High score plus guide (3)

Revised 27 March 2012 Page 1
Introduction to PANalytical X’Pert HighScore Plus v3.0
Scott A Speakman, Ph.D.
MIT Center for Materials Science and Engineering
Speakman@mit.edu
http://prism.mit.edu/xray
This document will introduce you to some of the basic functionality of PANalytical X’Pert
HighScore Plus, v3.0. There is much more that can be done with the program. Some of the
instructions in this document will allude to things that you can do in HighScore Plus without
telling you how to do them. In such cases, this is because a quick reading of the relevant help
section in HighScore Plus will clearly tell you how to accomplish the task.
The last page of this document gives you some keywords you might search one in the help to
learn about more advanced tools.
I. Selecting a User Interface and Program Settings
a. Desktops pg 2
b. Restoring Defaults pg 2
c. Panes pg 3
II. Displaying Data and Basic Manipulation
a. Opening Data pg 4
b. Zooming In/Out pg 4
c. Comparing Multiple Scans pg 5
III. Opening a PDF Reference Pattern
a. Retrieving a Card by Reference Code pg 6
b. Searching for a Reference Pattern pg 6-9
i. Using Chemistry as search parameters pg 7
ii. Using Quality Marks as search parameters pg 7-8
iii. Using Subfiles as search parameters pg 9
c. Manipulating Reference Patterns pg 9
d. Testing for K-beta peaks pg 10
IV. Search-Match
a. Fit Background pg 10
b. Find Peaks pg 11
i. Change the display of peaks pg 12
c. Optional Steps: Convert Slits and Strip Kα2 pg 12
d. Search-Match pg 13-14
V. Calculating Penetration Depth of X-Rays pg 15
VI. List of Other Features in HighScore Plus pg 15
Appendix A. Overview of the GUI pg 16-19

I. SELECTING THE USER INTERFACE AND PROGRAM SETTINGS
Desktops
“Desktops” are predefined arrangements of windows and toolbars in HighScore Plus. You can
create your own or use one of the default desktops provided with the HighScore Plus program.
Default Desktops are designed to be optimal for specific tasks, such as Phase ID or Profile
Fitting. If you start using HighScore Plus and the desktop is arranged in a way that you are
unfamiliar with, you can change the desktop to one that is more useful.
 To select a desktop, go to the menu View > Desktop
 Select a Desktop from the menu list, not from the Dropdown menu.
 Useful desktops are: Phase-ID, Line Profile Analysis, and Structures.
 You can also change the desktop layout to your preference and save it as a new desktop
(see Customizing the Application in the help).
Restoring Defaults
If you begin using HighScore Plus and it is behaving in an unusual way, you may want to restore
the program behavior to its factory defaults. In order to do this:
 Go the menu Customize > Program Settings
o Click on the button Reset All to Default
o Click on the OK button to close the window
o You can also explore Program Settings to modify the look, feel, and performance of
the program such as options for display behavior, automatic backing up of analysis
files, behavior during pattern simulation or Rietveld refinement, and data treatments
applied automatically when you open a file
 Go to the menu Customize > Document Settings
o Click on the button Reset All to Default
o Click on the OK button to close the window
o Note: this menu is only available after you have opened a file
o You can also explore the Document Settings to change options for the graphic
display, the analyze view, and labeling for legends and peak markers
Menus
By default, the menus only show the most recently used commands. To turn off this feature, so
that you can see all commands in the menus:
 Select the menu View > Toolbars > Customize
 Select the tab Options
 Uncheck the box next to “Menus show recently used commands first”
 Click Close

Panes
There are different work areas in HighScore Plus, called “Panes”. There are up to four different
Panes. Each Pane is a window that contains a certain element of the document. The Panes are:
 Main Graphics shows the primary plot of your data for analysis and manipulation
 Additional Graphics shows modified plots of your data to assist in analysis
 Lists Pane contains tables of information that provide an overview of your data and
summarizes the results of your analysis
 Object Inspector is a dynamic list that provides detailed information about any item that
you select in HighScore plus. In some desktops, it is a separate pane; in some desktops, it
is part of the Lists pane.
 To resize the panes, drag your mouse to the border between two panes until the cursor
changes to , then left-click and drag to resize the pane.
This image shows the basic layout of the “Phase-ID” desktop
Appendix A provides more detailed information about the panes and toolbars commonly used in
HighScore Plus.
Main Graphics
Additional Graphics
Lists Pane &
Object Inspector

