR CHEMISTRY AND CORROSION Section 6: Pitting Corrosion

By

D.H. Lister & W.G. Cook


Department of Chemical Engineering University of New Brunswick
1

UN1001: Section 6: Pitting Corrosion

PITTING: Extreme localized attack, may perforate metal sheet/plate . . . etc. Pitting factor =

p d

d = average penetration from weight loss; p = deepest penetration

Undercutting pit opening usually < 1 mm.

Pits may overlap to give the appearance of rough, general wastage.

UN1001: Section 6: Pitting Corrosion

Pitting is an insidious and destructive form of corrosion:


difficult to detect (pits may be small on surface, but extensive below surface from undercutting; may be covered with deposit); can cause equipment to fail (by perforation) with very little weight loss;

difficult to measure as pit depth and distribution vary widely under (nominally) identical conditions;
incubation period may be months or years.

UN1001: Section 6: Pitting Corrosion

Pitting of 18-8 stainless steel by acid-chloride solution.

Pitting of stainless steel condenser tube.


4

UN1001: Section 6: Pitting Corrosion

Pits usually occur on upward-facing horizontal surfaces,


pit growth

and less frequently on vertical surfaces;

pit growth

Gravity is involved.

rarely on downward-facing surfaces;

pit growth

UN1001: Section 6: Pitting Corrosion

Mechanism: Has some features in common with CREVICE CORROSION.... consider metal M being pitted by aerated NaCl solution...

Autocatalytic processes occurring in a corrosion pit.

UN1001: Section 6: Pitting Corrosion

Remember: inside pit - anodic, rapid dissolution;

outside pit - cathodic, O2 reduction;


most M+ will hydrolyse, form H+; positive charges attract Cl- ions; H+ and Cl- accelerate metal dissolution; high ionic concentrations in pit make O2 solubility very low; high density of solution within pits means pits are more stable when growing downwards;

static environment accelerates process.


7

UN1001: Section 6: Pitting Corrosion

At high pH (i.e., high OHconcentration), precipitation of iron hydroxides and oxidation to Fe3+ oxides can lead to corrosion product caps or tubes around pits on steels.

Corrosion tube growth mechanism.


8

UN1001: Section 6: Pitting Corrosion

Metals Susceptible to Pitting


Most often, passivating metals, especially stainless steels, often in passivating environments (e.g., containing oxygen) but with agents such as Cl- that attack the passive oxide film. SENSITIZED SS particularly vulnerable (its heat treatment has depleted the grain boundaries of Cr by precipitating chromium carbide). COLD WORKING increases pitting attack, perhaps dislocation pattern is important. DISCUSS ETCHED or GROUND surfaces more likely to pit than polished surfaces. Stainless Steel more susceptible than Carbon Steel (though CS will have more 9 rapid GENERAL CORROSION).

UN1001: Section 6: Pitting Corrosion

Some alloys developed especially to resist pitting. Effects of alloying on pitting resistance of stainless steel alloys

Element
Chromium Nickel Molybdenum Silicon Titanium and niobium Sulfur and selenium Carbon Nitrogen

Effect on pitting resistance


Increases Increases Increases Decreases; increases when present with molybdenum Decreases resistance in FeCI3, other mediums no effect Decreases Decreases, especially in sensitized condition Increases

Source: N. D. Greene and M. G. Fontana, Corrosion 15:25t (1959).


10

UN1001: Section 6: Pitting Corrosion

Pitting Environments
Usually, solutions containing chloride or chlorine-containing ions (e.g., hypochlorites [bleaches]) have strong pitting tendencies. Bromides are also aggressive, but fluorides and iodides are not. Cupric, ferric and mercuric ions promote pitting . . . easily reduced cathodically and do not require dissolved O2; CuCl2 and FeCl3 are extremely aggressive (latter used as a test solution).

Thiosulphate ion (S2O32-) may also promote pitting.

11

UN1001: Section 6: Pitting Corrosion

Evaluating Pitting Attack Weight loss of test specimens no good ( . . . why ?). Measurement of pit depth complicated because of statistical variations.

Relationship between pit depth and the number of pits appearing on a corroded surface.

Average pit depth of little use, since it is the deepest pit that causes failure.
12

UN1001: Section 6: Pitting Corrosion

MAXIMUM PIT DEPTH can be a useful way of expressing pitting corrosion, and for comparing pitting resistance of standard test samples.

HOWEVER, statistical nature of pitting means that sample size is important.

Pit depth as a function of exposed area.

Should never predict lifetime of plant components from tests on small samples. 13

UN1001: Section 6: Pitting Corrosion

Examples of pitting corrosion:


Alloy-800 SG tubes with phosphate chemistrypitting severe pitting wastage. Point Lepreau had some pitting, switched to AVT.
SS cooling water H.X. left static under silted conditionssevere pitting; replaced with Ti plate-type. Others?