II. DISPLAYING DATA AND BASIC MANIPULATION
Opening Data
To Open a data set, go to File>Open
 If you select multiple files, each one will open in its own document.
Zooming in Main Graphics
 Zoom in by left-click and dragging in the Main Graphics pane.
 Zoom out by double-clicking in the Main Graphics pane.
 When zoomed in, you can use the scroll bar at the bottom of the Main Graphics pane to move
the zoom view left and right
 When zoomed in, hold down the Alt key and left-click and drag the mouse:
o If you drag the mouse left-right, you will scroll left or right
o If you drag the mouse up-down, you will
zoom in or zoom out x (y autoscales to the
maximum intensity in the zoomed view)
 Use the Automatic Scale button of the Tool
Palette toolbar to switch autoscaling of intensity on
or off
 Use the Zoom Intensity button of the Tool
Palette toolbar to switch zooming in Y-axis direction
on or off.
 You change the Y-axis scale by toggling with the
"Set Y-axis Scale" button from the Tool Palette
toolbar.
o To switch directly to a "Linear Y-Axis",
"Square Root Y-Axis" or "Logarithmic Y-
Axis" scale use the small button next to it.
You can use the additional graphics pane to manipulate
your zoom view by enabling the Zoom Overview.
 Right-click in the Additional Graphics pane
 Select the menu Show Graphics > Zoom Overview
o The Additional Graphics pane will show you your entire scan, with a black box
highlighting the zoomed region
o To move the zoom region, left-click and drag the black highlight box
o To resize the zoom region, left-click and drag the white dot at the side of the black
highlight box.
Right-clicking in the Main Graphics pane will give you a menu with shortcuts to several options,
including analyses (determine background, strip K-Alpha2, etc) and cursors (show spectral lines,
insert peaks, etc).

Comparing Multiple Scans
To compare multiple data sets
 Open the first data file using the menu File > Open.
○ This will be the “Anchor Scan”
 Use the menu File > Insert to add additional scans to the document.
○ Select all of the additional data files that you want to add and click OK
○ You can select multiple files to insert by using shift+click or ctrl+click
 In the Main Graphics Pane, go to the Compare or 2D tabs to view all of the scans
To adjust scan properties such as line color
 Go to the Scan List tab in the Lists pane to see a list of all of the scans.
 In the Scan List, select the scan that you want to modify
 Go to the Object Inspector
 You can adjust properties of the scans, such as line color or name, in the Object Inspector.
To scale scans so that their intensities are similar:
 Go to the menu Treatment > Adjust to Anchor
 In the “Adjust” drop-down menu, select the scan that you want to adjust
 Select the Scale Factor, Vertical Shift, or Both tab
o Scale Factor adjusts the net intensity of the pattern, multiplying every data point by the
scale factor. This is useful if two patterns were collected with a different scan rate or the
samples had different packing densities, producing different overall intensities.
o Vertical Shift will move the entire pattern up or down by a set amount. This is often done
to match the background without scaling the intensity.
o Both will both scale the pattern intensity (to match the peak maximum) and to shift the
pattern up/down to match background
 In Method, select Fit Maximum, Fit Background, or User Defined
o The program will fit based on the part of the pattern visible in the Main graphics.
 Click the Adjust button
o The program will show you a preview of the result.
o You can change the adjustment (for example, the user defined value) and then click
Adjust again to preview the new result.
 Click the Accept button
 In the Main Graphics pane, go to the Compare tab to view the multiple scans.
Note: Treatment and Analysis tools only work on the Anchor scan

III. Opening a PDF Reference Pattern
The Powder Diffraction File (PDF) is a database of X-ray powder diffraction patterns maintained
by the International Center for Diffraction Data (ICDD). You can find more information about
the PDF, including tutorials and references, at www.icdd.com
Data in the PDF comes from:
 publications, journals, scientific periodicals and theses
 ICDD grants for new materials
 Data collections donated by companies or individuals
 Data from other database organizations that are licenses by the ICDD
To Retrieve PDF Patterns using the PDF Reference Number
1) Go to the menu Reference Patterns > Retrieve Pattern By > Reference Code
2) In the dialog box, type in the Reference Code(s) for the PDF card(s) that you want to open
3) Click Load
4) The cards will be loaded into the Pattern List in the Lists Pane
In older literature, you may see reference to JCPDS cards. The JCPDS database was the
predecessor to the PDF. You can use the original JCPDS reference number to retrieve that entry
in the PDF database.
To search the PDF Database for References
If you do not know the reference code for the PDF card for the material that you are interested in,
you can search the PDF database for the relevant entries.
1) Go to the menu Reference Patterns > Retrieve Pattern By > Restrictions
2) In the Restrictions dialogue window that opens, you define parameters to restrict which
patterns will be retrieved from the database. If you defined no parameters at all, then all
patterns in the database would be retrieved.
a) Each tab in the Restrictions window allows you to control a different subset of search
parameters. In each of the tabs, you can set the parameters for searching the PDF
database for reference patterns.
b) The options available in the tabs are described on the next page (pg 7)
c) Each tab that is being used to constrain the search will be highlighted with a red flag
d) The information bar at the bottom of the window tells you how many patterns will be
retrieved with the current set of restrictions. This number should be less than 10; anything
more is difficult to manage. If you cannot make this number less than 10, then you
should use Search & Match (pg 11) instead.
3) Once you have set up your search parameters, using as many or as few Restrictions as you
like, then you click Load to perform the search and find the reference patterns.
a) The reference patterns will be added to the Pattern List pane.
b) If you have other reference patterns already loaded, the Combine Patterns dialogue will
ask you to specify how you want to combine the new patterns with the previous. Make
your choice and click OK.
c) The Restrictions window will remain open, allowing you to retrieve more references
i) If you are done finding reference patterns, then click Close.

The tabs that you can use to constrain you search of the PDF database are:
Chemistry
This is the most common restriction that you will use.
 You have three fields to specify what compositions you want to find in the database:
 “All of:” all of these elements together must be present in each reference pattern
 “At least one of:” one or more of these elements must be present in each reference pattern
 “None of:” none of these elements must be present in each reference pattern
○ If you click on the button Add Rest to None Of, then every element not listed in “All
of:” or “At least one of:” fields is added to the “None of:” field
 The Min and Max Number of Elements controls how many unrestricted elements are
allowed in the retrieved reference patterns
Example:
 In this example, 2146 patterns will be
retrieved. These patterns would include
FePO4, LiPO4, and LiFePO4; but would
also include any material that contains P
and O, Li or Fe, and any other element—
for example, Fe2AsP3O12 or RbFeP2O7.
 In this example, only 181 patterns will be
retrieved. All elements except Li, Fe, P,
and O were added to the “None of:” field
by clicking the Add Rest to None Of
button. Patterns loaded would include
FePO4, LiPO4, and LiFePO4.
Quality
This is another very useful restriction to use.
 It is highly recommended that you check the entry “Skip marked as deleted by ICDD”
○ Entries are deleted from the database if they are replaced with better references or they
are found to be wrong.
○ These entries are kept in the electronic database in case you need access to them (perhaps
an old paper references a now obsolete PDF card), but you normally do not want these
entries to be included in your search results.
 You can use the other settings to restrict what type of reference cards you search. The quality
marking system of the ICDD is explained on the next page (pg 11)
 You can also use this tab to exclude data that was not collected at standard pressure and
temperature (“Skip non-ambient temperature” and “Skip non-ambient pressure”)

PDF cards have quality marks assigned by the ICDD to indicate how reliable the data is.
Star (S, +). Indicates the pattern represents high-quality diffractometer or Guinier data.
 The chemical composition has been well characterized.
 The intensities have been measured objectively-- no visual estimation is allowed.
 Good range and an even spread of intensity.
 Completeness of a pattern is sensible
 Each reflection with d-value less than or equal to 2.500 Angstroms has at least three
significant figures after the decimal point. Reflections with d-value less than or equal to
1.2000 Angstroms have at least four significant figures after the decimal point.
 No serious systematic errors exist.
 The |Δ2Θ| of a qualifying reflection is less than or equal to 0.05 degrees. In the case of
multiply-indexed reflections, only the minimum absolute Δ2Θ is considered.
 The average |Δ2Θ| value is less than 0.03 deg. for qualifying reflections.
 No un-indexed, space group extinct or impurity reflections are present.
Indexed (I). Indicates the pattern has been indexed.
 There is a reasonable range and even spread in intensities.
 Completeness of the pattern is sensible.
 Reflections with d-value less than or equal to 2.000 Angstroms have at least three significant
figures after the decimal point.
 No serious systematic errors exist.
 No qualifying reflection has an absolute Δ2Θ greater than or equal to 0.20 degrees.
 The average absolute Δ2Θ value should be less than or equal to 0.06 deg.
 The maximum number of un-indexed, space group extinct or impurity reflections is two, but
none of these reflections is among the strongest eight lines.
Blank (B). Indicates the pattern does not meet the Star, Indexed, or Low-Precision criteria.
Low Precision (O, ?). Indicates the diffraction data have been taken on poorly characterized
material, a sample with known (or suspected) problems such as preferred orientation, or that the
data are known (or suspected) to be of low precision.
 Data from a multi-phase mixture.
 Data from a phase poorly-characterized chemically.
 The "O" quality mark is commonly assigned to patterns for which no unit cell is reported
 Usually, the editor has inserted a comment to explain why the "O" was assigned.
 The number of un-indexed, space group extinct or impurity reflections is three or more.
 One of the three strongest reflections is un-indexed.
Prototyping (P). Indicates the structural data that was assigned to a particular entry from the
Linus Pauling File. Prototype structure is an editorial action to assign a space group and
coordinates for entries that have not recovered this information from the primary literature.
Rietveld (R). Indicates the d-values are directly the result of Rietveld refinement of the data.
Hypothetical (H). Indicates the structure is calculated theoretically from the atomic positions
and thermal parameters of an isostructural compound

Subfiles
This tab is used to restrict the search to certain
subfiles of the PDF. Data in the PDF comes
from several different sources. The data is
organized into subsets depending on the
source and subfiles depending on
characteristics of the material. In HSP, you
can search for entries from a single
subset/subfile, a combination of subsets and
subfiles, or from all subsets.
Crystallography
This restriction tab can be used to specify parameters of the crystal structure for all retrieved
entries, such as the Crystal System (cubic, hexagonal, …), Density (theoretical density based on
crystal structure), or lattice parameters. This restriction is not used that often.
Strings
This restriction is used to search for text in the PDF reference, such as a specific Mineral Name
(hematite, etc) or Compound Name (polyethylene, etc). This restriction is not used that often.
MANIPULATING THE REFERENCE CARDS THAT YOU HAVE LOADED
Once you have searched the database and added reference cards, you can view them in the Main
Graphics pane and manipulate them in the Lists Pane and Object Inspector
In the Lists Pane, go to the Pattern List tab. You can:
 Make the pattern Visible or Hidden by checking/unchecking the Visible column
 Change the pattern color by using the drop-down menu in the Display Color column
 Open the reference card by double-clicking on an entry
○ The entry will contain information such as formula, unit cell information, the reference
that the entry came from, and a list of peak positions and intensities.
○ You can use the peak list in the reference card to decide where you want to scan. A card
might list several peaks at low angles (below 20deg 2theta) that are very informative.
After 55.74deg 2theta, all of the diffraction peaks are weak. Therefore, a good scan range
would be from 5deg to 56deg 2theta.
In the Object Inspector, you can manipulate the display of the Reference Pattern (color, scaling)
 Click on an entry in the Pattern List
 go to the Object Inspector
○ Settings in the Display section of the Object Inspector will let you change the visual
display of the reference pattern in the Main Graphics
○ Other sections display information about the reference card
If you want to compare your data to the reference card for a specific phase, it is easier to use the
search-match procedure, explained on the next page.

To Test for K-Beta Peaks
1) Select the menu Tools >Spectral Lines
a) You now control a cursor that indicates the position of the K-alpha1 peak
2) Position the cursor over a major K-alpha1 diffraction peak
a) The solid blue line shows the position of the corresponding K-beta peak
b) The dotted lube line shows the position of the corresponding W L-alpha peak
c) The dotted red line shows the position of the corresponding K-alpha2 peak
3) You only need to check the one or two strongest peaks of the pattern for the presence of K-
beta peaks. The intensity of a K-beta peak is proportional to the intensity of the
corresponding K-alpha1 peak.
IV. SEARCH-MATCH
There are several steps involved when you want to determine the identity of unknown phases in
your diffraction pattern.
1) Fit the background.
a) Select the menu Treatment > Determine Background
b) Use a small bending factor (0-2) and a granularity between 15 to 30
c) When the background is good, Accept the background (do not Subtract).
 The granularity parameter changes the number of intervals used for background
determination
 The bending factor slider adjusts the curvature of the background

2) Search for Peaks
a) Select the menu Treatment > Search Peaks
b) Adjust the peak search parameters as necessary
i) Use the “Default” parameter settings as a starting point
ii) Click on the More button
iii) Select Default from the drop-down menu
 significance is a calculation of the probability that a possible peak is not noise-induced.
 Only peaks with a significance above the Minimum Significance are accepted by the
peak search procedure.
 A large Minimum Signifance (2 or more) is useful for noisy data- however, some
very small peaks could be missed.
 The minimum and the maximum tip width are a measure of the width of the peaks to be
found. The tip width is the width, where the 2nd derivative is < zero.
 The values 0.00 and 1.00 can be used for most scans.
 Increase the maximum peak tip width to find very broad peaks.
 Raising the minimum peak tip width can decrease the number of noise-induced peaks
detected, but at the risk of missing very small peaks.
 The Peak Base Width describes the width of the peak foot. It must be greater than the
maximum peak tip width. Increase this value if your data contains broad peaks.
c) Click on the Search Peaks button
 A preview lets you examine the quality of the peak search before accepting the results
 The peaks are represented in the Main Graphics as orange lines.
 K-alpha1 peaks are indicated by solid lines in the peak markers
 K-alpha2 peaks are indicated by dotted lines in the peak markers
 You can change where the peak markers are shown using the "Set Display of Peaks"
button in the Display Mode button bar. Access the dropdown list with the small button
 You can have the peak markers shown in the data or above the data (or both)
 The “Show Calculated Profile” button can be used to show or hide a simulated pattern
based on the peak search result.
Position [°2Theta] (Copper (Cu))
90 95
Counts
0
5000
10000

 Click on the "Peak List" tab in the Lists pane to see numerical details on every peak.
 Peaks derived from the Kα2 wavelength are indicated by a gray background color in the
peak list.
d) If too many/too few peaks were identified, then adjust the parameters and click the Search
Peaks button again
e) When you are happy with the result, click the Accept button.
f) You do not need to identify all small peaks.
g) All intensity above the background curve is considered in determining the best possible
phases to match the data.
h) Peaks that are explicitly identified are given more importance in the fitting algorithm.
3) OPTIONAL- Convert data collected with Automatic Divergence Slits
If you collected data from an “infinitely” thick sample using the Programmable Divergence Slit
in Automatic mode, then you should use the Divergence Slit correction to modify the peak
intensities to their equivalent if they had been collected in Fixed slit mode.
a) Select the menu Treatment > Corrections > Convert Divergence Slit
b) Load the Default parameters
i) Click on the More button
ii) Select Default from the drop-down menu
c) Click the ADS To FDS button
d) Click the Replace button
e) Click the Close button
4) OPTIONAL- Strip Kα2
You can numerically remove all K-alpha2 signal from your data. This is not necessary for phase
ID or other analyses. However, you might want to remove the Kα2 peaks from your observed
diffraction pattern so that the data is easier for you to evaluate good/poor matches or to clarify
the data plot when you are preparing it for a presentation or publication.
a) Select the menu Treatment >Strip K-Alpha2
b) Click the Strip K-alpha2 button.
c) Click the Replace button
d) Click the Close button

5) Run the Search-Match procedure
a) Select the menu Analysis > Search & Match >
Execute Search & Match
b) Adjust the Parameters as necessary
i) Load the Default parameters
(1) Click on the More button
(2) Select Default from the drop-down
ii) The parameters that you can adjust are:
 Data Source:
 Peak Data is the peak list produced from your peak search.
 Profile Data is all observed intensity above the background model produced when
you fit the background
 The best result is usually produced when you use both Peak & Profile Data
 Scoring Scheme: this should be Multi Phase unless you want to try to force the program
to find a single phase that will match all observed data.
 Auto Residue: if this is on, then when you accept a candidate as a good match all of the
remaining candidates will be rescored based on how well they fit the unmatched features
 Match Intensity: if this is off, the quality of the match is based only on agreement of
peak positions; if this is on, the score reflects the quality of the intensity match as well.
 Demote unmatched strong: if this is one, if a candidate has one strong (>50%) peak
missing in the observed data then the candidate is discarded—no matter how well the rest
of the peaks match.
 Allow pattern shift: If on, each reference pattern is shifted for an optimal fit with the
data. The maximum allowed pattern shift is ± 4 x FWHM.
c) The Restrictions tab will let you constrain the search by chemistry, quality, subfiles—any
of the categories in the Restrictions filter explained on the pages 7-9.
6) All possible matches are added to the Candidate list in the Patterns list.
a) A score is calculated for all candidates to determine how well they match the
experimental data. A high score indicates a better match.
b) When you accept a candidate as a good match, it is moved Accepted area in the Pattern
list. The scores for all other candidates are recalculated
c) Peaks not explained by a reference pattern have a little "V" mark, if you have them
displayed above the main graphics
d) High intensity areas in the main graphics are indicated in gray. These scan features are
explained by the accepted reference pattern. If no scan features are marked in gray press
the "Show Explained Features" button in the Display Mode button bar.
e) Right-click on the candidate pattern and select Analyze Pattern Lines from the menu.
i) This will show a list of the lines in the reference card and identify which ones are and
are not observed in the data.

There are several tools available to access the "match" of a candidate/accepted phase:
 Explained scan regions (graphically)
 matched peaks (graphically, textually)
 matched peaks by reference codes (textually)
 Reference pattern lines matched (textually)
 Number of matched lines, number of new matched lines (textually)
When you cannot identify all phases from the candidate list of the initial search-match, proceed
as follows:
1. Change the scores to find more candidates from the existing candidate list. There is a
toolbar of options that can be used for changing the score (shown on page 19).
 Change the “Match Intensity” parameter using the button.
 When looking for minor phases, switch off the “Demote unmatched strong” option
 Do not use the allow pattern shift parameter unless you are dealing with strong solid-
solution effects or with an incorrect sample height. In case of the usual, small pattern
shifts this parameter often favors patterns not fitting very well to the measurement.
 Change the “Data Source”
2. The next step is to repeat the search-match with new, different restrictions (and/or different
parameters). It is possible that the correct phase was excluded by the restrictions used in the
initial search-match being too tight, which prohibited the correct answer showing up in the
candidate list. Or the initial restrictions were too wide, allowing many isotypical phases to
pass and completely fill the candidate list, leaving no space for other candidates.
If necessary repeat step 1. with the new candidate list. Many identification problems can be
solved this way.
3. If you still have no success, you should switch on the track graph function. Now zoom in on
the low-angle region containing unexplained peaks and/or features and check the candidate
list. Only the peaks/features in the visible (=zoomed) region are taken into account now. If
there are no new matches found on top of the candidate list, you could also start a new
search-match using only the zoomed range as input.
4. Exclude all already matched peaks and to search-match again using only the remaining peak
data as input. To exclude peaks from the peak list:
1. Select the menu Tools > Set Peak Status
2. Select the parameters Matched = True Exclude
3. All peaks matched by accepted patterns will be excluded from the peak list
4. Run the search match setting the Data Source to “Peak Data”
Repeat steps 1. and 2. with the new candidate list, if necessary.

CALCULATING THE PENETRATION DEPTH OF X-RAYS INTO YOUR SAMPLE
How deeply X-rays penetrate into your sample depends on the mass absorption coefficient of
your sample, the density of your sample, and the incident angle of the X-rays. You can use
HighScore Plus to calculate the penetration depth.
1) Select the menu Tools > MAC Calculator
2) Enter the chemical formula of you sample in
the text field, then press enter
a. If you have a mixture, enter each
chemical formula one at a time
b. Then enter the Weight % of each
component in your mixture
c. Click Calculate Mixture MAC button
3) Click the button Calculate Penetration Depth
4) Enter the appropriate information in the next page
a. Packing is the fractional packing factor for your
sample. A value of 1 would mean 100% dense (ie 0%
porosity). The typical value for a packed powder is 0.7.
b. Density is the theoretical density for your material.
c. Incident angle is usually ½ 2θ
d. With these values entered, the program will calculate the Penetration Depth of X-
rays into your sample. If your sample is thicker than this, then your sample is
considered “infinitely thick”
V. LIST OF OTHER FEATURES IN HIGHSCORE PLUS
HighScore Plus can be used for quantification of data through a number of ways. Many of these
are well-document in the help or in other tutorial materials available at
http://prism.mit.edu/xray/tutorials.htm
Some of the capabilities you might want to explore, and the place they are found in the help, are:
1) Unit Cell Refinement
a) See Live Lattice for quick fitting of a unit cell to observed data
b) See Unit Cell Refinement for least-squares refinement of lattice parameters to observed
peaks
2) Line Profile Fitting
a) See Line Profile Analysis for instructions on profile fitting peaks
b) See Williamson-Hall Plot for using profile fitting to determine crystallite size
3) Cluster Analysis- Used to sort multiple datasets by similarities and differences
4) Rietveld Refinement

APPENDIX A. OVERVIEW OF GRAPHICAL USER INTERFACE IN HIGHSCORE PLUS
Panes
There are up to four Panes in HSP. Each Pane is a window that contains a certain element of the
file. The Panes are:
A. Main Graphics has 6 tabs that show different views of your data for analysis
 Analyze: shows the anchor scan, reference patterns, and any data manipulation or analysis
that you have done. The Analyze tab must be active to do most data analyses
 Compare: shows the Anchor scan, any additional scans, and reference patterns all overlayed
 2D, 3D and Isolines are different views to compare multiple scans.
 Pattern: shows the stick patterns for any PDF reference patterns that you have loaded.
B. Additional Graphics has 5 views showing modified plots of your data to assist analysis
1) Zoom overview (default):
a) displays the complete anchor scan and highlights the zoomed in range.
b) You can use this to move the visible region in the main graphics: left click and drag the
zoomed area to move it; drag the handles at the corners to resize
2) Difference plot
a) Shows you the difference between observed and calculated data when you are profile
fitting or doing a Rietveld refinement
3) Halfwidth plot
a) Plots FWHM vs 2Theta for profile fit peaks
4) All-in-one
a) Complements Phase ID: it shows all peaks, the lines of the accepted (identified) phase
patterns, the lines of a candidate pattern, and the lines currently unmatched by any
accepted patterns (the residue)
5) Pattern view
a) Displays just the reference pattern stick patterns for accepted phases
C. Lists Pane contains several tabs. Each one contains different information, controls, and tools
that summarize your data or your analysis results.
In any list, you can customize the columns of information shown.
 Right-click in the body (the area showing information) of the Lists Pane
 Select Customize Pattern List from near the bottom of the menu
 In the dialogue window that opens, select the column headers that you want to add to the List
 Drag the column header from the dialogue window into the column headers in the Lists Pane
 You can re-order column headers by drag and dropping
The most useful tabs that you can add to the Lists Pane (from the View menu) are:
1) Anchor Scan Data
a) Shows the actual raw data contained in the anchor scan file
2) Scan List

a) Shows a list of the anchor scan and all additional scans that have been loaded into the
document. Columns can be set to show some information from the scan files, such as
scan parameters (start angle, stop angle), Scan ID, etc.
b) Right-clicking in this list gives you a menu that will allow you to do certain actions, such
as changing which scan is the anchor scan, summing multiple scans, substracting a
background scan from the anchor scan, etc
3) Peak List
a) Shows a list of all peaks that have been found through a peak search or profile fitting.
Columns can be set to show information such as position, intensity, width, etc
b) Right-clicking in this list gives you a menu that will allow you to manipulate the peak
list, such as deleting a peak from the list, stripping K-alpha2, etc
4) Pattern List
a) Provides two lists: one of Accepted Reference Patterns and one of Candidate Reference
Patterns
b) All accepted reference patterns with a check mark are shown in the Main Graphics view
and are considered matches to the anchor scan
c) When manually searching the PDF database, all patterns retrieved are automatically
loaded into the accepted reference pattern
d) A search/match will load patterns into the candidate list, where they are considered
possible matches
e) Right clicking lets you access several options.
5) Refinement Control
a) Gives you information and controls for performing a Rietveld refinement
6) Structure Plot
a) Allows you to draw a 3D representation of a crystal structure that is loaded in the
Refinement Control list
7) Distances and Angles
a) Allows you to calculate bond distances and angles for a crystal structure that is loaded in
the Refinement Control list
D. Object Inspector is a dynamic list that shows you detailed information about any object that
you select in HSP.
a) For example, if you click on a data set in the Scan List, then the object inspector will
give you access to all of the information included in the data file.
b) If you float the mouse over a peak in the main graphics window, the object inspector will
give you detailed information about that peak and the ability to control settings used in
profile fitting that peak.
c) If you select an object in the Refinement Control list, the object inspector will show you
the current values and give you access to all applicable settings, values, constraints, and
other information and controls relevant to that object.
 Whenever you can’t find something somewhere else, look in the Object Inspector.
 The object inspector can be part of the Lists Pane (default in the Phase-ID desktop) or it can
be its own unique pane (default in Line Profile Analysis and Structures desktops)

Toolbars.
When you are in the Phase-ID desktop, the toolbars that are automatically loaded are:
 Standard Toolbar: Gives you the normal Windows functions—Save, Open, Cut, Copy, Paste,
Undo, etc.
 XRD Toolbox: Shortcuts to treatment and analysis functions used when processing XRD
data
 Tool Palette: Functions dealing with the cursor and zoom modes, graphics axes, and display
tools.
 Batches: Shortcut to automated batch routines for standard analyses
 Readout: Shows the cursor position in terms of 2Theta, d-spacing, and intensity when the
cursor is over the Main Graphics pane
 Pattern: Functions to retrieve reference patterns, start a search-match and change search-
match scoring criteria
 Display mode: Functions to switch on/off the display of certain data. This toolbar never
changes the document or data
 Desktop: Switch what desktop layout is being used
Display Mode:
Standard
XRD Toolbox
Batches
Tool Palette
Readout
Pattern
Display Mode
Desktop
Maximize Main
Graphics to occupy
the full screen; click
again to shrink to
normal size
Show/Hide Functions
which are useful
during search-match
Show/Hide Functions
which are usefulduring
Rietveld refinement

Tool Palette:
XRD Toolbox
Pattern
Change x and y axis
scales
Autoscale Y in
Main Graphics
Mouse Cursor controls
Zoom in Main Graphics
Zoom to arbitrary intensity
in Main Graphics
Mouse Cursor in Select Mode to
manipulate data analysis in Main
Graphics
Profile Fitting
Controls
Strip
Kα2
Fit
Background
Insert Peaks
Graphically
Peak
Search
Find PDF
Reference Patterns
Run
Search-
Match
Useful Controls when
doing a Search-Match

High score plus guide (3)

Recommended

More Related Content

What's hot (20)

Viewers also liked (9)

Similar to High score plus guide (3) (20)

Recently uploaded (20)

High score plus guide (3)